The protonated form of poly(vinyl amine) (PVAm—HCl) has two advantages over many cationic polymers high cationic charge densities are possible and the pendent primary amines have high reactivity. It has been appHed in water treatment, paper making, and textiles (qv). The protonated forms modified with low molecular weight aldehydes are usehil as fines and filler retention agents and are in use with recycled fibers. As with all new products, unexpected appHcations, such as in clear antiperspirants, have been found. It is usehil in many metal complexation appHcations (49). 

The molecular weight of a polymer can be controlled through the use of a chain-transfer agent, as well as by initiator concentration and type, monomer concentration, and solvent type and temperature. Chlorinated aUphatic compounds and thiols are particularly effective chain-transfer agents used for regulating the molecular weight of acryUc polymers (94). Chain-transfer constants (C at 60°C) for some typical agents for poly(methyl acrylate) are as follows (87) ... 

Cellulosics. CeUulosic adhesives are obtained by modification of cellulose [9004-34-6] (qv) which comes from cotton linters and wood pulp. Cellulose can be nitrated to provide cellulose nitrate [9004-70-0] which is soluble in organic solvents. When cellulose nitrate is dissolved in amyl acetate [628-63-7] for example, a general purpose solvent-based adhesive which is both waterproof and flexible is formed. Cellulose esterification leads to materials such as cellulose acetate [9004-35-7], which has been used as a pressure-sensitive adhesive tape backing. Cellulose can also be ethoxylated, providing hydroxyethylceUulose which is useful as a thickening agent for poly(vinyl acetate) emulsion adhesives. Etherification leads to materials such as methylceUulose [9004-67-5] which are soluble in water and can be modified with glyceral [56-81-5] to produce adhesives used as wallpaper paste (see Cellulose esters Cellulose ethers). 

Emulsion Adhesives. The most widely used emulsion-based adhesive is that based upon poly(vinyl acetate)—poly(vinyl alcohol) copolymers formed by free-radical polymerization in an emulsion system. Poly(vinyl alcohol) is typically formed by hydrolysis of the poly(vinyl acetate). The properties of the emulsion are derived from the polymer employed in the polymerization as weU as from the system used to emulsify the polymer in water. The emulsion is stabilized by a combination of a surfactant plus a coUoid protection system. The protective coUoids are similar to those used paint (qv) to stabilize latex. For poly(vinyl acetate), the protective coUoids are isolated from natural gums and ceUulosic resins (carboxymethylceUulose or hydroxyethjdceUulose). The hydroHzed polymer may also be used. The physical properties of the poly(vinyl acetate) polymer can be modified by changing the co-monomer used in the polymerization. Any material which is free-radically active and participates in an emulsion polymerization can be employed. Plasticizers (qv), tackifiers, viscosity modifiers, solvents (added to coalesce the emulsion particles), fillers, humectants, and other materials are often added to the adhesive to meet specifications for the intended appHcation. Because the presence of foam in the bond line could decrease performance of the adhesion joint, agents that control the amount of air entrapped in an adhesive bond must be added. Biocides are also necessary many of the materials that are used to stabilize poly(vinyl acetate) emulsions are natural products. Poly(vinyl acetate) adhesives known as "white glue" or "carpenter s glue" are available under a number of different trade names. AppHcations are found mosdy in the area of adhesion to paper and wood (see Vinyl polymers). 

In the case of poly(vinyl chloride) plastics, the FWA is mixed dry with the PVC powder before processing or dissolved in the plasticising agent (see Vinyl polymers). Polystyrene, acrylonitrile—butadiene—styrene (ABS), and polyolefin granulates are powdered with FWA prior to extmsion (2,78) (see... 

Suspension polymerization of VDE in water are batch processes in autoclaves designed to limit scale formation (91). Most systems operate from 30 to 100°C and are initiated with monomer-soluble organic free-radical initiators such as diisopropyl peroxydicarbonate (92—96), tert-huty peroxypivalate (97), or / fZ-amyl peroxypivalate (98). Usually water-soluble polymers, eg, cellulose derivatives or poly(vinyl alcohol), are used as suspending agents to reduce coalescence of polymer particles. Organic solvents that may act as a reaction accelerator or chain-transfer agent are often employed. The reactor product is a slurry of suspended polymer particles, usually spheres of 30—100 pm in diameter they are separated from the water phase thoroughly washed and dried. Size and internal stmcture of beads, ie, porosity, and dispersant residues affect how the resin performs in appHcations. 

