Polyester mechanical properties

Mechanical Properties. Polyester fibers are formed by melt spinning generally followed by hot drawing and heat setting to the final fiber form. The molecular orientation and crystalline fine stmcture developed depend on key process parameters in all fiber formation steps and are critical to the end use appHcation of the fibers. 

Although polymers in-service are required to be resistant toward hydrolysis and solar degradation, for polymer deformulation purposes hydrolysis is an asset. Highly crystalline materials such as compounded polyamides are difficult to extract. For such materials hydrolysis or other forms of chemolysis render additives accessible for analysis. Polymers, which may profitably be depolymerised into their monomers by hydrolysis include PET, PBT, PC, PU, PES, POM, PA and others. Hydrolysis occurs when moisture causes chain scissions to occur within the molecule. In polyesters, chain scissions take place at the ester linkages (R-CO-O-R ), which causes a reduction in molecular weight as well as in mechanical properties. Polyesters show their susceptibility to hydrolysis with dramatic shifts in molecular weight distribution. Apart from access to the additives fraction, hydrolysis also facilitates molecular characterisation of the polymer. In this context, it is noticed that condensation polymers (polyesters, -amides, -ethers, -carbonates, -urethanes) have also been studied much... 

Dr. Isao Noda has been working on the family of PHA called Nodax that consists of f/ j-3-hydroxyalkanoate comonomer units with medium size chain side groups and j-3-hydroxybutyrate. Because of the unique design of their molecular structure, the Nodax class PHA copolymers have a set of useful attributes, including polyolefin-like thermo-mechanical properties, polyester-like physicochemical properties, and interesting biological properties. Therefore, a broad range of industrial and consumer product applications are anticipated. 

It has been hypothesized that cross-linked polymers would have better mechanical properties if interchain bridges were located at the ends rather than the center of chains. To test this, low molecular weight polyesters were synthesizedf... 

Mechanical Properties. Properties of typical grades of PBT, either as unfiUed neat resin, glass-fiber fiUed, and FR-grades, are set out in Table 8. This table also includes impact-modified grades which incorporate dispersions of elastomeric particles inside the semicrystalHne polyester matrix. These dispersions act as effective toughening agents which greatly improve impact properties. The mechanisms are not fiiUy understood in all cases. The subject has been discussed in detail (171) and the particular case of impact-modified polyesters such as PBT has also been discussed (172,173). 

Mechanical Properties. The performance of various polyester resin compositions can be distinguished by comparing the mechanical properties of thin castings (3 mm) of the neat resin defined in ASTM testing procedures (15). This technique is used widely to characterize subtle changes in flexural, tensile, and compressive properties that are generally overshadowed in highly filled or reinforced laminates. 

Blends with good mechanical properties can be made from DMPPO and polymers with which DMPPO is incompatible if an appropriate additive, compatibilizing agent, or treatment is used to increase the dispersion of the two phases. Such blends include mixtures of DMPPO with nylon, polycarbonate, polyester, ABS, and poly(phenylene sulfide). 

Rubber. The mbber industry consumes finely ground metallic selenium and Selenac (selenium diethyl dithiocarbamate, R. T. Vanderbilt). Both are used with natural mbber and styrene—butadiene mbber (SBR) to increase the rate of vulcanization and improve the aging and mechanical properties of sulfudess and low sulfur stocks. Selenac is also used as an accelerator in butyl mbber and as an activator for other types of accelerators, eg, thiazoles (see Rubber chemicals). Selenium compounds are useflil as antioxidants (qv), uv stabilizers, (qv), bonding agents, carbon black activators, and polymerization additives. Selenac improves the adhesion of polyester fibers to mbber. 

Vinyl ester resins generally offer mechanical properties superior to those of polyester matrices but at an increased cost. Vinyl esters are chemically similar to epoxy resins but are manufactured via a cold-curing process similar to that used in the manufacture of polyester resins. Vinyl esters offer superior resistance to water and chemical attack and are used in such appHcations as underground pipes, tank liners, and storage tanks (see Vinyl polymers). 

