Sherrington et al. were the first to attempt the synthesis of chiral polymeric metal complexes by the chemical modification route,78,177,178 whereby the [Mn(salen)Cl] units are attached in a pendant fashion, by only one of the aromatic rings, to poly(styrene) or poly(methacrylate) resin beads of various morphology. Epoxidation of 1-phenylcyclohexene gave enantioselectivity values between 61% and 91%. 

On the other hand polymeric metal complexes can be used to generate colloidal metal thus Smith and Luca pre-prepared poly(l,3-octadienyliron tricarbonyl) (11) as an intermediary to iron clusters and particles. 

It should be noted that by immobilizing the metal complex catalysts on carbochain polymers it is possible to prepare polymer-polymer compositions using PVC, PMMA, poly(vinyl acetate), etc., as the polymeric fillers [286-287]. 

ORl OX w di-Miutyl peroxyoxalalc deactivation by reversible chain transfer and bioinolecular aclivaiion 456 atom transfer radical polymerization 7, 250, 456,457, 458,461.486-98 deactivation by reversible coupling and untmolecular activation 455-6, 457-86 carbon-centered radical-mediated poly nierizaiion 467-70 initiators, inferlers and iriiters 457-8 metal complex-mediated radical polymerization 484... 

Polyisothiouronium group chelating resins mineral processing, 6,826 Polyketones metal complexes, 2, 399 Poly(L-lysine) metal complexes, 2, 764 Polymerization solid state, 1, 470 Polymers... 

A great variety of suitable polymers is accessible by polymerization of vinylic monomers, or by reaction of alcohols or amines with functionalized polymers such as chloromethylat polystyrene or methacryloylchloride. The functionality in the polymer may also a ligand which can bind transition metal complexes. Examples are poly-4-vinylpyridine and triphenylphosphine modified polymers. In all cases of reactively functionalized polymers, the loading with redox active species may also occur after film formation on the electrode surface but it was recognized that such a procedure may lead to inhomogeneous distribution of redox centers in the film... 

Metal-free poly-4-vinyl-4 -methyl-2,2 -bipyridine films on electrodes have been prepared by the electroreductive polymerization of a Rh complex and subsequent leaching of the metal by a strong complexand. The films can incorporate a variety of transition metals... 

Tetra(o-aminophenyl)porphyrin, H-Co-Nl TPP, can for the purpose of electrochemical polymerization be simplistically viewed as four aniline molecules with a common porphyrin substituent, and one expects that their oxidation should form a "poly(aniline)" matrix with embedded porphyrin sites. The pattern of cyclic voltammetric oxidative ECP (1) of this functionalized metal complex is shown in Fig. 2A. The growing current-potential envelope represents accumulation of a polymer film that is electroactive and conducts electrons at the potentials needed to continuously oxidize fresh monomer that diffuses in from the bulk solution. If the film were not fully electroactive at this potential, since the film is a dense membrane barrier that prevents monomer from reaching the electrode, film growth would soon cease and the electrode would become passified. This was the case for the phenolically substituted porphyrin in Fig. 1. 

Polymeric pseudocrown ether networks have been generated in situ by the photopolymerization of poly(ethylene glycol) diacrylate transition metal complexes <00CM633>, and the effect of metal ion templation was evaluated. The 1,6,13,18-tetraoxa[6.6]paracyclophane-3,15-diyne (termed pyxophanes) was prepared from hydroquinone and l,4-dichlorobut-2-yne it forms size-selective 7i-complexes with alkali metal cations <00CC2377>. Dibenzo[ ]crown-m have been used in numerous elegant studies in which they were the needles that were threaded by diverse reagents the resultant... 

Control of the electron-transfer step was also attempted by combining two metal species on a polymer ligand167. We prepared polymer-metal complexes involving both the Cu(II) and Mn(III) ions. The oxidative polymerization of XOH catalyzed by the PVP-Cu, Mn mixed complex or the diethylaminomethylated poly(styrene)(PDA)-Cu Mn mixed complex proceeded 10 times faster than the polymerization catalyzed by either PVP- or PDA-metal complex. The maxima of the activity observed at [Cu]/[Mn] = 1 and [polymer]/[Cu,Mn] moderately small where Cu and Mn ions were crowded within the contracted polymer chain. Cooperative interaction between Cu and Mn was inferred. The rate constant of the electron-transfer step (ke in Scheme 14) for Cu(II) -> Cu(I) was much larger than that for Mn(III) -> Mn(II). The rate constants of the reoxidation step (k0) were polymer-Mn ex polymer-Cu.Mn > polymer-Cu, so the rapid redox reaction... 

