FIGURE 11.7 Inter-mbber bonding scheme for blending ethylene-propylene-diene monomer (EPDM) with nitrile mbber with a cross-linking agent. (From Naskar, M., Debnath, S.C., and Basu, D.K., Rubber Chem. TechnoL, 75, 309, 2002.)... 

In this paper, we wish to report two different types of elastomer blends, ethylene-propylene-diene terpolymer/polyacety-lene and styrene-diene triblock copolymer/polyacetylene, in the hope that the stability of polyacetylene might be improved by... 

One of the first mechanical thermoplastic IPNs was that prepared by Exxon Chemical and made by melt blending ethylene-propylene (E-P) copolymer or EPDM with polypropylene in the presence of a small amount of peroxide as cross-linking agent. Recently, Shell Chemical... 

Rubber modified polypropylene polypropylene/ethylene propylene rubber blends ethylene propylene rubber, polypropylene blends elastomer modified thermoplastic elastomer modified polypropylene impact modified polypropylene olefin thermoplastic elastomer thermoplastic polyolefc rubber. 

Organic peroxides are used in the polymer industry as thermal sources of free radicals. They are used primarily to initiate the polymerisation and copolymerisation of vinyl and diene monomers, eg, ethylene, vinyl chloride, styrene, acryUc acid and esters, methacrylic acid and esters, vinyl acetate, acrylonitrile, and butadiene (see Initiators). They ate also used to cute or cross-link resins, eg, unsaturated polyester—styrene blends, thermoplastics such as polyethylene, elastomers such as ethylene—propylene copolymers and terpolymers and ethylene—vinyl acetate copolymer, and mbbets such as siUcone mbbet and styrene-butadiene mbbet. 

Acrylonitrile—Butadiene—Styrene. ABS is an important commercial polymer, with numerous apphcations. In the late 1950s, ABS was produced by emulsion grafting of styrene-acrylonitrile copolymers onto polybutadiene latex particles. This method continues to be the basis for a considerable volume of ABS manufacture. More recently, ABS has also been produced by continuous mass and mass-suspension processes (237). The various products may be mechanically blended for optimizing properties and cost. Brittle SAN, toughened by SAN-grafted ethylene—propylene and acrylate mbbets, is used in outdoor apphcations. Flame retardancy of ABS is improved by chlorinated PE and other flame-retarding additives (237). 

Polyethylene is sometimes blended with ethylene-propylene rubber (see Chapter 11). In this application it is most commonly used as an additive to the rubber, which in turn is added to polypropylene to produce rubber-modified... 

In the early stages of development of polypropylene rubbers, particularly butyl rubber, were used to reduce the brittleness of polypropylene. Their use declined for some years with the development of the polypropylene copolymers but interest was greatly renewed in the 1970s. This interest has been centred largely around the ethylene-propylene rubbers which are reasonably compatible in all proportions with polypropylene. At first the main interest was with blends in which the rubber content exceeded 50% of the blend and such materials have been designated as thermoplastic polyolefin elastomers (discussed in Section 11.9.1). There is also increasing interest in compounds with less than 50% rubber, often referred to as elastomer-modified thermoplastics. It is of interest to note... 

Whilst the ASA materials are of European origin, the AES polymers have been developed in Japan and the US. The rubber used is an ethylene-propylene terpolymer rubber of the EPDM type (see Chapter 11) which has a small amount of a diene monomer in the polymerisation recipe. The residual double bonds that exist in the polymer are important in enabling grafting with styrene and acrylonitrile. The blends are claimed to exhibit very good weathering resistance but to be otherwise similar to ABS. 

The use of ABS has in recent years met considerable competition on two fronts, particularly in automotive applications. For lower cost applications, where demands of finish and heat resistance are not too severe, blends of polypropylene and ethylene-propylene rubbers have found application (see Chapters 11 and 31). On the other hand, where enhanced heat resistance and surface hardness are required in conjunction with excellent impact properties, polycarbonate-ABS alloys (see Section 20.8) have found many applications. These materials have also replaced ABS in a number of electrical fittings and housings for business and domestic applications. Where improved heat distortion temperature and good electrical insulation properties (including tracking resistance) are important, then ABS may be replaced by poly(butylene terephthalate). 

