Sulfonated poly with

Robeson and Matzner were the first to report the synthesis of the sulfonation of DCDPS.205 This work makes it possible to synthesize sulfonated poly(arylene ether sulfone) with well-controlled structures. Ueda et al. used this monomer (Scheme 6.27) as a comonomer of DCDPS to react with bisphenol A and high-molecular-weight bisphenol-A-based copolymers with up to 30 mol % sulfonation achieved.206 Biphenol-based copolymers with up to 100 mol % sulfonation were recently reported by Wang et al.207... 

Polyphosphazenes sulfonates XIX with the anion covalently attached to the polymer are a new class of cation conductors that have been synthesized by Shriver [625]. They were obtained by reaction of Na0C2H4S03Na with an excess of polydichlorophosphazene in the presence of 15-crown-5, followed by the reaction of the partially substituted product with the sodium salt of poly(ethylene glycol methyl ether). The conductivity at 80 °C of the polymer with x=1.8, m=7.22 is 1.7x10 S cm This low conductivity can be attributed to an extensive ion pair formation between the sodium and sulfonate ions. 

Synthetic examples include the poly(meth)acrylates used as flocculating agents for water purification. Biological examples are the proteins, nucleic acids, and pectins. Chemically modified biopolymers of this class are carboxymethyl cellulose and the lignin sulfonates. Polyelectrolytes with cationic and anionic substituents in the same macromolecule are called polyampholytes. 

Chromatography by ion exchange on a sulfonated poly(styrene-co-divinyl benzene) phase has been proposed as a replacement for titrimetry.57 Eluted by a dilute solution of a neutral salt such as sodium ethanesulfonate, the conductance of the protons can be measured in the absence of a suppressor from sub-millimolar to molar concentration. The response factors of mono-, di-, and trichloroacetic acid and of o-phthalic acid were large and essentially equivalent to ethanesulfonic acid, while the response factor of acetic acid was far smaller. A syringe pump has generated pressures as high as 72,000 psi (5000 bar) in a capillary column packed with 1 p particles, generating a fraction capacity of 300 peaks in 30 minutes.58... 

Figure 10 Separation of monochloroacetate, dichloroacetate, and trichloroacetate on a sulfonated poly(styrene-divinyl benzene) column with suppressed conductivity detection. Column 2% cross-linked sulfonated poly(styrene-divinyl benzene) capacity 0.02 meq/g. Flow rate 64 ml/hr. Eluant 15 mM sodium phenate. Suppressor 0.28 x 25 cm Dowex 50W X8 column (200-400 mesh). Detector Chromatronix conductivity cell connected to a Dow conductivity meter. (Reprinted with permission from Small, H., Stevens, T. S., and Bauman, W. C., Anal. Chem., 47,1801,1975. 1975 Analytical Chemistry.)...

To date, much effort has been undertaken to develop new alternatives. For example, sulfonated aromatic polymers, i.e., polymers with the sulfonic acid groups directly attached to the main chain or carrying short pendant side chains with terminal sulfonic acid units, attract increasing interest because of their chemical and thermal stability, and the ease of the sulfonation procedure. Some of the proposed polymers are sulfonated polysulfone (SPSU) [134] sulfonated poly(phenylene oxide) (SPPO) [135] sulfonated poly-(ether ether ketone) (SPEEK) [136] poly(phenylquinoxaline) (PPQ) [137] and poly(benzeneimidazole) (PBI) [138],... 

Diederich and coworkers [10] synthesized so-called dendrophanes (Figure 13.6) containing a paracyclophane core embedded in dendritic poly(ether-amide) shells. X-ray crystal-structure analysis indicated that these dendrimers had an open cavity binding site in the center, suitable for the binding of aromatic guests. NMR and fluorescence titration experiments revealed a site specific binding between these dendrimers and 6-(p-toluidino)naphthalene-2-sulfonate (TNS) with a 1 1 association. Also, the fluorescence spectral shift of TNS, which is... 

In addition to Nafion-based catalyst layers, additional types have been developed, including CLs with different ion exchange capacities (lECs) [57,58] or with other hydrocarbon-type ionomers such as sulfonated poly(ether ether ketone) [58-60], sulfonated polysulfone [61,62], sulfonated polyether ionomers [63], and borosiloxane electrolytes [64], as well as sulfonated polyimide [65]. These nonfluorinated polymer materials have been targeted to reduce cost and/or increase operating temperature. Unfortunately, such CLs still encounter problems with low Pt utilization, flooding, and inferior performance compared wifh convenfional Nafion-based CLs. 

Sulfonated poly(arylene ether)s (SPAEKs) have also been developed for application in PEMs, with sulfonated poly(ether ether ketone) (SPEEK) (9a) as the archetypical example of this group. The base polymer of SPEEK is commercially available and relatively cheap, and sulfonation is a straightforward procedure using concentrated sulfuric acid. At sufficient levels of sulfonation, proton conductivity values for SPEEK are comparable to or higher than those of Nafion. However, this does lead to random copolymers where there... 

