Resins poly

Resins formed from the reaction of poly(vinyl alcohol) with aldehydes. The formal derivative (from methanal) is used in wire coatings and adhesives and the bulyral (from butanal) is used in metal paints, wood-sealers, adhesives and in safety glass interlayers. 

Acrylonitrile-butadiene-styrene-poly(vinyl chlo- Nitrile resins... 

Cellulose-acetate-butyrate resin Poly(amide-imide)... 

Cellulose nitrate resin Poly(aryl ether)... 

Hydroxy-2-methylpropanenitrile is then reacted with methanol (or other alcohol) to yield methacrylate ester. Free-radical polymerization is initiated by peroxide or azo catalysts and produce poly(methyl methacrylate) resins having the following formula ... 

Poly (methyl Acrylate). The monomer used for preparing poly(methyl acrylate) is produced by the oxidation of propylene. The resin is made by free-radical polymerization initiated by peroxide or azo catalysts and has the following formula ... 

Casting resin Novolac resin Poly(tetrafluoroethylene) Poly(chloro- trifluoro- ... 

Fluorinated ethylene-propylene resin Poly(vinylidene fluoride) Ethylene-tetrafluoroethylene copolymer Ethylene- chlorotrifluoro- ethylene copolymer Cellulose- filled Glass-fiber- reinforced... 

Poly(oxyethylene) resins. See Poly(ethylene oxide) polymers. 

The majority of xylenes, which are mostly produced by catalytic reforming or petroleum fractions, ate used in motor gasoline (see Gasoline and other MOTORFUELs). The majority of the xylenes that are recovered for petrochemicals use are used to produce PX and OX. PX is the most important commercial isomer. Almost all of the PX is converted to terephthaUc acid and dimethylterephthalate, and then to poly(ethylene terephthalate) for ultimate use in fibers, films, and resins. 

The many commercially attractive properties of acetal resins are due in large part to the inherent high crystallinity of the base polymers. Values reported for percentage crystallinity (x ray, density) range from 60 to 77%. The lower values are typical of copolymer. Poly oxymethylene most commonly crystallizes in a hexagonal unit cell (9) with the polymer chains in a 9/5 helix (10,11). An orthorhombic unit cell has also been reported (9). The oxyethylene units in copolymers of trioxane and ethylene oxide can be incorporated in the crystal lattice (12). The nominal value of the melting point of homopolymer is 175°C, that of the copolymer is 165°C. Other thermal properties, which depend substantially on the crystallization or melting of the polymer, are Hsted in Table 1. See also reference 13. 

Acrylics. Acetone is converted via the intermediate acetone cyanohydrin to the monomer methyl methacrylate (MMA) [80-62-6]. The MMA is polymerized to poly(methyl methacrylate) (PMMA) to make the familiar clear acryUc sheet. PMMA is also used in mol ding and extmsion powders. Hydrolysis of acetone cyanohydrin gives methacrylic acid (MAA), a monomer which goes direcdy into acryUc latexes, carboxylated styrene—butadiene polymers, or ethylene—MAA ionomers. As part of the methacrylic stmcture, acetone is found in the following major end use products acryUc sheet mol ding resins, impact modifiers and processing aids, acryUc film, ABS and polyester resin modifiers, surface coatings, acryUc lacquers, emulsion polymers, petroleum chemicals, and various copolymers (see METHACRYLIC ACID AND DERIVATIVES METHACRYLIC POLYMERS). 

Uses. The largest uses of butanediol are internal consumption in manufacture of tetrahydrofuran and butyrolactone (145). The largest merchant uses are for poly(butylene terephthalate) resins (see Polyesters,thermoplastic) and in polyurethanes, both as a chain extender and as an ingredient in a hydroxyl-terminated polyester used as a macroglycol. Butanediol is also used as a solvent, as a monomer for vadous condensation polymers, and as an intermediate in the manufacture of other chemicals. 

Suspension Polymerization. Suspension polymerisation yields polymer in the form of tiny beads, which ate primarily used as mol ding powders and ion-exchange resins. Most suspension polymers prepared as mol ding powders are poly(methyl methacrylate) copolymers containing up to 20% acrylate for reduced btittieness and improved processibiUty are also common. 

The cured polymers are hard, clear, and glassy thermoplastic resins with high tensile strengths. The polymers, because of their highly polar stmcture, exhibit excellent adhesion to a wide variety of substrate combinations. They tend to be somewhat britde and have only low to moderate impact and peel strengths. The addition of fillers such as poly (methyl methacrylate) (PMMA) reduces the brittleness somewhat. Newer formulations are now available that contain dissolved elastomeric materials of various types. These mbber-modifted products have been found to offer adhesive bonds of considerably improved toughness (3,4). 

