Thermoset matrices polyester

Thermosetting unsaturated polyester resins constitute the most common fiber-reinforced composite matrix today. According to the Committee on Resin Statistics of the Society of Plastics Industry (SPl), 454,000 t of unsaturated polyester were used in fiber-reinforced plastics in 1990. These materials are popular because of thek low price, ease of use, and excellent mechanical and chemical resistance properties. Over 227 t of phenoHc resins were used in fiber-reinforced plastics in 1990 (1 3). PhenoHc resins (qv) are used when thek inherent flame retardance, high temperature resistance, or low cost overcome the problems of processing difficulties and lower mechanical properties. 

DMTA is a very interesting tool for characterizing heterogeneous materials in which domains of distinct Tg values coexist. The most interesting cases involve modified thermosets of different types (see Chapter 8). Examples are the use of rubbers (e.g., liquid polybutadiene and random copolymers), or thermoplastics (e.g., polyethersulphone or polyetherimide in epoxy matrices or poly(vinyl acetate) in unsaturated polyesters), as impact modifier (epoxies), or low-profile additives (polyesters). The modifier-rich phase may be characterized by the presence of a new a peak (Fig. 11.10). But on occasions there may be superposition of peaks and the presence of the modifier cannot be easily detected by these techniques. If part of the added polymer is soluble in the thermoset matrix, its eventual plasticizing effect can be determined from the corresponding matrix Tg depletion, and the... 

The fibres are surface treated during manufacture to prepare adhesion with the polymer matrix, whether thermosetting (epoxy, polyester, phenoUc and polyimide resins) or thermoplastic (polypropylene. Nylon 6.6, PMMA, PEEK). The fibre surface is roughened by chemical etching and then coated with an appropriate size to aid bonding to the specified matrix. Whereas composite tensile strength is primarily a function of fibre... 

Polymer composites are plastics within which fibres are embedded. The plastic is known as the matrix (resin) and the fibres dispersed witbin it are known as the reinforcement Thermosetting matrix materials include polyester, vinyl ester and epoxy resins. For higher temperature and extreme environments, bismaleimlde, polyimide and phenolic resins are used. Composites can be used to replace metal parts but care must be taken during design. Most engineering materials have similar properties in any direction (called isotropic) where composites have not This can however be offset by arranging the reinforcement layers in varying directions. 

The APC materials typically nsed for on-site rehabilitation of timber and concrete are composed of glass, carbon or aramid fibres and a polyester, epoxy or polynrethane polymeric matrix. Glass fibres are the most frequently used due to their moderate cost and good mechanical properties when compared to carbon fibres. They are used normally in the form of pultruded profiles or strips, fabrics (tissues) or mats. Carbon fibres are mainly used in the form of pultruded profiles of solid, open or hollow cross-sectional shapes. While in timber applications both thermoplastic and thermosetting matrix types are used, in concrete applications only the latter type is used. 

Preparation and testing of composites from a styrene/ unsaturated polyester thermoset matrix and wood flours... 

The thermoplastic or thermoset nature of the resin in the colorant—resin matrix is also important. For thermoplastics, the polymerisation reaction is completed, the materials are processed at or close to their melting points, and scrap may be reground and remolded, eg, polyethylene, propjiene, poly(vinyl chloride), acetal resins (qv), acryhcs, ABS, nylons, ceUulosics, and polystyrene (see Olefin polymers Vinyl polymers Acrylic ester polymers Polyamides Cellulose ESTERS Styrene polymers). In the case of thermoset resins, the chemical reaction is only partially complete when the colorants are added and is concluded when the resin is molded. The result is a nonmeltable cross-linked resin that caimot be reworked, eg, epoxy resins (qv), urea—formaldehyde, melamine—formaldehyde, phenoHcs, and thermoset polyesters (qv) (see Amino resins and plastics Phenolic resins). 

The generic thermosets are the epoxies and the polyesters (both widely used as matrix materials for fibre-reinforced polymers) and the formaldehyde-based plastics (widely used for moulding and hard surfacing). Other formaldehyde plastics, which now replace bakelite, are ureaformaldehyde (used for electrical fittings) and melamine-formaldehyde (used for tableware). 

Polymer-matrix materials include a wide range of specific materials. Perhaps the most commonly used polymer is epoxy. Other polymers include vinyl ester and polyester. Polymers can be either of the thermoset type, where cross-linking of polymer chains is irreversible, or of the thermoplastic type, where cross-linking does not take place but the matrix only hardens and can be softened and hardened repeatedly. For example, thermoplastics can be heated and reheated, as is essential to any injection-molding process. In contrast, thermosets do not melt upon reheating, so they cannot be injection molded. Polyimides have a higher temperature limit than epoxies (650°F versus 250°F or 350°F) (343°C versus 121°C or 177°C), but are much more brittle and considerably harder to process. 

---