Butadiene methacrylic acid

Butadiene—Methacrylic Acid Ionomers. Carboxyl groups can readily be introduced into butadiene elastomers by copolymerization, and the effects of partial neutralization have been reported (63—66). The ionized polymers exhibit some degree of fluidity at elevated temperatures, but are not thermoplastic elastomers, and are very deficient in key elastomer properties such as compression set resistance. 

For the styrene-butadiene-methacrylic acid copolymers, meth-acrylic acid was also found in the serum, on the particle surface, and buried inside the particles. At 23% degree of neutralization, less methacrylic acid was found in the serum and on the particle surface than with acrylic acid, i.e., more was buried inside the particle. At 3.0% methacrylic acid, the amount incorporated into the particle was fairly constant, independent of the degree of neutralization. The different distributions of methacrylic and acrylic acids were explained by their different distributions between the monomer-polymer and aqueous phases. Thus these characterization results show the effect of vinyl carboxylic acid type and concentration on the loci of the carboxyl groups. Similar correlations could be made with other systems. 

Toriumi et al(24) found that the ESR spectra of solid state Mh-SPS samples with varying sulfonate concentration could be reconstructed from a linear combinati of two spectra one purportedly due to entirely isolated Mn ions and one due to entirely associated ions. By doing so, these auth s were able to estimaj the relative concentrations of the two Mn states. For the Cu salt of a butadiene-methacrylic acid ionomer, Finerl et al(25) observed two distinct ESR signals at 33856 and another at 47356... 

Isoprene (2-methyl--1,3-butadiene) Methacrylic acid (2-methylpropenic acid) CHj=CH—C(CHj)=CH CH,=C(CHj)COOH... 

ABN rubber (acrylonitrile/butadiene/methacrylic acid, from Ciba Geigy) ... 

Butadiene-methacrylic acid copolymer (0.12 ephr COOH) 100 1600... 

Copolymer of acrylonitrile, acrylate (ester), and styrene Acrylonitrile-butadiene-acrylate copolymer Copolymer of acrylonitrile-butadiene-methyl acrylate Copolymer of acrylonitrile-butadiene-methacrylic acid Elastomeric copolymer from an acrylate (ester) and butadiene, a mbber... 

Additionally to the procedures described earlier, improvements for thermostabilization is copolymerisation of vinyl chloride with suitable monomers. A great number of monomers were investigated to optimize the properties of resins. But only vinyl acetate, vinylidene chloride, ethylene, propylene, acrylonitrile, acrylic acid esters, and maleic acid esters, respectively, are of interest commercially [305,436,437]. The copolymerization was carried out in emulsion, suspension, and solution in connection with water- or oil-soluble initiators, as mentioned elsewhere. Another possibility for modifying PVC is grafting of VC on suitable polymers [305,438], blends of PVC with butadiene/styrene and butadiene/ methacryl acid esters copolymers [433], and polymer-analogous reactions on the macromolecule [439,440] (e.g., chlorination of PVC). 

Elastomer adhesion mechanisms are discussed first from the viewpoint of vulcanization bonding to metals. The approaches of brass plate bonding, bonding with ebonite, with butadiene-methacrylic acid copolymers, and with proprietary adhesives are cursorily reviewed to invoke theories of chemisorption, diffusion, and directed chemical reaction. The time dependency of peel strength as an adhesion response through the vulcanization cycle is cited as a possible indication of mechanism. 

R-to-M Bonding with Butadiene - Methacrylic Acid Copolymers. 

Acrylics. Acetone is converted via the intermediate acetone cyanohydrin to the monomer methyl methacrylate (MMA) [80-62-6]. The MMA is polymerized to poly(methyl methacrylate) (PMMA) to make the familiar clear acryUc sheet. PMMA is also used in mol ding and extmsion powders. Hydrolysis of acetone cyanohydrin gives methacrylic acid (MAA), a monomer which goes direcdy into acryUc latexes, carboxylated styrene—butadiene polymers, or ethylene—MAA ionomers. As part of the methacrylic stmcture, acetone is found in the following major end use products acryUc sheet mol ding resins, impact modifiers and processing aids, acryUc film, ABS and polyester resin modifiers, surface coatings, acryUc lacquers, emulsion polymers, petroleum chemicals, and various copolymers (see METHACRYLIC ACID AND DERIVATIVES METHACRYLIC POLYMERS). 

