Radical polymerization other

Various side reactions may complicate RAFT polymerization. Transfer to solvents, monomer and initiator occur as in conventional radical polymerization. Other potential side reactions involve the intermediate radicals 165 and 167. These radicals may couple with another radical (Q ) to form 271 or disproportionate with Q to form 270. They may also react with oxygen. The intermediate radicals 165 and 167 are not known to add monomer. 

Coordination Polymerization of 1,3-Dienes Single-Site (or Metallocene) Catalysts Living Radical Polymerizations Other Types of Polymerizations, Polymers Ring-Opening Polymerization... 

Publications by a number of authors have shown that carbon dioxide is a favorable medium for free radical polymerization. Other than environmental advantages, there are a number of important advantages in the use of CO2 for polymerizing fluoropolymers. 

The presence of the gegen ion in the vicinity of the growing center differentiates cationic from radical polymerization. Other common reactions in cationic polymerization include the following. 

Hydroxy-2-methylpropanenitrile is then reacted with methanol (or other alcohol) to yield methacrylate ester. Free-radical polymerization is initiated by peroxide or azo catalysts and produce poly(methyl methacrylate) resins having the following formula ... 

The three-step mechanism for free-radical polymerization represented by reactions (6.A)-(6.C) does not tell the whole story. Another type of free-radical reaction, called chain transfer, may also occur. This is unfortunate in the sense that it complicates the neat picture presented until now. On the other hand, this additional reaction can be turned into an asset in actual polymer practice. One of the consequences of chain transfer reactions is a lowering of the kinetic chain length and hence the molecular weight of the polymer without necessarily affecting the rate of polymerization. 

We begin our discussion of copolymers by considering the free-radical polymerization of a mixture of two monomers. Mi and M2. This is already a narrow view of the entire field of copolymers, since more than two repeat units can be present in copolymers and, in addition, mechanisms other than free-radical chain growth can be responsible for copolymer formation. The essential features of the problem are introduced by this simpler special case, so we shall restrict our attention to this system. 

Among other possible reactions, these free radicals can initiate ordinary free-radical polymerization. The Ziegler-Natta systems are thus seen to encompass several mechanisms for the initiation of polymerization. Neither ionic nor free-radical mechanisms account for stereoregularity, however, so we must look further for the mechanism whereby the Ziegler-Natta systems produce this interesting effect. 

Sonochemistry is also proving to have important applications with polymeric materials. Substantial work has been accomplished in the sonochemical initiation of polymerisation and in the modification of polymers after synthesis (3,5). The use of sonolysis to create radicals which function as radical initiators has been well explored. Similarly the use of sonochemicaHy prepared radicals and other reactive species to modify the surface properties of polymers is being developed, particularly by G. Price. Other effects of ultrasound on long chain polymers tend to be mechanical cleavage, which produces relatively uniform size distributions of shorter chain lengths. 

Emulsion Adhesives. The most widely used emulsion-based adhesive is that based upon poly(vinyl acetate)—poly(vinyl alcohol) copolymers formed by free-radical polymerization in an emulsion system. Poly(vinyl alcohol) is typically formed by hydrolysis of the poly(vinyl acetate). The properties of the emulsion are derived from the polymer employed in the polymerization as weU as from the system used to emulsify the polymer in water. The emulsion is stabilized by a combination of a surfactant plus a coUoid protection system. The protective coUoids are similar to those used paint (qv) to stabilize latex. For poly(vinyl acetate), the protective coUoids are isolated from natural gums and ceUulosic resins (carboxymethylceUulose or hydroxyethjdceUulose). The hydroHzed polymer may also be used. The physical properties of the poly(vinyl acetate) polymer can be modified by changing the co-monomer used in the polymerization. Any material which is free-radically active and participates in an emulsion polymerization can be employed. Plasticizers (qv), tackifiers, viscosity modifiers, solvents (added to coalesce the emulsion particles), fillers, humectants, and other materials are often added to the adhesive to meet specifications for the intended appHcation. Because the presence of foam in the bond line could decrease performance of the adhesion joint, agents that control the amount of air entrapped in an adhesive bond must be added. Biocides are also necessary many of the materials that are used to stabilize poly(vinyl acetate) emulsions are natural products. Poly(vinyl acetate) adhesives known as "white glue" or "carpenter s glue" are available under a number of different trade names. AppHcations are found mosdy in the area of adhesion to paper and wood (see Vinyl polymers). 

Photoinitiation. Since photolysis of polysdanes generates sdyl radicals, which can add to carbon—carbon double bonds, these polymers have been used for the free-radical polymerization of unsaturated organic monomers (135,136). Though about one-tenth as efficient as other organic photoinitiators, polysdanes are nevertheless quite insensitive to oxygen effects, which somewhat compensates for their lower efficiency. 

Allyl alcohol, CH2=CH—CH2OH (2-propen-l-ol) [107-18-6] is the simplest unsaturated alcohol. One hydrogen atom can easily be abstracted from the aHyhc methylene (—CH2—) to form a radical. Since the radical is stabilized by resonance with the C=C double bond, it is very difficult to get high molecular weight polymers by radical polymerization. In spite of the fact that aHyl alcohol has been produced commercially for some years (1), it has not found use as a monomer in large volumes as have other vinyl monomers. 

Copolymers of VDC can also be prepared by methods other than conventional free-radical polymerization. Copolymers have been formed by irradiation and with various organometaHic and coordination complex catalysts (28,44,50—53). Graft copolymers have also been described (54—58). 