Thermosetting unsaturated polyester resins constitute the most common fiber-reinforced composite matrix today. According to the Committee on Resin Statistics of the Society of Plastics Industry (SPl), 454,000 t of unsaturated polyester were used in fiber-reinforced plastics in 1990. These materials are popular because of thek low price, ease of use, and excellent mechanical and chemical resistance properties. Over 227 t of phenoHc resins were used in fiber-reinforced plastics in 1990 (1 3). PhenoHc resins (qv) are used when thek inherent flame retardance, high temperature resistance, or low cost overcome the problems of processing difficulties and lower mechanical properties. 

Ease of cure, easy removal of parts from mold surfaces, and wide availabiHty have made polyesters the first choice for many fiber-reinforced composite molders. Sheet mol ding compound, filament winding, hand lay-up, spray up, and pultmsion are all weU adapted to the use of polyesters. Choosing the best polyester resin and processing technique is often a challenge. The polyester must be a type that is weU adapted to the processing method and must have the final mechanical properties requked by the part appHcation. Table 1 Hsts the deskable properties for a number of fiber-reinforced composite fabrication methods. 

Some typical properties of polyester-glass laminates are given in Table 25.1. From these figures it will be seen that laminates can have very high tensile strengths. On the other hand some laminates made by hand lay-up processes may have mechanical properties not very different from those of thermoplastics such as the polyacetals and unplasticised PVC. 

Because of their favourable price, polyesters are preferred to epoxide and furane resins for general purpose laminates and account for at least 95% of the low-pressure laminates produced. The epoxide resins find specialised uses for chemical, electrical and heat-resistant applications and for optimum mechanical properties. The furane resins have a limited use in chemical plant. The use of high-pressure laminates from phenolic, aminoplastic and silicone resins is discussed elsewhere in this book. 

The dough moulding compounds were originally developed in an attempt to combine the mechanical properties of polyester-glass laminates with the speed of cure of conventional moulding powder. In spite of their somewhat high cost they have now established themselves in a number of applications where a mechanieally strong electrical insulant is required. 

Compared with the polyesters the epoxide resins generally have better mechanical properties and, using appropriate hardeners, better heat resistance and chemical resistance, in particular, resistance to alkalis. 

Polyester resins, reinforced with glass fibers, are used widely in the construction of process equipment. Some physical and mechanical properties are presented in Table 3.48. Table 3.49 lists various materials used as filler and the properties they impart to different plastics. 

Several commercial products of PVC/TPU blends are available. The BF Goodrich Chemical Group has a PVC/ TPU blend based on their Estane series TPUs. For example, their Estane 54620, a polyester-based TPU with a °ShA 85 hardness, shows excellent compatibility with flexible PVC. The blends are produced by mixing PVC, TPU, plasticizer, stabilizer, and lubricant in a twin-screw extruder. These polymeric blends show intermediate mechanical properties between PVC and TPU. 

The surface energy of fibers is closely related to the hydrophilicity of the fiber [38]. Some investigations are concerned with methods to decrease hydrophilicity. The modification, of wood cellulose fibers with stearic acid [43] hydrophobizes those fibers and improves their dispersion in polypropylene. As can be observed in jute-reinforced unsaturated polyester resin composites, treatment with polyvinylacetate increases the mechanical properties [24] and moisture repellency. 

Table 3-1 gives typical mechanical property data for four materials, the exact values of which are unimportant for this discussion. Aluminum and mild steel have been used as representative metals and polypropylene (PP) and glass fiber-TS polyester reinforced plastics (GRP) as representative plastics. Higher-performance types could have been selected for both the metals and plastics, but those in this table offer a fair comparison for the explanation being presented. 

Note The principal reinforcement, with respect to quantity, is glass fibers, but many other types are used (cotton, rayon, polyester/TP, nylon, aluminum, etc.). Of very limited use because of their cost and processing difficulty are whishers (single crystals of alumina, silicon carbide, copper, or others), which have superior mechanical properties. 

For example, the molecular weight of unsaturated polyesters is controlled to less than 5000 g/mol. The low molecular weight of the unsaturated polyester allows solvation in vinyl monomers such as styrene to produce a low-viscosity resin. Unsaturated polyesters are made with monomers containing carbon-carbon double bonds able to undergo free-radical crosslinking reactions with styrene and other vinyl monomers. Crosslinking the resin by free-radical polymerization produces the mechanical properties needed in various applications. 

---