Transmission electronic microscopy TEM

Transmission electron microscopy (TEM) can resolve features down to about 1 nm and allows the use of electron diffraction to characterize the structure. Since electrons must pass through the sample however, the technique is limited to thin films. One cryoelectron microscopic study of fatty-acid Langmuir films on vitrified water [13] showed faceted crystals. The application of TEM to Langmuir-Blodgett films is discussed in Chapter XV. 

In many ways the nanocrystal characterization problem is an ideal one for transmission electron microscopy (TEM). Here, an electron beam is used to image a thin sample in transmission mode [119]. The resolution is a sensitive fimction of the beam voltage and electron optics a low-resolution microscope operating at 100 kV might... 

Occasionally, especially in the developmental phase of catalyst research, it is necessary to determine the oxidation state, exact location, and dispersion of various elements in the catalyst. Eor these studies, either transmission electron microscopy (TEM) or scanning electron microscopy (SEM) combined with various high vacuum x-ray, electron, and ion spectroscopies are used routinely. 

Alternatives to XRD include transmission electron microscopy (TEM) and diffraction, Low-Energy and Reflection High-Energy Electron Diffraction (LEED and RHEED), extended X-ray Absorption Fine Structure (EXAFS), and neutron diffraction. LEED and RHEED are limited to surfaces and do not probe the bulk of thin films. The elemental sensitivity in neutron diffraction is quite different from XRD, but neutron sources are much weaker than X-ray sources. Neutrons are, however, sensitive to magnetic moments. If adequately large specimens are available, neutron diffraction is a good alternative for low-Z materials and for materials where the magnetic structure is of interest. 

The field of carbon nanotube research was launched in 1991 by the initial experimental observation of carbon nanotubes by transmission electron microscopy (TEM) [151], and the subsequent report of conditions for the synthesis of large quantities of nanotubes [152,153]. Though early work was done on... 

The earliest observations of carbon nanotubes with very small (nanometer) diameters [151, 158, 159] are shown in Fig. 14. Here we see results of high resolution transmission electron microscopy (TEM) measurements, providing evidence for m-long multi-layer carbon nanotubes, with cross-sections showing several concentric coaxial nanotubes and a hollow core. One nanotube has... 

Processes that occur at a size scale larger than the individual chain have been studied using microscopy, mainly transmission electron microscopy (TEM), but optical microscopy has been useful to examine craze shapes. The knowledge of the crazing process obtained by TEM has been ably summarised by Kramer and will not be repeated here [2,3]. At an interface between two polymers a craze often forms within one of the materials, typically the one with lower crazing stress. 

The interface properties can usually be independently measured by a number of spectroscopic and surface analysis techniques such as secondary ion mass spectroscopy (SIMS), X-ray photoelectron spectroscopy (XPS), specular neutron reflection (SNR), forward recoil spectroscopy (FRES), scanning electron microscopy (SEM) and transmission electron microscopy (TEM), infrared (IR) and several other methods. Theoretical and computer simulation methods can also be used to evaluate H t). Thus, we assume for each interface that we have the ability to measure H t) at different times and that the function is well defined in terms of microscopic properties. 

Several structural characterisations of carbon nanotubes (CNTs) with the cylindrical graphite are reviewed from the viewpoint of transmission electron microscopy (TEM). Especially, electron energy loss spectroscopy (EELS) by using an energy-fdtered TEM is applied to reveal the dependence of fine structure of EELS on the diameter and the anisotropic features of CNTs. 

Multi-walled CNTs (MWCNTs) are produced by arc discharge between graphite electrodes but other carbonaceous materials are always formed simultaneously. The main by-product, nanoparticles, can be removed utilizing the difference in oxidation reaction rates between CNTs and nanoparticles [9]. Then, it was reported that CNTs can be aligned by dispersion in a polymer resin matrix [10]. However, the parameters of CNTs are uncontrollable, such as the diameter, length, chirality and so on, at present. Furthermore, although the CNTs are observed like cylinders by transmission electron microscopy (TEM), some reports have pointed out the possibility of non-cylindrical structures and the existence of defects [11-14]. 

Silver nitrate (AgN03) is a compound that fulfills the precedent requirements (Till = 212°C), and also it can be easily decomposed into pure silver by thermal treatment at 400 °C. As mentioned before, the basic characterisation technique for this studies is transmission electron microscopy (TEM) the atoms with rather high atomic number would facilitate the detection of the nanorods. 