Acryhc stmctural adhesives have been modified by elastomers in order to obtain a phase-separated, toughened system. A significant contribution in this technology has been made in which acryhc adhesives were modified by the addition of chlorosulfonated polyethylene to obtain a phase-separated stmctural adhesive (11). Such adhesives also contain methyl methacrylate, glacial methacrylic acid, and cross-linkers such as ethylene glycol dimethacrylate [97-90-5]. The polymerization initiation system, which includes cumene hydroperoxide, N,1S7-dimethyl- -toluidine, and saccharin, can be apphed to the adherend surface as a primer, or it can be formulated as the second part of a two-part adhesive. Modification of cyanoacrylates using elastomers has also been attempted copolymers of acrylonitrile, butadiene, and styrene ethylene copolymers with methylacrylate or copolymers of methacrylates with butadiene and styrene have been used. However, because of the extreme reactivity of the monomer, modification of cyanoacrylate adhesives is very difficult and material purity is essential in order to be able to modify the cyanoacrylate without causing premature reaction. 

In these equations I is the initiator and I- is the radical intermediate, M is a vinyl monomer, I—M- is an initial monomer radical, I—M M- is a propagating polymer radical, and and are polymer end groups that result from termination by disproportionation. Common vinyl monomers that can be homo-or copolymeri2ed by radical initiation include ethylene, butadiene, styrene, vinyl chloride, vinyl acetate, acrylic and methacrylic acid esters, acrylonitrile, A/-vinylirnida2ole, A/-vinyl-2-pyrrohdinone, and others (2). 

Organic peroxides are used in the polymer industry as thermal sources of free radicals. They are used primarily to initiate the polymerisation and copolymerisation of vinyl and diene monomers, eg, ethylene, vinyl chloride, styrene, acryUc acid and esters, methacrylic acid and esters, vinyl acetate, acrylonitrile, and butadiene (see Initiators). They ate also used to cute or cross-link resins, eg, unsaturated polyester—styrene blends, thermoplastics such as polyethylene, elastomers such as ethylene—propylene copolymers and terpolymers and ethylene—vinyl acetate copolymer, and mbbets such as siUcone mbbet and styrene-butadiene mbbet. 

Synthetic. The main types of elastomeric polymers commercially available in latex form from emulsion polymerization are butadiene—styrene, butadiene—acrylonitrile, and chloroprene (neoprene). There are also a number of specialty latices that contain polymers that are basically variations of the above polymers, eg, those to which a third monomer has been added to provide a polymer that performs a specific function. The most important of these are products that contain either a basic, eg, vinylpyridine, or an acidic monomer, eg, methacrylic acid. These latices are specifically designed for tire cord solutioning, papercoating, and carpet back-sizing. 

Third Monomers. In order to achieve certain property improvements, nitrile mbber producers add a third monomer to the emulsion polymerization process. When methacrylic acid is added to the polymer stmcture, a carboxylated nitrile mbber with greatly enhanced abrasion properties is achieved (9). Carboxylated nitrile mbber carries the ASTM designation of XNBR. Cross-linking monomers, eg, divinylbenzene or ethylene glycol dimethacrylate, produce precross-linked mbbers with low nerve and die swell. To avoid extraction losses of antioxidant as a result of contact with fluids duriag service, grades of NBR are available that have utilized a special third monomer that contains an antioxidant moiety (10). FiaaHy, terpolymers prepared from 1,3-butadiene, acrylonitrile, and isoprene are also commercially available. 

