Adhesive, adhesion promoters

Specific adhesion or chemisorption occurs when various types of primary bonds (ionic, metallic, covalent) are formed between the two surfaces, e.g. coating and substrate. This is typically achieved with the use of adhesion promoters. Adhesion promoters indeed often bind to surfaces with primary bonds. 

The use of hydroxyethyl (also hydroxypropyl) methacrylate as a monomer permits the introduction of reactive hydroxyl groups into the copolymers. This offers the possibility for subsequent cross-linking with an HO-reactive difunctional agent (diisocyanate, diepoxide, or melamine-formaldehyde resin). Hydroxyl groups promote adhesion to polar substrates. 

Most of the polymer s characteristics stem from its molecular stmcture, which like POE, promotes solubiUty in a variety of solvents in addition to water. It exhibits Newtonian rheology and is mechanically stable relative to other thermoplastics. It also forms miscible blends with a variety of other polymers. The water solubiUty and hot meltable characteristics promote adhesion in a number of appHcations. PEOX has been observed to promote adhesion comparable with PVP and PVA on aluminum foil, cellophane, nylon, poly(methyl methacrylate), and poly(ethylene terephthalate), and in composite systems improved tensile strength and Izod impact properties have been noted. 

Hybrid Circuits. The use of parylenes as a hybrid circuit coating is based on much the same rationale as its use in circuit boards. A significant distinction Hes in obtaining adhesion to the ceramic substrate material, the success of which determines the eventual performance of the coated part. Adhesion to the ceramic must be achieved using adhesion promoters, such as the organosilanes. 

To an experienced operator trained in the handling of industrial chemicals, the dimers present Httle cause for concern in handling or storage. The finished polymer coating presents even less of a health problem contact with the reactive monomer is unlikely. In the ancillary operations, such as cleaning or adhesion promotion, the operator must observe suitable precautions. Before using the process chemicals, operators must read and understand the current Material Safety Data Sheets, which are available from the manufacturers. 

The surface of PTFE articles is sHppery and smooth. Liquids with surface tensions below 18 mN/m(=dyn/cm) are spread completely on the PTFE surface hence, solutions of various perfluorocarbon acids in water wet the polymer (78). Treatment with alkafl metals promotes the adhesion between PTFE and other substances (79) but increases the coefficient of friction (80). 

Cell Adhesion. The membranes of leukocytes and platelets contain a variety of components that promote ceU-surface contact. Although numerous ceU-surface molecules are likely to play a role in ceU-surface adhesion, the group of selectins are of particular interest to research on this subject. Selectins are molecules that are known to promote leukocyte—platelet adhesion. However, selectin-based models have not been able to account for the fact that platelets are allowed to pass through the filter and leukocytes are not. 

Additives. Because of their versatility, imparted via chemical modification, the appHcations of ethyleneimine encompass the entire additive sector. The addition of PEI to PVC plastisols increases the adhesion of the coatings by selective adsorption at the substrate surface (410). PEI derivatives are also used as adhesion promoters in paper coating (411). The adducts formed from fatty alcohol epoxides and PEI are used as dispersants and emulsifiers (412). They are able to control the viscosity of dispersions, and thus faciHtate transport in pipe systems (413). Eatty acid derivatives of PEI are even able to control the viscosity of pigment dispersions (414). The high nitrogen content of PEIs has a flame-retardant effect. This property is used, in combination with phosphoms compounds, for providing wood panels (415), ceUulose (416), or polymer blends (417,418) with a flame-retardant finish. 

Aluminum, the most common material used for contacts, is easy to use, has low resistivity, and reduces surface Si02 to form interfacial metal-oxide bonds that promote adhesion to the substrate. However, as designs reach submicrometer dimensions, aluminum, Al, has been found to be a poor choice for metallization of contacts and via holes. Al has relatively poor step coverage, which is nonuniform layer thickness when deposited over right-angled geometric features. This leads to keyhole void formation when spaces between features are smaller than 0.7 p.m. New collimated sputtering techniques can extend the lower limit of Al use to 0.5-p.m appHcations. 

AppHcation of an adhesion-promoting paint before metal spraying improves the coating. Color-coded paints, which indicate compatibiHty with specific plastics, can be appHed at 20 times the rate of grit blasting, typically at 0.025-mm dry film thickness. The main test and control method is cross-hatch adhesion. Among the most common plastics coated with such paints are polycarbonate, poly(phenylene ether), polystyrene, ABS, poly(vinyl chloride), polyethylene, polyester, and polyetherimide. 

Another market appHcation for naphthenic acid is the tire industry, where cobalt naphthenate is used as an adhesion promoter (see Adhesives Tire cords). Cobalt naphthenate improves the bonding of brass-plated steel cords to mbber, presumably by suppressing the de-zincification of brass (50). Its first reported use was in 1970 and the first patent for its use was issued in 1975 (51). About 900 t of cobalt naphthenate is used worldwide as an adhesion promoter, half of it in North America. The unit value fluctuates between 8.75—13.25 /kg because of the volatility of cobalt prices. Although it is the industry standard, the use of cobalt naphthenate is declining with the advent of more economical high metal-containing substitutes. 

Polymers. AH nitro alcohols are sources of formaldehyde for cross-linking in polymers of urea, melamine, phenols, resorcinol, etc (see Amino RESINS AND PLASTICS). Nitrodiols and 2-hydroxymethyl-2-nitro-l,3-propanediol can be used as polyols to form polyester or polyurethane products (see Polyesters Urethane polymers). 2-Methyl-2-nitro-l-propanol is used in tires to promote the adhesion of mbber to tire cord (qv). Nitro alcohols are used as hardening agents in photographic processes, and 2-hydroxymethyl-2-nitro-l,3-propanediol is a cross-linking agent for starch adhesives, polyamides, urea resins, or wool, and in tanning operations (17—25). Wrinkle-resistant fabric with reduced free formaldehyde content is obtained by treatment with... 

Adhesives. Contact adhesives are blends of mbber, phenoHc resin, and additives suppHed in solvent or aqueous dispersion form they are typically appHed to both surfaces to be joined (80). Evaporation of the solvent leaves an adhesive film that forms a strong, peel-resistant bond. Contact adhesives are used widely in the furniture and constmction industries and also in the automotive and footwear industries. The phenoHc resins promote adhesion and act as tackifiers, usually at a concentration of 20—40%. In solvent-based contact adhesives, neoprene is preferred, whereas nitrile is used in specialty appHcations. The type and grade of phenoHc resin selected control tack time, bond strength, and durabiHty. 

Formulation. Polysulftde-based sealants are formulated with appropriate ingredients to obtain the desired properties for a particular appHcation. A typical formulation contains Hquid polysulftde polymer, curing agent, cure accelerators (bases) or retarders (acids), fillers, plasticizers, thixotropes, and adhesion promoters. 

Plasma processing technologies ate used for surface treatments and coatings for plastics, elastomers, glasses, metals, ceramics, etc. Such treatments provide better wear characteristics, thermal stability, color, controlled electrical properties, lubricity, abrasion resistance, barrier properties, adhesion promotion, wettability, blood compatibility, and controlled light transmissivity. 

---