Polymerization processes residence time

Partly aromatic copoly(amide)s prepared by conventional processes have triamine contents greater than 0.5%. This effects a deterioration in the product quality and to problems in preparation by a continuous method. For example, dihexamethylenetriamine, formed from HMD is used in the preparation. Copoly(amide)s with a low trianune content have the same solution viscosity but lower melt viscosities compared with products of the same composition which have a higher triamine content. The processability and the product properties are significantly improved by a low triamine content. The dimerization of the diamine can be suppressed by using special methods of polymerization. Short residence times in the high-temperature stage of the polycondensation process suppress the formation of triamines. ... [Pg.399]

Further consideration of the origin of different topologies caused by the process conditions include heat and mass transfer effects. Heat and mass transfer limitations are more easily present in the semi-batch slurry polymerizations, where residence times are... [Pg.208]

Industrial manufacture of LLDPE, based on slurry polymerization in hexane, in a series of continuous stirred tank reactors using 1-butene as the comonomer is known. Solution polymerization of LLDPE in cyclohexane under elevated temperature and pressure using 1-octene has also been practiced industrially. In all these manufacturing processes, residence time of the reactants in the reactors is an important consideration. [Pg.196]

The majority of thermal polymerizations are carried out as a batch process, which requires a heat-up and a cool down stage. Typical conditions are 250—300°C for 0.5—4 h in an oxygen-free atmosphere (typically nitrogen) at approximately 1.4 MPa (200 psi). A continuous thermal polymerization has been reported which utilizes a tubular flow reactor having three temperature zones and recycle capabiHty (62). The advantages of this process are reduced residence time, increased production, and improved molecular weight control. Molecular weight may be controlled with temperature, residence time, feed composition, and polymerizate recycle. [Pg.355]

Some slurry processes use continuous stirred tank reactors and relatively heavy solvents (57) these ate employed by such companies as Hoechst, Montedison, Mitsubishi, Dow, and Nissan. In the Hoechst process (Eig. 4), hexane is used as the diluent. Reactors usually operate at 80—90°C and a total pressure of 1—3 MPa (10—30 psi). The solvent, ethylene, catalyst components, and hydrogen are all continuously fed into the reactor. The residence time of catalyst particles in the reactor is two to three hours. The polymer slurry may be transferred into a smaller reactor for post-polymerization. In most cases, molecular weight of polymer is controlled by the addition of hydrogen to both reactors. After the slurry exits the second reactor, the total charge is separated by a centrifuge into a Hquid stream and soHd polymer. The solvent is then steam-stripped from wet polymer, purified, and returned to the main reactor the wet polymer is dried and pelletized. Variations of this process are widely used throughout the world. [Pg.384]

The second type of solution polymerization concept uses mixtures of supercritical ethylene and molten PE as the medium for ethylene polymerization. Some reactors previously used for free-radical ethylene polymerization in supercritical ethylene at high pressure (see Olefin POLYMERS,LOW DENSITY polyethylene) were converted for the catalytic synthesis of LLDPE. Both stirred and tubular autoclaves operating at 30—200 MPa (4,500—30,000 psig) and 170—350°C can also be used for this purpose. Residence times in these reactors are short, from 1 to 5 minutes. Three types of catalysts are used in these processes. The first type includes pseudo-homogeneous Ziegler catalysts. In this case, all catalyst components are introduced into a reactor as hquids or solutions but form soHd catalysts when combined in the reactor. Examples of such catalysts include titanium tetrachloride as well as its mixtures with vanadium oxytrichloride and a trialkyl aluminum compound (53,54). The second type of catalysts are soHd Ziegler catalysts (55). Both of these catalysts produce compositionaHy nonuniform LLDPE resins. Exxon Chemical Company uses a third type of catalysts, metallocene catalysts, in a similar solution process to produce uniformly branched ethylene copolymers with 1-butene and 1-hexene called Exact resins (56). [Pg.400]

