Acrylonitrile plastic

Some typical properties of styrene-acrylonitrile plastics, referred to in many countries as SAN, are compared with those of other styrene-based plastics in Table 16.7. 

Styrene-acrylonitrile plastics are used on a smaller scale in a variety of areas as may be seen from Table 16.11. Individual applications were discussed in Section 16.7. 

Although there are many variations on how carbon fibers are made, the typical process starts with the formation of PAN fibers from a conventional suspension or solution polymerization process between a mixture of acrylonitrile plastic powder with another plastic, such as methyl acrylate or methyl methacrylate, and a catalyst. The product is then spun into fibers, with the use of different methods, in order to be able to achieve the internal atomic structure of the fiber. After this, the fibers are washed and stretched to the desired fiber diameter. This step is sometimes called "spinning" and is also vital in order to align the molecules inside the fiber and thus provide a good basis for the formation of firmly bonded carbon crystals after carbonization [7]. 

SAN, styrene I acrylonitrile plastics. Copolymer of styrene and acrylonitrile. An amorphous thermoplastic, transparent in the original form, which is tougher, less brittle, somewhat more heat stable than the standard polystyrene. Applications transparent covers of car and signal lamps, machinery and instrument parts, and various consumer goods. Trade names Kostil (I), Luran (FRG), Lustran (USA), Tyril (USA). 

Styrene acrylonitrile plastics. Mainly symbolized as SAN in the literature. 

Acrylonitrile (H2C=CH-CN) is used as a co-polymer in approximately 25% of all synthetic fibers. It is further used for synthetic rubbers and for the production of acrylonitrile-butadiene-styrene plastics and styrene-acrylonitrile plastics. These ter- and co-polymers are used in the automobile industry and in the production of house wares, electrical appliances, suitcases, food packaging and disposable dishes. Acrylonitrile can also be a constituent in fabrics and paints (Bjorkner 1995). 

In the case of poly(vinyl chloride) plastics, the FWA is mixed dry with the PVC powder before processing or dissolved in the plasticising agent (see Vinyl polymers). Polystyrene, acrylonitrile—butadiene—styrene (ABS), and polyolefin granulates are powdered with FWA prior to extmsion (2,78) (see... 

Styrene plastics Acrylonitrile polypous Olefin polypous). 

Many cellular plastics that have not reached significant commercial use have been introduced or their manufacture described in Hterature. Examples of such polymers are chlorinated or chlorosulfonated polyethylene, a copolymer of vinyUdene fluoride and hexafluoropropylene, polyamides (4), polytetrafluoroethylene (5), styrene—acrylonitrile copolymers (6,7), polyimides (8), and ethylene—propylene copolymers (9). 

Over 70% of the total volume of thermoplastics is accounted for by the commodity resins polyethylene, polypropylene, polystyrene, and poly(vinyl chloride) (PVC) (1) (see Olefin polymers Styrene plastics Vinyl polymers). They are made in a variety of grades and because of their low cost are the first choice for a variety of appHcations. Next in performance and in cost are acryhcs, ceUulosics, and acrylonitrile—butadiene—styrene (ABS) terpolymers (see... 

Acrylic ESTER POLYMERS Acrylonitrile POLYMERS Cellulose esters). Engineering plastics (qv) such as acetal resins (qv), polyamides (qv), polycarbonate (qv), polyesters (qv), and poly(phenylene sulfide), and advanced materials such as Hquid crystal polymers, polysulfone, and polyetheretherketone are used in high performance appHcations they are processed at higher temperatures than their commodity counterparts (see Polymers containing sulfur). 

The use of TAG as a curing agent continues to grow for polyolefins and olefin copolymer plastics and mbbers. Examples include polyethylene (109), chlorosulfonated polyethylene (110), polypropylene (111), ethylene—vinyl acetate (112), ethylene—propylene copolymer (113), acrylonitrile copolymers (114), and methylstyrene polymers (115). In ethylene—propylene copolymer mbber compositions. TAG has been used for injection molding of fenders (116). Unsaturated elastomers, such as EPDM, cross link with TAG by hydrogen abstraction and addition to double bonds in the presence of peroxyketal catalysts (117) (see Elastol rs, synthetic). 

Ammonia is used in the fibers and plastic industry as the source of nitrogen for the production of caprolactam, the monomer for nylon 6. Oxidation of propylene with ammonia gives acrylonitrile (qv), used for the manufacture of acryHc fibers, resins, and elastomers. Hexamethylenetetramine (HMTA), produced from ammonia and formaldehyde, is used in the manufacture of phenoHc thermosetting resins (see Phenolic resins). Toluene 2,4-cHisocyanate (TDI), employed in the production of polyurethane foam, indirectly consumes ammonia because nitric acid is a raw material in the TDI manufacturing process (see Amines Isocyanates). Urea, which is produced from ammonia, is used in the manufacture of urea—formaldehyde synthetic resins (see Amino resins). Melamine is produced by polymerization of dicyanodiamine and high pressure, high temperature pyrolysis of urea, both in the presence of ammonia (see Cyanamides). 

---