Tetraethylene glycol may be used direcdy as a plasticizer or modified by esterification with fatty acids to produce plasticizers (qv). Tetraethylene glycol is used directly to plasticize separation membranes, such as siHcone mbber, poly(vinyl acetate), and ceUulose triacetate. Ceramic materials utilize tetraethylene glycol as plasticizing agents in resistant refractory plastics and molded ceramics. It is also employed to improve the physical properties of cyanoacrylate and polyacrylonitrile adhesives, and is chemically modified to form polyisocyanate, polymethacrylate, and to contain siHcone compounds used for adhesives. 

A poly( -vinyl-2-pyrroHdinone)-iodine complex [25655-41-8] (PVP-iodine), has been used extensively in hospitals and elsewhere because of its germicidal, bactericidal, fungicidal, and generally disinfecting properties (150). It is sold as a solution that contains about 10% available, or active, iodine and about 5% inactive iodine, in the form of iodide ion (see Disinfectants and antiseptics Industrial antimicrobial agents). 

In fluorescent lamps, phosphors are coated on the inside of the lamp tube using a slurry containing the powder and a Hquid which is either poured down through the tube, up-flushed, or in some cases the tubes are filled and then drained. Because of concerns over having volatile organic solvents in the air, the hquid medium containing the powder is usually water with an added agent, a thickener, to increase the viscosity of the suspension, such as poly(methacryhc... 

Alkenylsuccinic anhydrides made from several linear alpha olefins are used in paper sizing, detergents, and other uses. Sulfosuccinic acid esters serve as surface active agents. Alkyd resins (qv) are used as surface coatings. Chlorendric anhydride [115-27-5] is used as a flame resistant component (see Flame retardants). Tetrahydrophthalic acid [88-98-2] and hexahydrophthalic anhydride [85-42-7] have specialty resin appHcations. Gas barrier films made by grafting maleic anhydride to polypropylene [25085-53-4] film are used in food packaging (qv). Poly(maleic anhydride) [24937-72-2] is used as a scale preventer and corrosion inhibitor (see Corrosion and corrosion control). Maleic anhydride forms copolymers with ethylene glycol methyl vinyl ethers which are partially esterified for biomedical and pharmaceutical uses (189) (see Pharmaceuticals). 

Chain transfer to solvent is an important factor in controlling the molecular weight of polymers prepared by this method. The chain-transfer constants for poly(methyl methacrylate) in various common solvents (C) and for various chain-transfer agents are Hsted in Table 10. 

Another biomedical appHcation of mictocapsules is the encapsulation of Hve mammalian ceUs for transplantation into humans. The purpose of encapsulation is to protect the transplanted ceUs or organisms from rejection by the host. The capsule sheU must prevent entrance of harmful agents into the capsule, aUow free transport of nutrients necessary for ceU functioning into the capsule, and aUow desirable ceUular products to freely escape from the capsule. This type of encapsulation has been carried out with a number of different types of Hve ceUs, but studies with encapsulated pancreatic islets or islets of Langerhans ate most common. The alginate—poly(L-lysine) encapsulation process originally developed in 1981 (54) catalyzed much of the ceU encapsulation work carried out since. A discussion of the obstacles to the appHcation of microencapsulation in islet transplantation reviewed much of the mote recent work done in this area (55). Animal ceU encapsulation has also been researched (56). 

Sacrificial adsorption agents such as lignosulfonates (148—151) can be used to reduce the adsorption of more expensive polymers and surfactants. Other chemicals tested include poly(vinyl alcohol) (152), sulfonated poly(vinyl alcohol) (153), sulfonatedpoly(vinylpyrrohdinone) (153), low molecular weight polyacrylates (154), and sodium carbonate (155). 

---