In 1979, Maciejewski et al. also explored Method 3 for the preparation of main-chain poly(vinylidene chloride-/ -CD rotaxane) 35 [74, 75]. Radiation polymerization and AIBN-initiated solution polymerization of the complex of vinyli-dene chloride with 21 gave products with min = 0.34 and 0.49, respectively. However, the polyrotaxane via Method 1 had a much lower min (0.087) with much lower CD/monomer feed ratio than for those via the polymerization of the complex (1 1 ratio). Therefore, the reported min values are not comparable, so the difference between the two methods in terms of threading efficiencies cannot be distinguished. Although the authors did not see any threading via Method 2 for the same polyrotaxanes, Ogino and coworkers prepared a true CD-based polyrotaxane of Type 5 using metal complexes as stoppers [76]. It was also found that... 

Many other types of polymer have been prepared which exhibit semiconductivity. All obey the equation a = a0exp — E/kT. These include xanthene polymers (109, 110), polymerized phthalocyanines (111, 112), epoxides and polydiketones (86, 113), polypentadienes (114), polydicyanoacetylenes (115), polyvinylferrocene and substituted ferrocene (116, 117, 118, 119), polymeric complexes of tetracyanoethylene and metals (120), poly(vinyl chloride) and poly(vinylidene chloride) (121), polyvinylene and polyphenylene (122) and poly(Schiff s bases) (123, 124). 

In the most important series of polymers of this type, the metallotetraphenylporphyrins, a metalloporphyrin ring bears four substituted phenylene groups X, as is shown in 7.19. The metals M in the structure are typically iron, cobalt, or nickel cations, and the substituents on the phenylene groups include -NH2, -NR2, and -OH. These polymers are generally insoluble. Some have been prepared by electro-oxidative polymerizations in the form of electroactive films on electrode surfaces.79 The cobalt-metallated polymer is of particular interest since it is an electrocatalyst for the reduction of dioxygen. Films of poly(trisbipyridine)-metal complexes also have interesting electrochemical properties, in particular electrochromism and electrical conductivity.78 The closely related polymer, poly(2-vinylpyridine), also forms metal complexes, for example with copper(II) chloride.80... 

Organic compounds having labile hydrogen atoms, such as phenols, anilines, and acetylenes, are also oxidatively polymerized by metal-complex catalysts (Eqs. 1-3). The oxidative coupling is a dehydrogenation reaction the polymer chain produced contains the dehydrogenated monomer structure as a repeating unit. As a remarkable example, poly(phenylene ether), one of the... 

Kinetically slow steps in the formation of melanin from DOPA are the formation of dopaquinone from DOPA (step 1, kD), the reaction of dopachrome to dihydroxyindole (step 2), and the polymerization to form melanin (step 3, kM). Step 1 and step 2 proceed with about the same rate in the oxidative coupling polymerization catalyzed by tyrosinase. However, step 1 becomes remarkably slow when a macromolecule-metal complex is used as a catalyst. The copper complex in poly(l-vinylimidazole-co-vinylpyrrolidone) has been found [38] to act as an excellent catalyst and to exhibit the highest activity for melanin formation. The ratio of the rate constants ( m/ d) is approximately 3 (tyrosinase... 

Organic compounds having labile hydrogens, such as phenols [41,42], phenylene-diamines [43], and acetylenes [44], can be oxidatively coupled in the presence of specific metal complexes to form polymeric compounds. The oxidative polymerization of 2,6-disubstituted phenols with a copper-amine complex produces poly(2,6-disubstituted phenylene ether) [45-51], Poly(2,6-dimethylphenylene ether) and poly(2,6-diphenylphenylene ether) are commercially produced from 2,6-dimethyl phenol and 2,6-diphenylphenol, respectively (Figure 5). These polymers exhibit excellent performance as engineering plastics. 

---