Ionic polymers other than Nation have also been included in ionic/non-ionic PEM blends. Poly(ether sulfone) (PES) has been used to strengthen SPEEK as well as sulfonated poly(ether sulfone) (SPES) with contents ranging from 20 to 60 wt%. The conductivity of the SPEEK component was relatively the same as unmodified SPEEK up to about 40 wt%. A similar effect was seen for PES/SPES blends, although the drop in MeOH permeability was more dramatic for PES/SPES from unmodified SPES than for PES/SPEEK from unmodified SPEEK. PVDF has also been used as a blending material to reinforce SPEEK. s The strength of the PEM was increased over unmodified SPEEK. Although conductivity levels decreased as a function of increasing PVDF content, the selectivity (ratio of proton conductivity to MeOH permeability) of the blended PEMs was increased over that of unmodified SPEEK and Nation. 

One of the first examples of this type of blend was composed of SPEEK or SPES as the acidic component and diaminated PES, poly(4-vinylpyridine) (P4VP), poly(benzimidazole) (PBl), or poly(ethyleneimine) (PEI) as the basic component. " For blend lEC values of 1.0 meq/g, conductivity values were reported to be good, as was H2/O2 EC performance. Thermal stabilities for these blends was also demonstrated to be high (>270°C). Other examples of acid-base PEMs include blends of SPPO and PBI, sulfonated poly(phthalazinone ether ketone) and aminated SPES, SPIs and aminated Pls, and SPEEK with PES bearing benzimidazole side groups, ° as well as an unusual example in which the blend is composed of sulfonated, hyper-branched polyether and pyridine-functionalized polysulfone. ... 

Kosmala, B. and Schauer, J. 2002. Ion-exchange membranes prepared by blending sulfonated poly(2,6-dimethyl-l,4-phenylene oxide) with polybenzimidazole. Journal of Applied Polymer Science 85 1118-1127. 

Alberti et al. investigated the influence of relative humidity on proton conductivity and the thermal stability of Nafion 117 and compared their results with data they obtained for sulfonated poly(ether ether ketone) membranes over the broad, high temperature range 80—160 °C and RHs from 35 to 100%. The authors constructed a special cell used in conjunction with an impedance analyzer for this purpose. Data were collected at high temperatures within the context of reducing Pt catalyst CO poison-... 

The highest level, at structural scales >10 nm, is that over which long-range transport takes place and diffusion depends on the degree of connectivity of the water pockets, which involves the concept of percolation. The observed decrease in water permeation with decreasing water volume fraction is more pronounced in sulfonated poly(ether ketone) than in Nafion, owing to differences in the state of percolation. Proton conductivity decreases in the same order, as well. 

These polymers show lower water uptake than the analogous sulfonated poly(arylene ether sulfone) materials, possibly suggesting some interaction between the aromatic nitrile and sulfonic acid. The phosphine oxide functional moiety could also be used as a compatibilizer with other materials. Sulfonated poly(arylene ether phosphine oxide sulfone) terpoly-mers have been prepared both with sulfonated triphenyl phosphine oxide and with triphenyl phosphine oxide with 3,3 -disulfonate-4,4 —dichlorodiphenyl sulfone as the sulfonic acid bearing monomer. Block copolymers containing phosphine oxide appear to avoid the ether—ether interchange that results when non—phosphine oxide blocks are utilized, and this is being further pursued. ... 

Sulfonated poly(4-substituted benzoyl-1,4-phenylene) homopolymers and copolymers using concentrated sulfuric acid or fuming sulfuric acid have been shown to form sulfonated polymers with variable degrees of sulfonation. To improve film formation of the sulfonated polyphenylenes, multiblock copolymers have been synthesized by reacting a more flexible poly(arylene ether sulfone) with sulfonated poly-phenylenes. ... 

The synthesis of poly(arylene ether sulfone)s with other bisphenols, e.g., 4,4-bis(4-hy-droxyphenyl)pentanoic acid, can be carried out in a similar way. 

Fastness Improvement. The wetfastnesses of dyeings on wool that has been chlorinated to prevent felting and has received a finish with synthetic resin (poly-amide-epichlorohydrin or polyurethane superwash wool) can be increased by means of methylol amide compounds. Both fastness and antifelting finish can be improved through the application of a polyquatemary compound [88]. Anionic condensation products such as aromatic sulfonic acids with formaldehyde can form a barrier at the surface of the fiber and thus diminish the bleeding of anionic dyes. 

Wijers, M.C., Jin, M., Wessling, M. and Strathmann, H. (1998) Supported liquid membranes modification with sulfonated poly(ether ether ketone) - permeability selectivity and stability Journal of Membrane Science, 147, 117. 

---