Acrylates effects

A tandem radical addition/cyclization process has been described for the formation of benzindolizidine systems from l-(2-iodoethyl)indoles and methyl acrylate <00TL10181>. In this process, sun-lamp irradiation of a solution of the l-(2-iodoethyl)ethylindoles 149 in refluxing benzene containing hexamethylditin and methyl acrylate effects intermolecular radical addition to the activated double bond leading to the stabilized radical 150. Intramolecular cyclization to the C-2 position of the indole nucleus then affords the benzindolzidine derivatives 151 after rearomatization of the tricyclic radical. 

STARCH- -P0LY(METHYL ACRYLATE)—EFFECTS OF GRAFT LEVEL AND MOLECULAR WEIGHT ON TENSILE STRENGTH... 

Minari RJ, Goikoetxea M, Beristain, I, Paulis M, Barandiaran MJ, Asua JM. Post-polymerization of waterborne alkyd/ acrylics. Effect on polymer architecture and particle morphology. Polymer 2009 50 5892-5900. 

Manahan, a. R. Photolym of poly (tert-butyl acrylate) in the region of the glass transifron temperature. J. Polymer Sci. Part A-1, 4, 2381 (1966). — Photochemistry of poly (tert-butyl acrylate). Effect of ester spatial conformation on the cydoelimination process. J. Polymer Sci. Part A-1, 5, 2333 (1967). 

Additives acting on the pour point also modify the crystal size and, in addition, decrease the cohesive forces between crystals, allowing flow at lower temperatures. These additives are also copolymers containing vinyl esters, alkyl acrylates, or alkyl fumarates. In addition, formulations containing surfactants, such as the amides or fatty acid salts and long-chain dialkyl-amines, have an effect both on the cold filter plugging point and the pour point. 

The solvent effect on the diastereofacial selectivity in the reactions between cyclopentadiene and (lR,2S,5R)-mentyl acrylate is dominated by the hydrogen bond donor characteristics of the solvent... 

Apart from the thoroughly studied aqueous Diels-Alder reaction, a limited number of other transformations have been reported to benefit considerably from the use of water. These include the aldol condensation , the benzoin condensation , the Baylis-Hillman reaction (tertiary-amine catalysed coupling of aldehydes with acrylic acid derivatives) and pericyclic reactions like the 1,3-dipolar cycloaddition and the Qaisen rearrangement (see below). These reactions have one thing in common a negative volume of activation. This observation has tempted many authors to propose hydrophobic effects as primary cause of ftie observed rate enhancements. 

AH the common monobasic (107) and dibasic esters (108) of tetrahydrofurfuryl alcohol have been prepared by conventional techniques the dibasic esters and some of the mono esters are effective as primary or secondary plasticizers for vinyl polymers. Tetrahydrofurfuryl acrylate [2399-48-6] and methacrjiate [2455-24-5] specialty monomers, have been produced by carbonylation (nickel carbonyl and acetylene) of the alcohol (109) as weU as by direct esterification (110—112) and ester interchange (111). 

Pure dry reactants are needed to prevent catalyst deactivation effective inhibitor systems are also desirable as weU as high reaction rates, since many of the specialty monomers are less stable than the lower alkyl acrylates. The alcohol—ester azeotrope (8) should be removed rapidly from the reaction mixture and an efficient column used to minimize reactant loss to the distillate. After the reaction is completed, the catalyst may be removed and the mixture distilled to obtain the ester. The method is particularly useful for the preparation of functional monomers which caimot be prepared by direct esterification. 

Repeated exposures of animals to high (near-lethal) concentrations of vapors result in inflammation of the respiratory tract, as weU as degenerative changes in the Hver, kidneys, and heart muscle. These effects arise at concentrations far above those causing irritation. Such effects have not been reported in humans. The low odor threshold and irritating properties of acrylates cause humans to leave a contaminated area rather than tolerate the irritation. 

In normal practice, inhibitors such as hydroquinone (HQ) [123-31 -9] or the monomethyl ether of hydroquinone (MEHQ) [150-76-5] are added to acrylic monomers to stabilize them during shipment and storage. Uninhibited acrylic monomers should be used prompdy or stored at 10°C or below for no longer than a few weeks. Improperly iahibited monomers have the potential for violent polymerizations. HQ and MEHQ require the presence of oxygen to be effective inhibitors therefore, these monomers should be stored in contact with air and not under inert atmosphere. Because of the low concentration of inhibitors present in most commercial grades of acrylic monomers (generally less than 100 ppm), removal before use is not normally required. However, procedures for removal of inhibitors are available (67). 

