Mechanical properties thermoplastic

No polymer is ever 100% crystalline at best, patches of crystallinity are present in an otherwise amorphous matrix. In some ways, the presence of these domains of crystallinity is equivalent to cross-links, since different chains loop in and out of the same crystal. Although there are similarities in the mechanical behavior of chemically cross-linked and partially crystalline polymers, a significant difference is that the former are irreversibly bonded while the latter are reversible through changes of temperature. Materials in which chemical cross-linking is responsible for the mechanical properties are called thermosetting those in which this kind of physical cross-linking operates, thermoplastic. [Pg.26]

We noted above that the presence of monomer with a functionality greater than 2 results in branched polymer chains. This in turn produces a three-dimensional network of polymer under certain circumstances. The solubility and mechanical behavior of such materials depend critically on whether the extent of polymerization is above or below the threshold for the formation of this network. The threshold is described as the gel point, since the reaction mixture sets up or gels at this point. We have previously introduced the term thermosetting to describe these cross-linked polymeric materials. Because their mechanical properties are largely unaffected by temperature variations-in contrast to thermoplastic materials which become more fluid on heating-step-growth polymers that exceed the gel point are widely used as engineering materials. [Pg.314]

The typical mechanical properties that qualify PCTFE as a unique engineering thermoplastic are provided ia Table 1 the cryogenic mechanical properties are recorded ia Table 2. Other unique aspects of PCTFE are resistance to cold flow due to high compressive strength, and low coefficient of thermal expansion over a wide temperature range. [Pg.393]

Aromatic polyethers are best characterized by their thermal and chemical stabiUties and mechanical properties. The aromatic portion of the polyether contributes to the thermal stabiUty and mechanical properties, and the ether fiinctionahty faciUtates processing but stiU possesses both oxidative and thermal stabiUty. With these characteristic properties as well as the abiUty to be processed as mol ding materials, many of the aromatic polyethers can be classified as engineering thermoplastics (see Engineering PLASTICS). [Pg.326]

The effect of temperature on PSF tensile stress—strain behavior is depicted in Figure 4. The resin continues to exhibit useful mechanical properties at temperatures up to 160°C under prolonged or repeated thermal exposure. PES and PPSF extend this temperature limit to about 180°C. The dependence of flexural moduli on temperature for polysulfones is shown in Figure 5 with comparison to other engineering thermoplastics. [Pg.466]

Table 1. Mechanical Properties and Relative Costs of Thermosetting and Thermoplastic Composites... Table 1. Mechanical Properties and Relative Costs of Thermosetting and Thermoplastic Composites...
The classification given in Table 1 is based on the process, ie, thermosetting or thermoplastic, by which polymers in general are formed into usehil articles and on the mechanical properties, ie, rigid, flexible, or mbbery, of the final product. AH commercial polymers used for molding, extmsion, etc, fit into one of these six classifications the thermoplastic elastomers are the newest. [Pg.11]

Some typical properties of polyester-glass laminates are given in Table 25.1. From these figures it will be seen that laminates can have very high tensile strengths. On the other hand some laminates made by hand lay-up processes may have mechanical properties not very different from those of thermoplastics such as the polyacetals and unplasticised PVC. [Pg.706]

The physical and mechanical properties of the principal thermoplastics of interest for process plant applications are listed in Table 3.42. Table 3.43 gives typical hydrostatic design stresses for different types of thermoplastic pipe. Plastics widely employed in piping systems are described briefly below. [Pg.105]

An important subdivision within the thermoplastic group of materials is related to whether they have a crystalline (ordered) or an amorphous (random) structure. In practice, of course, it is not possible for a moulded plastic to have a completely crystalline structure due to the complex physical nature of the molecular chains (see Appendix A). Some plastics, such as polyethylene and nylon, can achieve a high degree of crystallinity but they are probably more accurately described as partially crystalline or semi-crystalline. Other plastics such as acrylic and polystyrene are always amorphous. The presence of crystallinity in those plastics capable of crystallising is very dependent on their thermal history and hence on the processing conditions used to produce the moulded article. In turn, the mechanical properties of the moulding are very sensitive to whether or not the plastic possesses crystallinity. [Pg.4]