Eastman Chemical has utilized a unique, high temperature solution process for propylene polymerization. Polymerization temperatures are maintained above 150°C to prevent precipitation of the isotactic polypropylene product in the hydrocarbon solvent. At these temperatures, the high rate of polymerization decreases rapidly, requiring low residence times (127). Stereoregularity is also adversely affected by high temperatures. Consequentiy, the... [Pg.414]

Anionic polymerization offers fast polymerization rates on account of the long life-time of polystyryl carbanions. Early studies have focused on this attribute, most of which were conducted at short reactor residence times (< 1 h), at relatively low temperatures (10—50°C), and in low chain-transfer solvents (typically benzene) to ensure that premature termination did not take place. Also, relatively low degrees of polymerization (DP) were typically studied. Continuous commercial free-radical solution polymerization processes to make PS, on the other hand, operate at relatively high temperatures (>100° C), at long residence times (>1.5 h), utilize a chain-transfer solvent (ethylbenzene), and produce polymer in the range of 1000—1500 DP. [Pg.517]

Continuous polymerization in a staged series of reactors is a variation of this process (82). In one example, a mixture of chloroprene, 2,3-dichloro-l,3-butadiene, dodecyl mercaptan, and phenothiazine (15 ppm) is fed to the first of a cascade of 7 reactors together with a water solution containing disproportionated potassium abietate, potassium hydroxide, and formamidine sulfinic acid catalyst. Residence time in each reactor is 25 min at 45°C for a total conversion of 66%. Potassium ion is used in place of sodium to minimize coagulum formation. In other examples, it was judged best to feed catalyst to each reactor in the cascade (83). [Pg.541]

Emulsions Emulsions have particles of 0.05 to 5.0 [Lm diameter. The product is a stable latex, rather than a filterable suspension. Some latexes are usable directly, as in paints, or they may be coagulated by various means to produce massive polymers. Figures 23-23d and 23-23 show bead and emulsion processes for vinyl chloride. Continuous emulsion polymerization of outadiene-styrene rubber is done in a CSTR battery with a residence time of 8 to 12 h. Batch treating of emulsions also is widely used. [Pg.2102]

A factor in addition to the RTD and temperature distribution that affects the molecular weight distribution (MWD) is the nature of the chemical reaciion. If the period during which the molecule is growing is short compared with the residence time in the reactor, the MWD in a batch reactor is broader than in a CSTR. This situation holds for many free radical and ionic polymerization processes where the reaction intermediates are very short hved. In cases where the growth period is the same as the residence time in the reactor, the MWD is narrower in batch than in CSTR. Polymerizations that have no termination step—for instance, polycondensations—are of this type. This topic is treated by Denbigh (J. Applied Chem., 1, 227 [1951]). [Pg.2102]

During the high-temperature operations, intermolecular hydrogen transfer reactions occur, transforming some indene to indane. The high indane concentration in the resin feedstock causes low yield and poor quality in the polymerization process. The indene loss can be reduced by decreasing the temperature and the residence time during distillation. [Pg.604]

On an industrial scale, PA-6 is synthesized from e-caprolactam with water as the initiator. The process is very simple if the reaction is earned out at atmospheric pressure. The polymerization is earned out in a VK-reactor (Fig. 3.23), which is a continuous reactor without a stirrer, with a residence time of 12-24 h at temperatures of 260-280°C.5,28 Molten lactam, initiator (water), and chain terminator (acetic acid) are added at the top and the polymer is discharged at the bottom to an extruder. In this extruder, other ingredients such as stabilizers, whiteners, pigments, and reinforcing fillers are added. The extruded thread is cooled in a water bath and granulated. The resultant PA-6 still contains 9-12%... [Pg.174]

The color of the polymer can also be affected by inappropriate reaction conditions in the polymerization process, such as temperature, residence time, deposits of degraded polymer or the presence of oxygen. Degradation of polyesters and the generation of chromophores are thermally effected [29b, 29c, 39], The mechanism of thermal decomposition is based on the pyrolysis of esters and the formation of unsaturated compounds, which can then polymerize into colored products. It can be assumed that the discoloration takes place via polymerization of the vinyl ester end groups or by further reaction of AA to polyene aldehydes. [Pg.483]

