Emulsion polymerization copolymerization

Emulsion Process. The emulsion polymerization process utilizes water as a continuous phase with the reactants suspended as microscopic particles. This low viscosity system allows facile mixing and heat transfer for control purposes. An emulsifier is generally employed to stabilize the water insoluble monomers and other reactants, and to prevent reactor fouling. With SAN the system is composed of water, monomers, chain-transfer agents for molecular weight control, emulsifiers, and initiators. Both batch and semibatch processes are employed. Copolymerization is normally carried out at 60 to 100°C to conversions of - 97%. Lower temperature polymerization can be achieved with redox-initiator systems (51). 

Almost all synthetic binders are prepared by an emulsion polymerization process and are suppHed as latexes which consist of 48—52 wt % polymer dispersed in water (101). The largest-volume binder is styrene—butadiene copolymer [9003-55-8] (SBR) latex. Most SBRlatexes are carboxylated, ie, they contain copolymerized acidic monomers. Other latex binders are based on poly(vinyl acetate) [9003-20-7] and on polymers of acrylate esters. Poly(vinyl alcohol) is a water-soluble, synthetic biader which is prepared by the hydrolysis of poly(viayl acetate) (see Latex technology Vinyl polymers). 

The reactions of alkyl hydroperoxides with ferrous ion (eq. 11) generate alkoxy radicals. These free-radical initiator systems are used industrially for the emulsion polymerization and copolymerization of vinyl monomers, eg, butadiene—styrene. The use of hydroperoxides in the presence of transition-metal ions to synthesize a large variety of products has been reviewed (48,51). 

Styrene is a colorless Hquid with an aromatic odor. Important physical properties of styrene are shown in Table 1 (1). Styrene is infinitely soluble in acetone, carbon tetrachloride, benzene, ether, / -heptane, and ethanol. Nearly all of the commercial styrene is consumed in polymerization and copolymerization processes. Common methods in plastics technology such as mass, suspension, solution, and emulsion polymerization can be used to manufacture polystyrene and styrene copolymers with different physical characteristics, but processes relating to the first two methods account for most of the styrene polymers currendy (ca 1996) being manufactured (2—8). Polymerization generally takes place by free-radical reactions initiated thermally or catalyticaHy. Polymerization occurs slowly even at ambient temperatures. It can be retarded by inhibitors. 

Random copolymers of vinyl chloride and other monomers are important commercially. Most of these materials are produced by suspension or emulsion polymerization using free-radical initiators. Important producers for vinyl chloride—vinyUdene chloride copolymers include Borden, Inc. and Dow. These copolymers are used in specialized coatings appHcations because of their enhanced solubiUty and as extender resins in plastisols where rapid fusion is required (72). Another important class of materials are the vinyl chloride—vinyl acetate copolymers. Principal producers include Borden Chemicals Plastics, B. F. Goodrich Chemical, and Union Carbide. The copolymerization of vinyl chloride with vinyl acetate yields a material with improved processabihty compared with vinyl chloride homopolymer. However, the physical and chemical properties of the copolymers are different from those of the homopolymer PVC. Generally, as the vinyl acetate content increases, the resin solubiUty in ketone and ester solvents and its susceptibiUty to chemical attack increase, the resin viscosity and heat distortion temperature decrease, and the tensile strength and flexibiUty increase slightly. 

It may also be possible to crosslink the acrylic PSA with the help of multifunctional acrylates or methacrylates [87], These monomers can simply be copolymerized with the balance of the other monomers to form a covalently crosslinked network in one step. Since the resulting polymer is no longer soluble, this typ)e of crosslinking is typically limited to bulk reactions carried out as an adhesive coating directly on the article or in emulsion polymerizations where the crosslinked particles can be dried to a PSA film. 

With some limitations. Single-stage soapless emulsion polymerization can be used for the direct copolymerization of a relatively apolar monomer with a polar... 

DSEP direct soapless emulsion polymerization, SSEC seeded soapless emulsion copolymerization, DDC direct dispersion copolymerization, TDSC two-stage dispersion copolymerization, ATES Allyl trietoxysilane, VTES vinyl trietoxysilane, DMAEM dimethylaminoethyl-methacrylate, CMS chloromethylstyrene, GA glutaraldehyde, AAc Acrylic acid Aam Acrylamide HEMA 2-hydroxyethylmethacrylate. 

The soapless seeded emulsion copolymerization method was used for producing uniform microspheres prepared by the copolymerization of styrene with polar, functional monomers [115-117]. In this series, polysty-rene-polymethacrylic acid (PS/PMAAc), poly sty rene-polymethylmethacrylate-polymethacrylic acid (PS/ PMMA/PMAAc), polystyrene-polyhydroxyethylmeth-acrylate (PS/PHEMA), and polystyrene-polyacrylic acid (PS/PAAc) uniform copolymer microspheres were synthesized by applying a multistage soapless emulsion polymerization process. The composition and the average size of the uniform copolymer latices prepared by multistage soapless emulsion copolymerization are given in Table 11. 

