Functionalized conducting monomers can be deposited on electrode surfaces aiming for covalent attachment or entrapment of sensor components. Electrically conductive polymers (qv), eg, polypyrrole, polyaniline [25233-30-17, and polythiophene/23 2JJ-J4-j5y, can be formed at the anode by electrochemical polymerization. For integration of bioselective compounds or redox polymers into conductive polymers, functionalization of conductive polymer films, whether before or after polymerization, is essential. In Figure 7, a schematic representation of an amperomethc biosensor where the enzyme is covalendy bound to a functionalized conductive polymer, eg, P-amino (polypyrrole) or poly[A/-(4-aminophenyl)-2,2 -dithienyl]pyrrole, is shown. Entrapment of ferrocene-modified GOD within polypyrrole is shown in Figure 7. 

PMo220 4q, is analytically usehil, being formed in the molybdenum test for phosphate ion. Poly- and heteropolymolybdate ions are used in the precipitation of dyes. The protonated forms of the ions are strongly acidic and many poly- and heteropolymolybdate compounds have catalytic activity that is attributable to their acid—base or redox properties. 

Redox initiator systems are normally used in the emulsion polymerization of VDC to develop high rates at low temperatures. Reactions must be carried out below - 80° C to prevent degradation of the polymer. Poly(vinyHdene chloride) in emulsion is also attacked by aqueous base. Therefore, reactions should be carried out at low pH. 

Generation of radicals by redox reactions has also been applied for synthesizing block copolymers. As was mentioned in Section II. D. (see Scheme 23), Ce(IV) is able to form radical sites in hydroxyl-terminated compounds. Thus, Erim et al. [116] produced a hydroxyl-terminated poly(acrylamid) by thermal polymerization using 4,4-azobis(4-cyano pentanol). The polymer formed was in a second step treated with ceric (IV) ammonium nitrate, hence generating oxygen centered radicals capable of starting a second free radical polymeriza-... 

Emulsion polymerization is the most important process for production of elastic polymers based on butadiene. Copolymers of butadiene with styrene and acrylonitrile have attained particular significance. Polymerized 2-chlorobutadiene is known as chloroprene rubber. Emulsion polymerization provides the advantage of running a low viscosity during the entire time of polymerization. Hence the temperature can easily be controlled. The polymerizate is formed as a latex similar to natural rubber latex. In this way the production of mixed lattices is relieved. The temperature of polymerization is usually 50°C. Low-temperature polymerization is carried out by the help of redox systems at a temperature of 5°C. This kind of polymerization leads to a higher amount of desired trans-1,4 structures instead of cis-1,4 structures. Chloroprene rubber from poly-2-chlorbutadiene is equally formed by emulsion polymerization. Chloroprene polymerizes considerably more rapidly than butadiene and isoprene. Especially in low-temperature polymerization emulsifiers must show good solubility and... 

The stoichiometry of the redox reactions of conducting polymers (n and m in reactions 1 and 2) is quite variable. Under the most widely used conditions, polypyrroles and polythiophenes can be reversibly oxidized to a level of one hole per ca. 3 monomer units (i.e., a degree of oxidation, n, of ca. 0.3).7 However, this limit is dictated by the stability of the oxidized film under the conditions employed (Section V). With particularly dry and unreactive solvents, degrees of oxidation of 0.5 can be reversibly attained,37 and for poly-(4,4 -dimethoxybithiophene), a value of n = 1 has been reported.38 Although much fewer data are available for n-doping, it appears to involve similar stoichiometries [i.e., m in Eq. (2) is typically ca. 0.3].34,39"41 Polyanilines can in principle be reversibly p-doped to one... 

Figure 4 compares cyclic voltammograms for a redox polymer (poly-[Fe(5-amino-1,10-phenanthroline)3]3+/2+)91 and p-doping and undoping of a conducting polymer (polypyrrole).92 The voltammogram for the redox... 