Radical chain polymerization of ethylene to polyethylene is carried out at high pressures of 120-300 MPa (17,000-43,000 psi) and at temperatures above the Tm of polyethylene (Fig. 3-18) [Doak, 1986]. Batch processes are not useful since the long residence time gives relatively poor control of product properties. Long-chain branching due to intermolecular chain transfer becomes excessive with deleterious effects on the physical properties. Continuous processes allow better control of the polymerization. [Pg.300]

The polymerization temperature is in the range of 50-80°C. The ethene pressure is 2-8 M Pa. In the case of a continuous polymerization process, the average residence time should be in the range of 3-4 h (1). [Pg.190]

A continuous bulk polymerization process with three reaction zones in series has been developed. The degree of polymerization increases from the first reactor to the third reactor. Examples of suitable reactors include continuous stirred tank reactors, stirred tower reactors, axially segregated horizontal reactors, and pipe reactors with static mixers. The continuous stirred tank reactor type is advantageous, because it allows for precise independent control of the residence time in a given reactor by adjusting the level in a given reactor. Thus, the residence time of the polymer mixtures can be independently adjusted and optimized in each of the reactors in series (8). [Pg.271]

A possible design of an extruder for reactive processing is shown in Fig. 4.34.240 Two screws are installed on the same axis inside a common barrel 1 but they have independent drives. This design eliminates stagnation zones, where the extruder is obstructed by the polymeric product. Independent drives for both screws permits the choice of optimal rotation speeds, i. e., to synchronize the polymerization rate with the residence times of the reactive mass in both stages of the process. [Pg.168]

Reactive extruders and extrusion dies of different designs can be easily included in standard technological scheme of polymer production plants, such as those for polycaproamide synthesis, as shown in Fig. 4.39. In this case, a reactive material premixed in a tank 1 is fed into a static device 2 for prepolymerization, where part of the polymerization process takes place. Then the reactive mixture enters the extruder-reactor 3. The necessary temperature distribution is maintained along the extruder. Transfer of the reactive mass proceeds by a system of two coaxial screws mounted in series in a common barrel. Controlling the relative rotation speed of both screws provides the necessary residence time for the reactive mass in the extrader, so that the material reaching the outlet section of the die is a finished polymer. [Pg.171]

As in any type of polymerization, a batch reaction is not as commercially attractive as a continuous polymerization process that can produce larger quantities of polymer in the same amount of time. The first continuous polymerizations in C02 were reported (Charpentier et al., 1999) with the monomers acrylic acid and vinylidene fluoride. The vinylidene fluoride polymerization was extensively studied at 75 °C, 275 bar. The polymerizations were run with residence times that varied between 15 and 40 min in a continuous-stirred-tank reactor before collection in a filter. The maximum rate of polymerization was determined to be 19 x 10 5 mol L-1s-1. Future research will move toward continuous removal of polymer, recycling of unreacted monomer and C02, and expansion to other monomers. [Pg.154]


See other pages where Polymerization processes residence time is mentioned: [Pg.34]    [Pg.65]    [Pg.233]    [Pg.272]    [Pg.65]    [Pg.77]    [Pg.503]    [Pg.304]    [Pg.283]    [Pg.821]    [Pg.93]    [Pg.336]    [Pg.220]    [Pg.115]    [Pg.549]    [Pg.3]    [Pg.795]    [Pg.34]    [Pg.26]    [Pg.772]    [Pg.233]    [Pg.272]    [Pg.87]    [Pg.428]    [Pg.117]    [Pg.145]    [Pg.166]    [Pg.167]    [Pg.199]    [Pg.129]   
See also in sourсe #XX -- [ Pg.330 , Pg.332 , Pg.333 ]




SEARCH



Polymerization times

Process time

Processing time

Resid processing

© 2024 chempedia.info