PS/PHEM A particles in micron-size range were also obtained by applying the single-stage soapless emulsion copolymerization method [124]. But, this method provided copolymer particles with an anomalous shape with an uneven surface. PS or PHEMA particles prepared by emulsifier-free emulsion polymerization were also used as seed particles with the respective comonomer to achieve uniform PS/PHEMA or PHEMA/PS composite particles. PS/PHEMA and PHEMA/PS particles in the form of excellent spheres were successfully produced 1 iLitm in size in the same study. 

Utilization of another function of the macroinitiator was tried in emulsion polymerization [30]. An MAI composed of PEG (molecular weight of a segment is 1000) linked with AGP units was confirmed to be usable as a surface active initiator (Inisurf) for preparing PSt-b-PEG [30]. A higher molecular weight block copolymer was obtained in comparison with the case of solution copolymerization. 

Copolymerization of macromonomers formed by backbiting and fragmentation is a second mechanism for long chain branch formation during acrylate polymerization (Section 4.4.3.3). The extents of long and short chain branching in acrylate polymers in emulsion polymerization as a function of conditions have been quantified.20 ... 

Using copolymerization theory and well known phase equilibrium laws a mathematical model is reported for predicting conversions in an emulsion polymerization reactor. The model is demonstrated to accurately predict conversions from the head space vapor compositions during copolymerization reactions for two commercial products. However, it appears that for products with compositions lower than the azeotropic compositions the model becomes semi-empirical. 

Two different emulsion polymerization reactions were Investigated. One was the polymerization of acrylonitrile and methylacrylate (75/25 AN/MA) In the presence of an acrylonitrile elastomer (70/30 BD/AN) to produce a graft resin, llie second was the copolymerization oiE acrylonitrile and styrene (70/30 AN/S). Chromatographic analyses of latex solutions were conducted periodically during both types of polymerization reactions, using acetonitrile as latex solvent and chromatographic mobile phase. 

We have considerable latitude when it comes to choosing the chemical composition of rubber toughened polystyrene. Suitable unsaturated rubbers include styrene-butadiene copolymers, cis 1,4 polybutadiene, and ethylene-propylene-diene copolymers. Acrylonitrile-butadiene-styrene is a more complex type of block copolymer. It is made by swelling polybutadiene with styrene and acrylonitrile, then initiating copolymerization. This typically takes place in an emulsion polymerization process. 

The mechanism of crosslinking emulsion polymerization and copolymerization differs significantly from linear polymerization. Due to the gel effect and, in the case of oil-soluble initiators, monomer droplets polymerize preferentially thus reducing the yield of microgels. In microemulsion polymerization, no monomer droplets exist. Therefore this method is very suitable to form microgels with high yields and a narrow size distribution, especially if oil-soluble initiators are used. 

Anionic complexes, tungsten, 25 386-387 Anionic copolymerization, 7 624-626 block copolymers, 7 645 Anionic emulsifiers, in VDC emulsion polymerization, 25 722 Anionic extractants, 10 750 Anionic flotation, 24 497 Anionic gels, 9 59-60... 

Many commercially important polymers are produced via emulsion polymerization. This is also one of the most common methods to produce dye-doped beads. A dye is added to the mixture of monomers prior to initiating the polymerization and is either noncovalently entrapped or is copolymerized. The second method ensures that no leaching will occur from the particle but requires modification of the dye (typically by providing it with a double bond). This method is most common for preparation of pH-sensitive beads where a pH indicator is entrapped inside cross-linked polyacrylamide particles. The size of the beads can be tuned over a wide range so that preparation of both nano- and microbeads is possible. Despite thorough washing the surfactants are rather difficult to remove completely and their traces can influence the performance of some biological systems. 

Erbil, H.Y., 2000, Vinyl Acetate Emulsion Polymerization and Copolymerization with Acrylic Monomers, CRC, Boca-Raton, FL. 

Over 5.5 billion pounds of synthetic rubber is produced annually in the United States. The principle elastomer is the copolymer of butadiene (75%) and styrene (25) (SBR) produced at an annual rate of over 1 million tons by the emulsion polymerization of butadiene and styrene. The copolymer of butadiene and acrylonitrile (Buna-H, NBR) is also produced by the emulsion process at an annual rate of about 200 million pounds. Likewise, neoprene is produced by the emulsion polymerization of chloroprene at an annual rate of over 125,000 t. Butyl rubber is produced by the low-temperature cationic copolymerization of isobutylene (90%) and isoprene (10%) at an annual rate of about 150,000 t. Polybutadiene, polyisoprene, and EPDM are produced by the anionic polymerization of about 600,000, 100,000, and 350,000 t, respectively. Many other elastomers are also produced. 

---