Acrylate polymerizations are markedly inhibited by oxygen therefore, considerable care is taken to exclude air during the polymerization stages of manufacturing. This inhibitory effect has been shown to be caused by copolymerization of oxygen with monomer, forming an alternating copolymer (81,82). 

The molecular weight of a polymer can be controlled through the use of a chain-transfer agent, as well as by initiator concentration and type, monomer concentration, and solvent type and temperature. Chlorinated aUphatic compounds and thiols are particularly effective chain-transfer agents used for regulating the molecular weight of acryUc polymers (94). Chain-transfer constants (C at 60°C) for some typical agents for poly(methyl acrylate) are as follows (87) ... 

The preparation of flocked fabric using acryflc adhesives is detailed in Reference 198. In flocking, cut fibers are bonded to an adhesive-coated fabric to achieve both a decorative and a functional effect. Acrylics can be tailored to provide the unique balance between softness and durability required for this... 

Unlike most crystalline polymers, PVDF exhibits thermodynamic compatibiUty with other polymers (133). Blends of PVDF and poly(methyl methacrylate) (PMMA) are compatible over a wide range of blend composition (134,135). SoHd-state nmr studies showed that isotactic PMMA is more miscible with PVDF than atactic and syndiotactic PMMA (136). MiscibiUty of PVDF and poly(alkyl acrylates) depends on a specific interaction between PVDF and oxygen within the acrylate and the effect of this interaction is diminished as the hydrocarbon content of the ester is increased (137). Strong dipolar interactions are important to achieve miscibility with poly(vinyhdene fluoride) (138). PVDF blends are the object of many papers and patents specific blends of PVDF and acryflc copolymers have seen large commercial use. 

Derivatives of hemicellulose components have properties similar to the ceUulosic equivalents but modified by the effects of thek lower molecular weight, more extensive branching, labile constituents, and more heterogeneous nature. Acetates, ethers, carboxymethylxylan (184), and xylan—poly(sodium acrylate) (185) have been prepared. 

Heteroatom functionalized terpene resins are also utilized in hot melt adhesive and ink appHcations. Diels-Alder reaction of terpenic dienes or trienes with acrylates, methacrylates, or other a, P-unsaturated esters of polyhydric alcohols has been shown to yield resins with superior pressure sensitive adhesive properties relative to petroleum and unmodified polyterpene resins (107). Limonene—phenol resins, produced by the BF etherate-catalyzed condensation of 1.4—2.0 moles of limonene with 1.0 mole of phenol have been shown to impart improved tack, elongation, and tensile strength to ethylene—vinyl acetate and ethylene—methyl acrylate-based hot melt adhesive systems (108). Terpene polyol ethers have been shown to be particularly effective tackifiers in pressure sensitive adhesive appHcations (109). 

Peioxydicaibonates are efficient polymerization initiators for most vinyl monomer polymerizations, especially for monomers such as acrylates, ethylene, and vinyl chloride. They are particularly good initiators for less reactive monomers such as those containing aHyl groups. They are also effective for curing of unsaturated polyester mol ding resins. 

Methacryhc acid and its ester derivatives are Ctfjy -unsaturated carbonyl compounds and exhibit the reactivity typical of this class of compounds, ie, Michael and Michael-type conjugate addition reactions and a variety of cycloaddition and related reactions. Although less reactive than the corresponding acrylates as the result of the electron-donating effect and the steric hindrance of the a-methyl group, methacrylates readily undergo a wide variety of reactions and are valuable intermediates in many synthetic procedures. 

T is the glass-transition temperature at infinite molecular weight and is the number average molecular weight. The value of k for poly(methyl methacrylate) is about 2 x 10 the value for acrylate polymers is approximately the same (9). A detailed discussion on the effect of molecular weight on the properties of a polymer may be found in Reference 17. 

The versatility of this reaction is extended to a variety of aldehydes. The bisphenol derived from 2,6-di-/ f2 -butylphenol and furfural, (25) where R = furfuryl (13), is also used as an antioxidant. The utility of the 3,5-di-/ f2 -butyl-4-hydroxyben2yl moiety is evident in stabili2ets of all types (14), and its effectiveness has spurred investigations of derivatives of hindered alkylphenols to achieve better stahi1i2ing quaUties. Another example is the Michael addition of 2,6-di-/ f2 -butyl phenol to methyl acrylate. This reaction is carried out under basic conditions and yields methyl... 

Specifically MSA has been found to be more effective than -toluenesulfonic acid and sulfuric acid in preparing dioctyl phthalate (405). A U.S. patent also discloses its use to prepare light-colored fatty esters (406). It is also important as a catalyst to prepare acrylates, methacrylates, adipates, phthalates, trimeUitates, thioglycolates, and other esters. 

---