Fig. 2. (a) (b) Transmission electron microscopy (TEM) images of as-grown VGCFs (broken portion) with the PCNT core exposed field emission-type scanning electron microscopy (FE-SEM) image of (c) as-grown and (d) heat-treated VGCFs (broken portion) at 2800°C with PCNT (white line) exposed [20],... 

The crystallization of glassy Pd-Ni-P and Pd-Cu-P alloys is complicated by the formation of metastable crystalline phaf s [26]. The final (stable) crystallization product consists of a mixture of a (Pd,Ni) or (Pd,Cu) fee solid solution and more than one kind of metal phosphide of low crystallographic symmetry. Donovan et al. [27] used transmission electron microscopy (TEM) and X-ray microanalysis to study the microstructure of slowly cooled crystalline Pd4oNi4oP2o- They identified the compositions of the metal phosphides to be Pd34Ni45P2j and Pdg8Ni[4Pjg. 

Small needle-shaped single crystals were examined by transmission electron microscopy (TEM) and electron diffraction (ED) (see Fig. 16-17). The results show that the crystals are elongated along the b-axis, which is the direction of weak intermolecular n-n interactions, and have a well-developed (ab) top surface. It corresponds to the surface of aliphatic tails (direction of weak intermolecular interactions). There are indications of displacement of successive ( / )-laycrs along the fl-axis, in line with the other signs of disorder in the aliphatic layer. 

Also a good interface resolution is obtained with transmission electron microscopy (TEM), where, however, a dedicated sample preparation and treatment are necessary to achieve nanometer resolution and suitable contrast [64]. Thus the... 

SAXS), IR spectroscopy, NMR, transmission electron microscopy (TEM), or atomic force microscopy (AFM) and the thermal transitions by DSC and DMA. 

The nano-scale structures in polymer layered-silicate nano-composites can be thoroughly characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). XRD is used to identify intercalated structures. XRD allows quantification of changes in layer spacing and the most commonly used to probe the nano-composite structure and... 

In the transmission electron microscopy (TEM) images, the starch nanoplatelets (SNPs) are believed to aggregate as a result of hydrogen bond interactions due to the surface hydroxyl groups [13] (Fig. lA). Blocking these interactions by relatively large molecular weight molecules obviously improves the individualization of the nanoparticles. The acetylated starch and cellulose nanoparticles (SAcNPs and CelAcNPs) appeared more individualized and monodispersed than their unmodified counterparts with a size of about 50 nm (Fig. IB C). 

SEM), and transmission electron microscopy (TEM). Study of mechanical and thermal properties shows significant improvement over the gum. The thermal results are given in Table 2.1. 

FIGURE 2.8 Transmission electron microscopy (TEM) photographs of clay nanocomposites with acrylonitrile-butadiene rubber (NBR) having (a) 50% and (b) 19% acrylonitrile content, respectively... 

FIGURE 2.13 Transmission electron microscopy (TEM) photographs of (a) FNA4 and (b) F20A4. (From Maiti, M. and Bhowmick, A.K., J. Appl. Polym. Sci., 105, 435, 2007. Courtesy of Wiley InterScience.)... 

Recent demands for polymeric materials request them to be multifunctional and high performance. Therefore, the research and development of composite materials have become more important because single-polymeric materials can never satisfy such requests. Especially, nanocomposite materials where nanoscale fillers are incorporated with polymeric materials draw much more attention, which accelerates the development of evaluation techniques that have nanometer-scale resolution." To date, transmission electron microscopy (TEM) has been widely used for this purpose, while the technique never catches mechanical information of such materials in general. The realization of much-higher-performance materials requires the evaluation technique that enables us to investigate morphological and mechanical properties at the same time. AFM must be an appropriate candidate because it has almost comparable resolution with TEM. Furthermore, mechanical properties can be readily obtained by AFM due to the fact that the sharp probe tip attached to soft cantilever directly touches the surface of materials in question. Therefore, many of polymer researchers have started to use this novel technique." In this section, we introduce the results using the method described in Section 21.3.3 on CB-reinforced NR. 

FIGURE 22.1 Transmission electron microscopy (TEM) micrograph of a carbon black network obtained from an ultrathin cut of a filled rubber sample. 

---