Photopolymerization reactions are widely used for printing and photoresist appHcations (55). Spectral sensitization of cationic polymerization has utilized electron transfer from heteroaromatics, ketones, or dyes to initiators like iodonium or sulfonium salts (60). However, sensitized free-radical polymerization has been the main technology of choice (55). Spectral sensitizers over the wavelength region 300—700 nm are effective. AcryUc monomer polymerization, for example, is sensitized by xanthene, thiazine, acridine, cyanine, and merocyanine dyes. The required free-radical formation via these dyes may be achieved by hydrogen atom-transfer, electron-transfer, or exciplex formation with other initiator components of the photopolymer system. 

Other Types of Polymerization. Nonradical polymerization has not produced commercially useful products, although a large variety of polymerization systems have been tested. The stmctural factors that activate chloroprene toward radical polymerization often retard polymerization by other mechanisms. 

High pressure (60—350 MPa) free-radical polymerization using oxygen, peroxide, or other strong oxidizers as initiators at temperatures of up to 350°C to produce low density polyethylene (LDPE), a highly branched polymer, with densities from 0.91 to 0.94 g/cm. ... 

In contrast to ionic chain polymerizations, free radical polymerizations offer a facile route to copolymers ([9] p. 459). The ability of monomers to undergo copolymerization is described by the reactivity ratios, which have been tabulated for many monomer systems for a tabulation of reactivity ratios, see Section 11/154 in Brandrup and Immergut [14]. These tabulations must be used with care, however, as reactivity ratios are not always calculated in an optimum manner [15]. Systems in which one reactivity ratio is much greater than one (1) and the other is much less than one indicate poor copolymerization. Such systems form a mixture of homopolymers rather than a copolymer. Uncontrolled phase separation may take place, and mechanical properties can suffer. An important ramification of the ease of forming copolymers will be discussed in Section 3.1. 

The reaction between benzoyl peroxide and A,A-dimethylaniline has been the subject of many examinations over the years. The following mechanism of initiation is fairly well accepted in the polymerization of styrene. It seems likely that a similar mechanism is followed for other free-radical polymerizations (Scheme 5). 

Polypropylene made by free-radical polymerization is generally atactic , that is to say, there is no pattern to the stereochemistry. On the other hand, both isotactic polypropylene (in which all the stereocenters are the same) and syndiotactic polypropylene (in which the stereocenters alternate) may be made via the Ziegler-Natta process (see Chapter 18, Problem 4). Experimentally, both isotactic and syndiotactic polypropylene generally have higher melting points than atactic polypropylene. 

The effects of increasing the concentration of initiator (i.e., increased conversion, decreased M , and broader PDi) and of reducing the reaction temperature (i.e., decreased conversion, increased M , and narrower PDi) for the polymerizations in ambient-temperature ionic liquids are the same as observed in conventional solvents. May et al. have reported similar results and in addition used NMR to investigate the stereochemistry of the PMMA produced in [BMIM][PFgj. They found that the stereochemistry was almost identical to that for PMMA produced by free radical polymerization in conventional solvents [43]. The homopolymerization and copolymerization of several other monomers were also reported. Similarly to the findings of Noda and Watanabe, the polymer was in many cases not soluble in the ionic liquid and thus phase-separated [43, 44]. 

The previous sections show that certain ionic liquids, namely the chloroalumi-nate(III) ionic liquids, are capable of acting both as catalyst and as solvent for the polymerization of certain olefins, although in a somewhat uncontrolled manner, and that other ionic liquids, namely the non-chloroaluminate(III) ionic liquids, are capable of acting as solvents for free radical polymerization processes. In attempts to carry out polymerization reactions in a more controlled manner, several studies have used dissolved transition metal catalysts in ambient-temperature ionic liquids and have investigated the compatibility of the catalyst towards a range of polymerization systems. 

To examine potentiality of other ylides and their metal complex containing Sb, As, P, Bi, and Se as new novel initiator in polymer synthesis via living radical polymerization. 

There are some indications that the situation described above has been realized, at least partially, in the system styrene-methyl methacrylate polymerized by metallic lithium.29 29b It is known51 that in a 50-50 mixture of styrene and methyl methacrylate radical polymerization yields a product of approximately the same composition as the feed. On the other hand, a product containing only a few per cent of styrene is formed in a polymerization proceeding by an anionic mechanism. Since the polymer obtained in the 50-50 mixture of styrene and methyl methacrylate polymerized with metallic lithium had apparently an intermediate composition, it has been suggested that this is a block polymer obtained in a reaction discussed above. Further evidence favoring this mechanism is provided by the fact that under identical conditions only pure poly-methyl methacrylate is formed if the polymerization is initiated by butyl lithium and not by lithium dispersion. This proves that incorporation of styrene is due to a different initiation and not propagation. 

Most other hydrophilic monomers inclined to radical polymerization (methacrylamide, methacrylic acid, N-vinylpyrrolidone, aminoalkyl and hydroxyalkyl methacrylates) do not form hydrogels with high swellability in water. 

Gandini and Rieumont26,119 have carried out an extensive examination of the polymerizability of several vinyl esters of furan carboxylic acids and of the causes of the autoinhibition which most of them display with free-radical initiation. The compounds studied were the vinyl esters of 2-furoic, 2-furylacetic, 2-furylpropionic, 2-furylacrylic and sorbic acid. All these derivatives, showed the same strong indifference towards radical polymerization. Only when treated with large doses (10—30%) of initiator did they give small yields of oligomers. The structure of all these products was carefully studied by spectroscopic and other techniques. Invariably, it was... 

---