Figure 4. (A) Cyclic voltammograms over a range of scan rates for a redox polymer (poly-[Fe 5-amino-1,10-phenanthrotme)3]3+/>)91 and (B) p-doping and undoping of a conducting polymer (polypyrrole) (B). [(A) Reprinted from X. Ren and P. O. Pickup, Strong dependence of the election hopping rate in poly-tris(5-amino-1,10-phenan-throline)iron(HI/II) on the nature of the counter-anion J. Electroanal. Chem. 365, 289-292,1994, with kind permission from Elsevier Sciences S.A.]...

On the other hand, Doblhofer218 has pointed out that since conducting polymer films are solvated and contain mobile ions, the potential drop occurs primarily at the metal/polymer interface. As with a redox polymer, electrons move across the film because of concentration gradients of oxidized and reduced sites, and redox processes involving solution species occur as bimolecular reactions with polymer redox sites at the polymer/solution interface. This model was found to be consistent with data for the reduction and oxidation of a variety of species at poly(7V-methylpyrrole). This polymer has a relatively low maximum conductivity (10-6 - 10 5 S cm"1) and was only partially oxidized in the mediation experiments, which may explain why it behaved more like a redox polymer than a typical conducting polymer. 

A great variety of suitable polymers is accessible by polymerization of vinylic monomers, or by reaction of alcohols or amines with functionalized polymers such as chloromethylat polystyrene or methacryloylchloride. The functionality in the polymer may also a ligand which can bind transition metal complexes. Examples are poly-4-vinylpyridine and triphenylphosphine modified polymers. In all cases of reactively functionalized polymers, the loading with redox active species may also occur after film formation on the electrode surface but it was recognized that such a procedure may lead to inhomogeneous distribution of redox centers in the film... 

The bridging polymer is a conducting poly(3-methyIthiophene) or polyaniline and the solid state redox conduction between all electrodes is accomplished by a common coating with poly(ethyleneoxide)/Li" CF3S03- or poly(vinyl alcohol)/ The polyaniline based molecular transistor proved as a very sensitive moisture detector it works well in a dry argon atmosphere but in water saturated argon the device cuts out... 

There is one report of the redox properties of poly(ferrocenylene) by Oyama et al. noting that the cyclic voltammetry of low molecular weight poly(ferrocenylene) (Mw 900) dissolved in CH2C12 or electrodeposited on Pt gives a broad redox wave with two (or three) peaks between 0.2 and 0.8 V vs. SSCE (70). 

Related Polymer Systems and Synthetic Methods. Figure 12A shows a hypothetical synthesis of poly (p-phenylene methide) (PPM) from polybenzyl by redox-induced elimination. In principle, it should be possible to accomplish this experimentally under similar chemical and electrochemical redox conditions as those used here for the related polythiophenes. The electronic properties of PPM have recently been theoretically calculated by Boudreaux et al (16), including bandgap (1.17 eV) bandwidth (0.44 eV) ionization potential (4.2 eV) electron affinity (3.03 eV) oxidation potential (-0.20 vs SCE) reduction potential (-1.37 eV vs SCE). PPM has recently been synthesized and doped to a semiconductor (24). 

A possible synthesis of poly(p-phenylene methine) from polybenzyl via redox elimination (A). The two limiting structures of polyaniline (B). 

We report here studies on a polymer fi1m which is formed by the thermal polymerization of a monomeric complex tris(5,5 -bis[(3-acrylvl-l-propoxy)carbonyll-2,2 -bipyridine)ruthenium(11) as its tosylate salt,I (4). Polymer films formed from I (poly-I) are insoluble in all solvents tested and possess extremely good chemical and electrochemical stability. Depending on the formal oxidation state of the ruthenium sites in poly-I the material can either act as a redox conductor or as an electronic (ohmic) conductor having a specific conductivity which is semiconductorlike in magnitude. 

---