Copolymerization of methacrylic acid with butadiene and isoprene was photoinitiated by Mn2(CO)io without any halide catalyst [28,29]. The po]ymerization system is accompanied by a Dieis-Alder additive. Cross propagation reaction was promoted by adding trieth-y]aluminum chioride. 

Dimethyl peroxide Diethyl peroxide Di-t-butyl-di-peroxyphthalate Difuroyl peroxide Dibenzoyl peroxide Dimeric ethylidene peroxide Dimeric acetone peroxide Dimeric cyclohexanone peroxide Diozonide of phorone Dimethyl ketone peroxide Ethyl hydroperoxide Ethylene ozonide Hydroxymethyl methyl peroxide Hydroxymethyl hydroperoxide 1-Hydroxyethyl ethyl peroxide 1 -Hydroperoxy-1 -acetoxycyclodecan-6-one Isopropyl percarbonate Isopropyl hydroperoxide Methyl ethyl ketone peroxide Methyl hydroperoxide Methyl ethyl peroxide Monoperoxy succinic acid Nonanoyl peroxide (75% hydrocarbon solution) 1-Naphthoyl peroxide Oxalic acid ester of t-butyl hydroperoxide Ozonide of maleic anhydride Phenylhydrazone hydroperoxide Polymeric butadiene peroxide Polymeric isoprene peroxide Polymeric dimethylbutadiene peroxide Polymeric peroxides of methacrylic acid esters and styrene... 

Partially saponified poly(vinyl acetate) Fully saponified poly(vinyl acetate) Copolymers with crotonic acid Copolymers with vinyl acetate with methacrylic acid with acrylic acid esters with acrylonitrile with styrene with ethyl vinyl ether with butadiene... 

Acrylonitrile-butadiene-styrene (ABS) copolymers Ethylene-methacrylic acid copolymers Styrene-butadiene rubber copolymers (SBR)... 

In 1838 Regnault [15] reported that vinylidene chloride could be polymerized. In 1839 Simon [16] and then Blyth and Hofmann (1845) [17] reported the preparation of polystyrene. These were followed by the polymerization of vinyl chloride (1872) [18], isoprene (1879) [19], methacrylic acid (1880) [20], methylacrylate (1880) [21], butadiene (1911) [22], vinyl acetate (1917) [23], vinyl chloroacetate [23], and ethylene (1933) [24]. Klatte and Rollett [23] reported that benzoyl peroxide is a catalyst for the polymerization of vinyl acetate and vinyl chloroacetate. 

In the agglomeration step, the latexes are partially agglomerated using a core/shell agglomerating agent latex, which consists of an elastomeric 1,3-butadiene/slyrene copolymer core and an ethyl acrylate/methacrylic acid copolymer shell. This partial agglomeration operation should not be confused with a coagulation operation where the emulsion is fully destabilized (13). 

A copolymer derived from monomers comprising a mixture of high density poly(ethylene) (HDPE), a copolymer of ethylene/methacrylic acid, and a synthetic block copolymer rubber such as styrene/butadiene, and... 

The vinyl monomers used in this study, methacrylic acid, methyl methacrylate, acrylic acid, methyl acrylate, and acrylonitrile, as well as the solvents, initiators, and polystyrene were supplied by the Aldrich Chemical Company. The styrene-butadiene block copolymer was supplied by Shell as Kraton D1102, known as SBS this contains approximately 75% butadiene and 25% styrene. 

The stable polymer dispersions with small-sized polymer particles of diameter >60 nm were prepared by dispersion copolymerization of PEO-MA macromonomer with styrene, 2-ethylhexyl acrylate, acrylic and methacrylic acids, and butadiene at 60 °C [79]. The particle size was reported to decrease with increasing macromonomer fraction in the comonomer feed. Besides, it varied with the type of the classical monomer as a comonomer. Tg of polymer product was found to be a function of the copolymer composition, the weight ratio macromonomer/monomer, and monomer type and varied from 50.6 to 220.4 °C. 

