Paint film

The principal chemical markets for acetylene at present are its uses in the preparation of vinyl chloride, vinyl acetate, and 1,4-butanediol. Polymers from these monomers reach the consumer in the form of surface coatings (paints, films, sheets, or textiles), containers, pipe, electrical wire insulation, adhesives, and many other products which total biUions of kg. The acetylene routes to these monomers were once dominant but have been largely displaced by newer processes based on olefinic starting materials. 

Miscellaneous, New, and Developmental Antimicrobial Agents. Table 11 shows some of the antimicrobials that do not neady fit into the principal families. Acrolein (qv) is a unique chemical used for secondary oil recovery (43). Biobor has become the antimicrobial addition of choice for aviation fuels (44). Cbloropbtbalonil (tetrachloroisophthalnitrile [1897-45-6]) is a significant agricultural fungicide, in addition to being one of the most important latex paint film preservatives (producer, ISK). 

Oxidation. Inks that dry by oxidation behave much like oil paint films and dry by means of the reaction of drying oils (qv) with oxygen. They contain metallic driers, which catalyze the absorption of oxygen by the drying oil (see Driers and metallic soaps Paint). 

Whereas semigloss paints can use only one extender, dat paints, especially interior, can use combinations of three or more. Gloss paints typically do not use extenders, which decrease gloss. As a result, gloss paints lack the hardening effect of extenders and must rely on harder binders for adequate durabihty. Other types of extenders used in paints can have functional properties such as corrosion resistance, mildew resistance, and film-hardening effects. Thek functional properties result from thek reactive nature in the paint film. Zinc oxide is an example of a functional extender that contributes to these properties in a paint film. 

Solvents. Solvents in house paints serve several essential purposes. They keep the binder dispersed or dissolved and the pigments dispersed in an easy-to-use state. Solvents allow the paint to be appHed in the correct thickness and uniformity, and evaporate from the paint film after the paint is apphed. Solvent choice is limited mainly to a solvent that is compatible with the binder system and that has the desked evaporation rate and toxicity profile. The volatility or evaporation rate of a solvent determines to a large extent the open-time and dry-time properties of a paint (6). 

PyCis usuaHy expressed in percentage, but the % sign is often omitted. Although many additives in the paint formulation are nonvolatile, they are often omitted from this calculation, because they represent a smaH fraction of the volume of a newly formed paint film and, in exterior paints, are often water-soluble materials leached out by rainfaH, and therefore wHl probably not factor into the long-term performance of the paint film. 

A third criterion for the proper formulation of house paints is volume soHds level. Paint with low volume soHds are characterized by poor adhesion and poor exterior durabiUty. A low volume soHds paint film does not have the tensile strength properties necessary for good adhesion found in a higher volume soHds paint (10). Also, any slight dismption or imperfection in the dried paint film or in the appHcation of a low volume soHds paint can result in poor durabiHty properties. 

The characteristics of interior paints that require testing and analysis include hiding and appearance, package stabiHty, adhesion, spatter resistance, flow and leveling, color and sheen uniformity, touch-up, stain removal, burnish resistance, and block and print resistance. A popular test that assesses the wet abrasion resistance of an interior paint is to measure its scmb resistance. A mechanical device is used to scmb a paint film of a specified thickness with a standard bmsh and abrasive cleanser suspension. The number of scmb cycles (back and forth movements of the weighted bmsh) at various end points (first cut through, or 50% removal of the film) is then recorded. Scmb resistance usually holds steady or decreases slightly as PVC is increased, but drops quickly once the CPVC is exceeded in a paint formulation. 

Displacement of a volatile with a nonvolatile alcohol is an important reaction for curing paint films with amino cross-linkers and amino resias on textile fabrics or paper. FoUowiag is an example of a methoxymethyl group on an amino resia reacting with a hydroxyl group of a polymer chain. 

Titanates react with ester groups ki paint vehicles, eg, linseed oil, tuna oil, and alkyds, and with hydroxy groups, eg, ki caster oil and some alkyds, to prevent wrinkling of paint films (104,447). 

Zinc compounds are generally colorless unless the other component, eg, chromate, is colored. The lack of color of most zinc compounds in visible light is a great advantage in that they do not color paint films, plastics, mbber, cosmetics, etc. However, when excited by various types of radiation and at various temperatures, zinc oxide, sulfide, selenide [1315-09-9], and related compounds exhibit luminescence, ie, they emit colored light (see Luminescent materials). Zinc-based phosphors can be produced in many colors, depending upon the added dopants. They are used in television tubes, luminescent glasses, and various specialty products. 

The ultrafine siUcon carbide produced in an electric arc is used as an insulation in cryogenic appHcations (152) (see Cryogenics). It generally increases the wear resistance of the paint film when added to paint formulations. 

Paint Driers and Polymer Additives. Paints based on alkyd resins (qv) dry by the oxidation and cross-linking of unsaturated side chains. Metal catalysts are included in paint formulations to promote this drying. Cerium carboxylates, eg, the naphthenate, are used as through driers, ie, to promote drying in the body of the paint film rather than at the film s surface (44). 

Anchor Pattern (Surface Profile)—the shape and amplitude of the profile of blast-cleaned or grooved steel, which influences the bond between metallic or paint films and the substrate. 

Similar considerations also apply to the dielectric films formed on the metal surface during anodising, and, for example, in the case of the valve metals (Al, Ti, Ta, Nb, etc.) IR drops of hundreds of volts may be produced by the anodic oxide film formed on the metal surfaces. Paint films applied to a metal surface also exert resistance control see Section 14.3). 

---