Initial materials of this super-tough type were blends of nylon 66 with an ionomer resin (see Chapter 11). More recent materials are understood to be blends of nylon 66 with a modified ethylene-propylene-diene terpolymer rubber (EPDM rubber—also see Chapter 11). One such modification involves treatment of the rubber with maleic anhydride, this reacting by a Diels—Alder or other... 

A manufacturer considering using a thermoplastic elastomer would probably first consider one of the thermoplastic polyolefin rubbers or TPOs, since these tend to have the lowest raw polymer price. These are mainly based on blends of polypropylene and an ethylene-propylene rubber (either EPM or EPDM) although some of the polypropylene may be replaeed by polyethylene. A wide range of blends are possible which may also contain some filler, oil and flame retardant in addition to the polymers. The blends are usually subject to dynamic vulcanisation as described in Section 11.9.1. 

Elastomers, plastics, fabrics, wood and metals can be joined with themselves and with each other using nitrile rubber/epoxy resin blends cured with amines and/or acidic agents. Ethylene-propylene vulcanizates can also be joined using blends of carboxylated nitrile rubber, epoxy resin and a reactive metal filler (copper, nickel, cobalt). However, one of the largest areas of use of nitrile rubber modified epoxy systems is in the printed circuit board area [12]. 

TPEs from blends of rubber and plastics constitute an important category of TPEs. These can be prepared either by the melt mixing of plastics and rubbers in an internal mixer or by solvent casting from a suitable solvent. The commonly used plastics and rubbers include polypropylene (PP), polyethylene (PE), polystyrene (PS), nylon, ethylene propylene diene monomer rubber (EPDM), natural rubber (NR), butyl rubber, nitrile rubber, etc. TPEs from blends of rubbers and plastics have certain typical advantages over the other TPEs. In this case, the required properties can easily be achieved by the proper selection of rubbers and plastics and by the proper change in their ratios. The overall performance of the resultant TPEs can be improved by changing the phase structure and crystallinity of plastics and also by the proper incorporation of suitable fillers, crosslinkers, and interfacial agents. 

Compatibilization along with dynamic vulcanization techniques have been used in thermoplastic elastomer blends of poly(butylene terephthalate) and ethylene propylene diene rubber by Moffett and Dekkers [28]. In situ formation of graft copolymer can be obtained by the use of suitably functionalized rubbers. By the usage of conventional vulcanizing agents for EPDM, the dynamic vulcanization of the blend can be achieved. The optimum effect of compatibilization along with dynamic vulcanization can be obtained only when the compatibilization is done before the rubber phase is dispersed. 

Els and McGill [48] reported the action of maleic anhydride on polypropylene-polyisoprene blends. A graft copolymer was found in situ through the modifier, which later enhanced the overall performance of the blend. Scott and Macosko [49] studied the reactive and nonreactive compatibilization of nylon-ethylene-propylene rubber blends. The nonreactive polyamide-ethylene propylene blends showed poor interfacial adhesion between the phases. The reactive polyamide-ethylene propylene-maleic anhydride modified blends showed excellent adhesion and much smaller dispersed phase domain size. 

Greco et al. [50] studied the effect of the reactive compatibilization technique in ethylene propylene rubber-polyamide-6 blends. Binary blends of polyamide-6-ethylene propylene rubber (EPR) and a ternary blend of polyamide-6-EPR-EPR-g-succinic anhydride were prepared by the melt mixing technique, and the influence of the degree of grafting of (EPR-g-SA) on morphology and mechanical properties of the blends was studied. 

Currently, important TPE s include blends of semicrystalline thermoplastic polyolefins such as propylene copolymers, with ethylene-propylene terepolymer elastomer. Block copolymers of styrene with other monomers such as butadiene, isoprene, and ethylene or ethylene/propy-lene are the most widely used TPE s. Styrene-butadiene-styrene (SBS) accounted for 70% of global styrene block copolymers (SBC). Currently, global capacity of SBC is approximately 1.1 million tons. Polyurethane thermoplastic elastomers are relatively more expensive then other TPE s. However, they are noted for their flexibility, strength, toughness, and abrasion and chemical resistance. Blends of polyvinyl chloride with elastomers such as butyl are widely used in Japan. ... 

---