Emulsion Adhesives. The most widely used emulsion-based adhesive is that based upon poly(vinyl acetate)—poly(vinyl alcohol) copolymers formed by free-radical polymerization in an emulsion system. Poly(vinyl alcohol) is typically formed by hydrolysis of the poly(vinyl acetate). The properties of the emulsion are derived from the polymer employed in the polymerization as weU as from the system used to emulsify the polymer in water. The emulsion is stabilized by a combination of a surfactant plus a coUoid protection system. The protective coUoids are similar to those used paint (qv) to stabilize latex. For poly(vinyl acetate), the protective coUoids are isolated from natural gums and ceUulosic resins (carboxymethylceUulose or hydroxyethjdceUulose). The hydroHzed polymer may also be used. The physical properties of the poly(vinyl acetate) polymer can be modified by changing the co-monomer used in the polymerization. Any material which is free-radically active and participates in an emulsion polymerization can be employed. Plasticizers (qv), tackifiers, viscosity modifiers, solvents (added to coalesce the emulsion particles), fillers, humectants, and other materials are often added to the adhesive to meet specifications for the intended appHcation. Because the presence of foam in the bond line could decrease performance of the adhesion joint, agents that control the amount of air entrapped in an adhesive bond must be added. Biocides are also necessary many of the materials that are used to stabilize poly(vinyl acetate) emulsions are natural products. Poly(vinyl acetate) adhesives known as "white glue" or "carpenter s glue" are available under a number of different trade names. AppHcations are found mosdy in the area of adhesion to paper and wood (see Vinyl polymers). 

Dry chlorine has a great affinity for absorbing moisture, and wet chlorine is extremely corrosive, attacking most common materials except HasteUoy C, titanium, and tantalum. These metals are protected from attack by the acids formed by chlorine hydrolysis because of surface oxide films on the metal. Tantalum is the preferred constmction material for service with wet and dry chlorine. Wet chlorine gas is handled under pressure using fiberglass-reinforced plastics. Rubber-lined steel is suitable for wet chlorine gas handling up to 100°C. At low pressures and low temperatures PVC, chlorinated PVC, and reinforced polyester resins are also used. Polytetrafluoroethylene (PTFE), poly(vinyhdene fluoride) (PVDE), and... 

The beater additive process starts with a very dilute aqueous slurry of fibrous nitrocellulose, kraft process woodpulp, and a stabilizer such as diphenylamine in a felting tank. A solution of resin such as poly(vinyl acetate) is added to the slurry of these components. The next step, felting, involves use of a fine metal screen in the shape of the inner dimensions of the final molded part. The screen is lowered into the slurry. A vacuum is appHed which causes the fibrous materials to be deposited on the form. The form is pulled out after a required thickness of felt is deposited, and the wet, low density felt removed from the form. The felt is then molded in a matched metal mold by the appHcation of heat and pressure which serves to remove moisture, set the resin, and press the fibers into near final shape (180—182). 

Polyester sheet products may be produced from amorphous poly(ethylene terephalate) (PET) or partiaHy crystallized PET. Acid-modified (PETA) and glycol modified (PETG) resins are used to make ultraclear sheet for packaging. Poly(butylene terephthalate) (PBT) has also been used in sheet form. Liquid-crystal polyester resins are recent entries into the market for specialty sheet. They exhibit great strength, dimensional stabHity, and inertness at temperatures above 250°C (see Polyesters,thermoplastic). 

Table 6 shows the sales estimates for principal film and sheet products for the year 1990 (14). Low density polyethylene films dominate the market in volume, followed by polystyrene and the vinyls. High density polyethylene, poly(ethylene terephthalate), and polypropylene are close in market share and complete the primary products. A number of specialty resins are used to produce 25,000—100,000 t of film or sheet, and then there are a large number of high priced, high performance materials that serve niche markets. The original clear film product, ceUophane, has faUen to about 25,000 t in the United States, with only one domestic producer. Table 7 Hsts some of the principal film and sheet material manufacturers in the United States.

Poly etrafluoroethylene is manufactured and sold in three forms granular, fine powder, and aqueous dispersion each requires a different fabrication technique. Granular resins are manufactured in a wide variety of grades to obtain a different balance between powder flows and end use properties (Pig. 1). Pine powders that are made by coagulating aqueous dispersions also are available in various grades. Differences in fine powder grades correspond to their usefulness in specific appHcations and to the ease of fabrication. Aqueous dispersions are sold in latex form and are available in different grades. A variety of formulation techniques are used to tailor these dispersions for specific appHcations. 

---