Alkyd resins paint coatings

Oil-base (including oil-modified alkyd resin) paint films should not be used in alkaline environments as the paint will deteriorate owing to saponification alkali-resistant coatings are provided by some cellulose ethers, e.g. ethyl cellulose, certain polyurethane, chlorinated rubber, epoxy, p.v.c./ p.v.a. copolymer, or acrylic-resin-based paints. In particular, aluminium and its alloys should be protected by alkali-resistant coatings owing to the detrimental effects of alkali on these metals. 

Butyl glycolate reduces the viscosity of alkyd resin paints. It improves the flow properties and gloss in air-drying and oven-drying paints, especially in coil coating and leather lacquers. It is also used to lower the film-forming temperature in polyfvinyl acetate) dispersions. 

Uses Antiskinning agent for air-drying alkyds, air-drying oils, oil-modified PU resins, paints/coatings that dry by oxidation Features Prevents formation of top film/skin on storage minimal effect on drying and film props. 

Uses Alkyd resins paints dynamite ester gums perfumery lubricants softener bacteriostat penetrant emollient antifreeze prod, of antibiotics plasticizer for regenerated cellulose film, sodium silicate foundry resins solvent (printing inks) humectant (tobacco, starch adhesives, textile sizes) solvent, humectant, plasticizer, bodying agent for foods, food pkg., cosmetics plasticizer, solvent, solubilizer, preservative for pharmaceuticals PU crosslinker heat costabilizer (PVC) sweetener preservative plasticizer in food-contact coatings Use Level 0.2-65.7% (topicals), 1-50% (liq. orals), 50% (parenterals), 7-10% (dentifrices), 0.5-3.0% (ophthalmics)... 

General paint coating systems are a combination of oil-type rust preventative primer and long oil alkyd resin paint or chlorinated rubber paint (intermediate and overcoats) with a total thickness of less than 150 p,m. These are applied in relatively mild atmospheres such as rural, mountain, and city. 

Alkoxysilanes Alkyd coatings Alkyd paints Alkyd resins... 

The most important industrial use of pentaerythritol is in a wide variety of paints, coatings, and varnishes, where the cross-linking capabiUty of the four hydroxy groups is critical. Alkyd resins (qv) are produced by reaction of pentaerythritol with organic acids such as phthaUc acid or maleic acid and natural oil species. 

Vinyl resins ie, copolymers of vinyl chloride and vinyl acetate which contain hydroxyl groups from the partial hydrolysis of vinyl acetate and/or carboxyl groups, eg, from copolymerized maleic anhydride, may be formulated with alkyd resins to improve their appHcation properties and adhesion. The blends are primarily used in making marine top-coat paints. 

Thermoplastic polyamides are used in coatings to modify alkyd resins (qv) in thixotropic systems (238) and to plasticize nitroceUulose lacquers (239). DETA-taH oil fatty acid-based polyamides are suggested for use as corrosion inhibitors in alkyd paints (240). Printing inks for fiexo-gravure appHcation on certain paper, film and foil webs rely on EDA- and PDA-based polyamides for their specific performance (241). 

Stripping of top coats soaked by rain or sea-water has occurred with alkyd-resin-based paint systems, mainly on ships. The risk of such intercoat failure is reduced if the time interval between application of coats is reduced, but is best controlled by modification of the alkyd resin with a proportion of a different material. 

By depolymerizing PET waste with a polyol and subsequently condensing the oligomeric product with a polycarboxylic acid or anhydride, polyester resins are produced which have wide industrial applications. Depending on the polyol and polycarboxylic acid or anhydride used, saturated resins, alkyd resins, or unsaturated resins are obtained. PET wastes have been used for the production of alkyd resins in water thinnable paints. The materials obtained from the reaction of PET with a mixture of fatty acids high in linoleic acid content and trimethylolethane have been used in the preparation of water-dispersible coatings. Products of the depolymerization of PET with trimethylolpropane and pentaerythritol are used in the manufacture of high-solids paints. In the first step, PET is depolymerized with trimethylopropane and pentaerythritol at temperatures of 230-240°C. The final paint compositions contain 30-50% of PET depolymerization products.12... 

There are over 400 different commercial alkyd resin formulations based on phthalic anhydride used in the coatings business. Alkyd resins for paints are made by reacting phthalic anhydride with a poly-alcohol (usually from naturally occurring sources rather than synthetic) that contains unreacted double bonds. The paint dries by the resin crosslinking through reaction of the double bonds under the influence of oxygen in the air. 

These are the most important components of paint. Coatings can be either clear or opaque (containing pigments) and either solvent- or water-based. With solvent-based paints, after application, most of the solvent is lost through evaporation. These solvent-based coatings are mostly alkyds (name derived from alkyl/acid) or modified alkyd resins. Normally they contain 30% polymer solids higher solids content is limited by the increasing viscosity of the system. 

Microgels have also been detected as a component of alkyd resins, an early but still important binder of organic coatings [316-321] and are accountable for their ability to fill pores, fissures and other irregularities of the substrate such as wood. This property may be explained by the size of the microgels which prevents the paint becoming soaked up by the substrate. 

Marine coatings Organic coatings for corrosion control Paint acrylic ester polymers, 7 388-389 adhesion, 7 90-92 advanced ceramic, 7 704-705 alkanolamines from olefin oxides and ammonia, 2 136 alkyd resins, 2.T67-168 amino acid resin applications, 2 635—637 anticorrosion, 25 134 anticorrosion metallic, 7 713-714... 

Together, antifreeze, PET, and polyester polymers account for about 98% of the ethylene glycol produced in the United States. It is also used sometimes as a deicer for aircraft surfaces. The two hydroxyl groups in the EG molecule also make EG suitable for the manufacture of surfactants and in latex paints. Other applications include hydraulic brake fluid, the manufacture of alkyd resins for surface coatings, and stabilizers for water dispersions of urea-formaldehyde and melamine-formaldehyde The hygroscopic properties (absorbs moisture from the air) make EG useful as a humectant for textile fibers, paper, leather, and adhesives treatment. 

---