Thermoplastics molecular weight

The effect of thermoplastic molecular weight and curing rate on gelation behavior has also been studied [70]. By using modified DGEBA-anhydride systems with three different molecular weight-types of PES (20 wt%) and different amounts of... 

Cblorina.ted Pa.ra.ffins, The term chlotinated paraffins covers a variety of compositions. The prime variables are molecular weight of the starting paraffin and the chlorine content of the final product. Typical products contain from 12—24 carbons and from 40—70 wt % chlorine. Liquid chlotinated paraffins are used as plasticizers (qv) and flame retardants ia paint (qv) and PVC formulations. The soHd materials are used as additive flame retardants ia a variety of thermoplastics. In this use, they are combiaed with antimony oxide which acts as a synergist. Thermal stabilizers, such as those used ia PVC (see vinyl polymers), must be used to overcome the inherent thermal iastabiUty. 

Many challenging industrial and military applications utilize polychlorotriduoroethylene [9002-83-9] (PCTFE) where, ia addition to thermal and chemical resistance, other unique properties are requited ia a thermoplastic polymer. Such has been the destiny of the polymer siace PCTFE was initially synthesized and disclosed ia 1937 (1). The synthesis and characterization of this high molecular weight thermoplastic were researched and utilized duting the Manhattan Project (2). The unique comhination of chemical iaertness, radiation resistance, low vapor permeabiUty, electrical iasulation properties, and thermal stabiUty of this polymer filled an urgent need for a thermoplastic material for use ia the gaseous UF diffusion process for the separation of uranium isotopes (see Diffusion separation methods). 

The lower molecular weight PCTFE oils, waxes, and greases are used as inert sealants and lubricants for equipment handling oxygen and other oxidative or corrosive media. Other uses include gyroscope flotation fluids and plasticizers for thermoplastics. 

Vinyl organosol coatings, which incorporate a high molecular weight thermoplastic PVC organosol dispersion resin, are extremely flexible. Soluble thermosetting resins, including epoxy, phenoHc, and polyesters, are added to enhance the film s product resistance and adhesion. 

Hydrocarbon resin is a broad term that is usually used to describe a low molecular weight thermoplastic polymer synthesized via the thermal or catalytic polymerization of coal-tar fractions, cracked petroleum distillates, terpenes, or pure olefinic monomers. These resins are used extensively as modifiers in the hot melt and pressure sensitive adhesive industries. They are also used in numerous other appHcations such as sealants, printing inks, paints, plastics, road marking, carpet backing, flooring, and oil field appHcations. They are rarely used alone. 

With the improvement of refining and purification techniques, many pure olefinic monomers are available for polymerization. Under Lewis acid polymerization, such as with boron trifluoride, very light colored resins are routinely produced. These resins are based on monomers such as styrene, a-methylstryene, and vinyltoluene (mixed meta- and i ra-methylstyrene). More recently, purified i ra-methylstyrene has become commercially available and is used in resin synthesis. Low molecular weight thermoplastic resins produced from pure styrene have been available since the mid-1940s resins obtained from substituted styrenes are more recent. 

Petroleum resins are low molecular weight thermoplastic hydrocarbon resins synthesized from steam cracked petroleum distillates. These resins are differentiated from higher molecular weight polymers such as polyethylene and polypropylene, which are produced from essentially pure monomers. Petroleum resin feedstocks are composed of various reactive and nonreactive aliphatic and aromatic components. The resins are usually classified as C-5... 

Strong-Acid Catalysts, Novolak Resins. PhenoHc novolaks are thermoplastic resins having a molecular weight of 500—5000 and a glass-transition temperature, T, of 45—70°C. The phenol—formaldehyde reactions are carried to their energetic completion, allowing isolation of the resin ... 

Thermoplasticity. High molecular weight poly(ethylene oxide) can be molded, extmded, or calendered by means of conventional thermoplastic processing equipment (13). Films of poly(ethylene oxide) can be produced by the blown-film extmsion process and, in addition to complete water solubiUty, have the typical physical properties shown in Table 3. Films of poly(ethylene oxide) tend to orient under stress, resulting in high strength in the draw direction. The physical properties, melting behavior, and crystallinity of drawn films have been studied by several researchers (14—17). 

Composites. High molecular weight PPS can be combiaed with long (0.6 cm to continuous) fiber to produce advanced composite materials (131). Such materials having PPS as the polymer matrix have been developed by usiag a variety of reinforcements, including glass, carbon, and Kevlar fibers as mat, fabric, and unidirectional reinforcements. Thermoplastic composites based on PPS have found application ia the aircraft, aerospace, automotive, appliance, and recreation markets (see Composite materials, polymer-matrix). 

The largest use for 2,4-dicumylphenol is in a production of a uv stabilizer of the benzotriazole class, 2-(2 -hydroxy-3, 5 -dicumylphenyl)benzotriazole [70321-86-7] which is used in engineering thermoplastics where high molding temperatures are encountered (67). The high molecular weight of... 

Cycloahphatic diamines react with dicarboxyUc acids or their chlorides, dianhydrides, diisocyanates and di- (or poly-)epoxides as comonomers to form high molecular weight polyamides, polyimides, polyureas, and epoxies. Polymer property dependence on diamine stmcture is greater in the linear amorphous thermoplastic polyamides and elastomeric polyureas than in the highly crosslinked thermo set epoxies (2—4). 

General-Purpose Polystyrene. Polystyrene is a high molecular weight M = 2 — 3 x 10 ), crystal-clear thermoplastic that is hard, rigid, and free of odor and taste. Its ease of heat fabrication, thermal stabiUty, low specific gravity, and low cost result in mol dings, extmsions, and films of very low unit cost. In addition, PS materials have excellent thermal and electrical properties that make them useful as low cost insulating materials (see Insulation, ELECTRIC Insulation, thermal). 

In addition, polyester polyols are made by the reaction of caprolactone with diols. Poly(caprolactone diols) are used in the manufacture of thermoplastic polyurethane elastomers with improved hydrolytic stabiHty (22). The hydrolytic stabiHty of the poly(caprolactone diol)-derived TPUs is comparable to TPUs based on the more expensive long-chain diol adipates (23). Polyether/polyester polyol hybrids are synthesized from low molecular weight polyester diols, which are extended with propylene oxide. 

Polyester and polyether diols are used with MDI in the manufacture of thermoplastic polyurethane elastomers (TPU). The polyester diols are obtained from adipic acid and diols, such as ethylene glycol, 1,4-butanediol, or 1,6-hexanediol. The preferred molecular weights are 1,000 to 2,000, and low acid numbers are essential to ensure optimal hydrolytic stabihty. Also, caprolactone-derived diols and polycarbonate diols are used. Polyether diols are... 

---