Figure 2 shows that the PP domain is smallest with the compatibilized blend containing the maleic-grafted EMA versus the binary blend (Figure 1). There is an increase in number of pores with the compatibilized blends versus the binary system, as well as the pores are smaller. The pores do not seem to be interconnected as can be seen from the commercial Celgard films in Figure 3. The pore size is also significantly smaller.

Alkenylsuccinic anhydrides made from several linear alpha olefins are used in paper sizing, detergents, and other uses. Sulfosuccinic acid esters serve as surface active agents. Alkyd resins (qv) are used as surface coatings. Chlorendric anhydride [115-27-5] is used as a flame resistant component (see Flame retardants). Tetrahydrophthalic acid [88-98-2] and hexahydrophthalic anhydride [85-42-7] have specialty resin appHcations. Gas barrier films made by grafting maleic anhydride to polypropylene [25085-53-4] film are used in food packaging (qv). Poly(maleic anhydride) [24937-72-2] is used as a scale preventer and corrosion inhibitor (see Corrosion and corrosion control). Maleic anhydride forms copolymers with ethylene glycol methyl vinyl ethers which are partially esterified for biomedical and pharmaceutical uses (189) (see Pharmaceuticals). 

Poly(phenylene oxide)s undergo many substitution reactions (25). Reactions involving the aromatic rings and the methyl groups of DMPPO include bromination (26), displacement of the resultant bromine with phosphoms or amines (27), lithiation (28), and maleic anhydride grafting (29). Additional reactions at the open 3-position on the ring include nitration, alkylation (30), and amidation with isocyanates (31). 

Most elastomers that are used for nylon modification contain a small amount of maleic anhydride (0.3 to 2%). In the melt blending process, these elastomers react with the primary amine end groups in nylon, giving rise to nylon grafted elastomers. These grafts reduce the interfacial tension between the phases and provide steric stabili2ation for the dispersed mbber phase. Typically, thermally stable, saturated mbbers such as EPR, EPDM, and styrene—ethylene/butylene—styrene (SEBS) are used. 

Another important use of BCl is as a Ftiedel-Crafts catalyst ia various polymerisation, alkylation, and acylation reactions, and ia other organic syntheses (see Friedel-Crafts reaction). Examples include conversion of cyclophosphasenes to polymers (81,82) polymerisation of olefins such as ethylene (75,83—88) graft polymerisation of vinyl chloride and isobutylene (89) stereospecific polymerisation of propylene (90) copolymerisation of isobutylene and styrene (91,92), and other unsaturated aromatics with maleic anhydride (93) polymerisation of norhornene (94), butadiene (95) preparation of electrically conducting epoxy resins (96), and polymers containing B and N (97) and selective demethylation of methoxy groups ortho to OH groups (98). 

Extension of the chlorosulfonation technology to base resins other than polyethylene, where value can be added, seems a logical next step. Polypropylene and ethylene copolymers containing additional functionaUty, ie, maleic anhydride graft, vinyl acetate, acrylic acid, etc, have been chlorinated and chlorosulfonated to broaden the appHcation base, particularly in coatings and adhesives (9,10). 

Modifications of epichlorohydrin elastomers by radical-induced graft polymeri2ation have been reported. Incorporated monomers include styrene and acrylonitrile, styrene, maleic anhydride, vinyl acetate, methyl methacrylate, and vinyHdene chloride (81), acryHc acid (82), and vinyl chloride (81,83,84). When the vinyl chloride-modified epichlorohydrin polymers were used as additives to PVC, impact strength was improved (83,84). 

Two interesting developments should also be noted syndiotactic polypropylene produced by a novel metallocene system and polypropylene grafted with styrene and/or maleic anhydride marketed by Montell as Hivalloy. 

Based on the results of the hydrophobization of po-ly(MA-DP), we applied the hydrophobically grafting technique to poly(maleic acid-fl//-7,l2-dioxaspiro-[5,6]-... 

Els and McGill [48] reported the action of maleic anhydride on polypropylene-polyisoprene blends. A graft copolymer was found in situ through the modifier, which later enhanced the overall performance of the blend. Scott and Macosko [49] studied the reactive and nonreactive compatibilization of nylon-ethylene-propylene rubber blends. The nonreactive polyamide-ethylene propylene blends showed poor interfacial adhesion between the phases. The reactive polyamide-ethylene propylene-maleic anhydride modified blends showed excellent adhesion and much smaller dispersed phase domain size. 

One of the earliest references on compatibilizing a nylon-6-polypropylene blend using maleic anhydride grafted PP (PP-g-MAH) was the work of Ide and Hase-gawa published in 1974 [35]. In their study, the formation of a graft copolymer was confirmed by DSC after solvent extraction of the PP component. Blends with PP-g-MAH... 

Figure 7 Notched impact strength vs. interparticle distance for PBT-maleic anhydride grafted EOR blends. Source Ref. 58.

PP-g-AA - acrylic acid grafted polypropylene PP-g-MAH - maleic anhydride grafted polypropylene PPacr - acrylic acid grafted polypropylene PPmal - maleic anhdride grafted polypropylene PPS - polyphenylene sulfide PS - polystyrene... 

SEBS-g-MA - maleic anhydride grafted styrene (ethyl-... 

---