ABA ABS ABS-PC ABS-PVC ACM ACS AES AMMA AN APET APP ASA BR BS CA CAB CAP CN CP CPE CPET CPP CPVC CR CTA DAM DAP DMT ECTFE EEA EMA EMAA EMAC EMPP EnBA EP EPM ESI EVA(C) EVOH FEP HDI HDPE HIPS HMDI IPI LDPE LLDPE MBS Acrylonitrile-butadiene-acrylate Acrylonitrile-butadiene-styrene copolymer Acrylonitrile-butadiene-styrene-polycarbonate alloy Acrylonitrile-butadiene-styrene-poly(vinyl chloride) alloy Acrylic acid ester rubber Acrylonitrile-chlorinated pe-styrene Acrylonitrile-ethylene-propylene-styrene Acrylonitrile-methyl methacrylate Acrylonitrile Amorphous polyethylene terephthalate Atactic polypropylene Acrylic-styrene-acrylonitrile Butadiene rubber Butadiene styrene rubber Cellulose acetate Cellulose acetate-butyrate Cellulose acetate-propionate Cellulose nitrate Cellulose propionate Chlorinated polyethylene Crystalline polyethylene terephthalate Cast polypropylene Chlorinated polyvinyl chloride Chloroprene rubber Cellulose triacetate Diallyl maleate Diallyl phthalate Terephthalic acid, dimethyl ester Ethylene-chlorotrifluoroethylene copolymer Ethylene-ethyl acrylate Ethylene-methyl acrylate Ethylene methacrylic acid Ethylene-methyl acrylate copolymer Elastomer modified polypropylene Ethylene normal butyl acrylate Epoxy resin, also ethylene-propylene Ethylene-propylene rubber Ethylene-styrene copolymers Polyethylene-vinyl acetate Polyethylene-vinyl alcohol copolymers Fluorinated ethylene-propylene copolymers Hexamethylene diisocyanate High-density polyethylene High-impact polystyrene Diisocyanato dicyclohexylmethane Isophorone diisocyanate Low-density polyethylene Linear low-density polyethylene Methacrylate-butadiene-styrene... 

Wilkie and co-workers [47, 158] have used TG and TG-FTIR to study grafting of vinyl monomers, such as methacrylic acid, onto styrene-butadiene block rubber (SBS) or ABS... 

Abbreviations y x AFM AIBN BuMA Ca DCP DMA DMS DSC EGDMA EMA EPDM FT-IR HDPE HTV IPN LDPE LLDPE MA MAA MDI MMA PA PAC PB PBT PBuMA PDMS PDMS-NH2 interfacial tension viscosity ratio atomic force microscopy 2,2 -azobis(isobutyronitrile) butyl methacrylate capillary number dicumyl peroxide dynamic mechanical analysis dynamic mechanical spectroscopy differential scanning calorimetry ethylene glycol dimethacrylate ethyl methacrylate ethylene-propylene-diene rubber Fourier transform-infra-red high density polyethylene high temperature vulcanization interpenetrating polymer network low density polyethylene linear low density polyethylene maleic anhydride methacrylic acid 4,4 -diphenylmethanediisocyanate methyl methacrylate poly( amide) poly( acrylate) poly(butadiene) poly(butylene terephtalate) poly(butyl methacrylate) poly(dimethylsiloxane) amino-terminated poly(dimethylsiloxane)... 

Styrene can be copolymerized with many monomers. The following monomers can be used along with styrene in the manufacture of food contact materials a-methylsty-rcne, vinyltoluene, divinylbenzene, acrylonitrile, ethyleneoxide, butadiene, fumaric and maleic acid esters of the mono functional saturated aliphatic alcohols C1-C8, acrylic acid ester and methacrylic acid, maleic acid anhydride, methylacrylamide-methylol ether, vinylmethyl ether, vinylisobutyl ether. Styrene and/or a-methylstyrene and/or vinyltoluene should be the main mixture component in every case. 

---