Many thermoplastics are now accepted as engineering materials and some are distinguished by the loose description engineering plastics. The term probably originated as a classiflcation distinguishing those that could be substituted satisfactorily for metals such as aluminium in small devices and structures from those with inadequate mechanical properties. This demarcation is clearly artificial because the properties on which it is based are very sensitive to the ambient temperature, so that a thermoplastic might be a satisfactory substitute for a metal at a particular temperature and an unsatisfactory substitute at a different one. [Pg.6]

Strength and Stiffness. Thermoplastic materials are viscoelastic which means that their mechanical properties reflect the characteristics of both viscous liquids and elastic solids. Thus when a thermoplastic is stressed it responds by exhibiting viscous flow (which dissipates energy) and by elastic displacement (which stores energy). The properties of viscoelastic materials are time, temperature and strain rate dependent. Nevertheless the conventional stress-strain test is frequently used to describe the (short-term) mechanical properties of plastics. It must be remembered, however, that as described in detail in Chapter 2 the information obtained from such tests may only be used for an initial sorting of materials. It is not suitable, or intended, to provide design data which must usually be obtained from long term tests. [Pg.18]

Oridation. This is caused by contact with oxidising acids, exposure to u-v, prolonged application of excessive heat, or exposure to weathering. It results in a deterioration of mechanical properties (embrittlement and possibly stress cracking), increase in power factor, and loss of clarity. It affects most thermoplastics to varying degrees, in particular polyolefins, PVC, nylons, and cellulose derivatives. [Pg.27]

Throne, J.L. Mechanical properties of thermoplastic structural foams, in Wendle, B.C. (ed.) Engineering Guide to Structural Foams, Technomic, Lancaster, PA, USA (1976) pp. 91 -114. [Pg.157]

As normally polymerized, PVF melts between IH5 and 210 °C and contains 12 18% inverted monomer units ft is normally considered a thermoplastic, but because of its instability above its melting point, it cannot be processed by conventional thermoplastic techniques Instead it is generally extruded into films in a solvent swollen (organosol) form and the solvent is subsequently evaporated and recovered Such films can be onented further to achieve specific mechanical properties PVF films are exceptionally weather and radiabon resistant considenng their modest fluonne content PVF is insoluble below 100 °C but, at higher temperatures, it dissolves in polar solvents like amides, ketones, tetramethylene sulfone, and tetramethylurea Resistance to acids and bases at room temperature IS good [1, 29 ... [Pg.1111]

Coran and Patel [33] selected a series of TPEs based on different rubbers and thermoplastics. Three types of rubbers EPDM, ethylene vinyl acetate (EVA), and nitrile (NBR) were selected and the plastics include PP, PS, styrene acrylonitrile (SAN), and PA. It was shown that the ultimate mechanical properties such as stress at break, elongation, and the elastic recovery of these dynamically cured blends increased with the similarity of the rubber and plastic in respect to the critical surface tension for wetting and with the crystallinity of the plastic phase. Critical chain length of the rubber molecule, crystallinity of the hard phase (plastic), and the surface energy are a few of the parameters used in the analysis. Better results are obtained with a crystalline plastic material when the entanglement molecular length of the... [Pg.641]

The formation of a fibrillar structure in TLCP blends makes the mechanical properties of this kind of composites similar to those of conventional fiber reinforced thermoplastics [11,26]. However, because the molecular orientation and fibrillation of TLCPs are generally flow-induced, the formation, distribution, and alignment of these droplets and fibers are considerably more processing-dependent. We do not know ... [Pg.698]


See other pages where Mechanical properties thermoplastic is mentioned: [Pg.753]    [Pg.753]    [Pg.263]    [Pg.382]    [Pg.515]    [Pg.281]    [Pg.331]    [Pg.359]    [Pg.441]    [Pg.443]    [Pg.447]    [Pg.96]    [Pg.519]    [Pg.337]    [Pg.6]    [Pg.7]    [Pg.8]    [Pg.261]    [Pg.261]    [Pg.659]    [Pg.112]    [Pg.199]    [Pg.327]    [Pg.399]    [Pg.441]    [Pg.474]    [Pg.577]    [Pg.578]    [Pg.582]    [Pg.585]    [Pg.589]    [Pg.591]    [Pg.642]    [Pg.647]    [Pg.802]   
See also in sourсe #XX -- [ Pg.1050 ]

See also in sourсe #XX -- [ Pg.2242 ]

See also in sourсe #XX -- [ Pg.205 , Pg.206 , Pg.207 ]

See also in sourсe #XX -- [ Pg.288 ]