The protonated form of poly(vinyl amine) (PVAm—HCl) has two advantages over many cationic polymers high cationic charge densities are possible and the pendent primary amines have high reactivity. It has been appHed in water treatment, paper making, and textiles (qv). The protonated forms modified with low molecular weight aldehydes are usehil as fines and filler retention agents and are in use with recycled fibers. As with all new products, unexpected appHcations, such as in clear antiperspirants, have been found. It is usehil in many metal complexation appHcations (49). 

In conventional tenter orientation, the sequence of steps is as described above (MD—TD). In some cases it is advantageous to reverse the draw order (TD—MD) or to use multiple draw steps, eg, MD—TD—MD. These other techniques are used to produce "tensilized" films, where the MD tensile properties are enhanced by further stretching. The films are generally unbalanced in properties and in extreme cases may be fibrillated to give fiber-like elements for special textile appHcations. Tensilized poly(ethylene terephthalate) is a common substrate for audio and video magnetic tape and thermal transfer tape. 

Poly(methyl methacrylate). PMMA offers distinct advantages over BPA-PC with respect to significandy lower birefringence, higher modulus, and lower costs, but has not been successhil as a material for audio CDs and CD-ROM as well as a substrate material for WORM and EOD disks because of its high water absorption (which makes it prone to warp) and its unsuitabiUty for metallising, and less so because of its low resistance to... 

In the second quarter of the twentieth century, with the development of poly(vinyl chloride), nylon, polyurethane, and other polymers, many new and improved leather-like materials, so-called coated fabrics (qv), were placed on the market. Shortages of leather after World War 11 led to the expansion of these leather-like materials ("man-made" leathers) to replace leather in shoes, clothing, bags, upholstery, and other items. DurabiUty and waterproof quahties superior to leather made coated fabrics advantageous, in spite of imperfection in breathabihty and flexibiUty. Demands for shoes, clothing, and other items are stiU increasing due to growing world population and urbanization. 

Analysis for Poly(Ethylene Oxide). Another special analytical method takes advantage of the fact that poly(ethylene oxide) forms a water-insoluble association compound with poly(acryhc acid). This reaction can be used in the analysis of the concentration of poly(ethylene oxide) in a dilute aqueous solution. Ereshly prepared poly(acryhc acid) is added to a solution of unknown poly(ethylene oxide) concentration. A precipitate forms, and its concentration can be measured turbidimetricaHy. Using appropriate caUbration standards, the precipitate concentration can then be converted to concentration of poly(ethylene oxide). The optimum resin concentration in the unknown sample is 0.2—0.4 ppm. Therefore, it is necessary to dilute more concentrated solutions to this range before analysis (97). Low concentrations of poly(ethylene oxide) in water may also be determined by viscometry (98) or by complexation with KI and then titration with Na2S202 (99). 

Emulsions of fatty- and petroleum-based substances, both oils and waxes, of the o/w type are made by using blends of sorbitan fatty esters and their poly(oxyethylene) derivatives. Mixtures of poly(oxyethylene(20)) sorbitan monostearate (Polysorbate 60) and sorbitan monostearate are typical examples of blends used for lotions and creams. Both sorbitan fatty acid esters and their poly(oxyethylene) derivatives are particularly advantageous in cosmetic uses because of their very low skin irritant properties. Sorbitan fatty ester emulsifiers for w/o emulsions of mineral oil are used in hair preparations of both the lotion and cream type. Poly(oxyethylene(20)) sorbitan monolaurate is useflil in shampoo formulations (see Hairpreparations). Poly(oxyethylene) sorbitan surfactants are also used for solubilization of essential oils in the preparation of colognes and after-shave lotions. 

Polymer Solvent. Sulfolane is a solvent for a variety of polymers, including polyacrylonitrile (PAN), poly(vinyhdene cyanide), poly(vinyl chloride) (PVC), poly(vinyl fluoride), and polysulfones (124—129). Sulfolane solutions of PAN, poly(vinyhdene cyanide), and PVC have been patented for fiber-spinning processes, in which the relatively low solution viscosity, good thermal stabiUty, and comparatively low solvent toxicity of sulfolane are advantageous. Powdered perfluorocarbon copolymers bearing sulfo or carboxy groups have been prepared by precipitation from sulfolane solution with toluene at temperatures below 300°C. Particle sizes of 0.5—100 p.m result. 

Polymerization Solvent. Sulfolane can be used alone or in combination with a cosolvent as a polymerization solvent for polyureas, polysulfones, polysUoxanes, polyether polyols, polybenzimidazoles, polyphenylene ethers, poly(l,4-benzamide) (poly(imino-l,4-phenylenecarbonyl)), sUylated poly(amides), poly(arylene ether ketones), polythioamides, and poly(vinylnaphthalene/fumaronitrile) initiated by laser (134—144). Advantages of using sulfolane as a polymerization solvent include increased polymerization rate, ease of polymer purification, better solubilizing characteristics, and improved thermal stabUity. The increased polymerization rate has been attributed not only to an increase in the reaction temperature because of the higher boiling point of sulfolane, but also to a decrease in the activation energy of polymerization as a result of the contribution from the sulfonic group of the solvent. 

Ionic polymers are also formulated from TDI and MDI (43). Poly(urethane urea) and polyurea ionomers are obtained from divalent metal salts of /)-aminohen2oic acid, MPA, dialkylene glycol, and 2,4-TDI (44). In the case of polyureas, the glycol extender is omitted. If TDI is used in coatings apphcations, it is usually converted to a derivative to lower the vapor pressure. A typical TDI prepolymer is the adduct of TDI with trimethyl olpropane (Desmodur L). Carbodiimide-modified MDI offers advantages in polyester-based systems because of improved hydrolytic stabihty (45). Moisture cure systems based on aromatic isocyanates are also available. 

The use of poly(vinyl acetate) or copolymer emulsions eliminates the need for expensive, flammable, odorous, or toxic solvents and the need for the recovery of such solvents. They are easy to apply and the equipment is easy to clean with water, if done promptly. Emulsions also offer the advantage of high sohds content with fluidity, siace the viscosity of emulsions are iadependent of the molecular weight of the resia iu the particles. 

Poly(vinyl acetate) latex paints are the first choice for interior use (149). Their abihty to protect and decorate is reinforced by several advantages belonging exclusively to latex paints they do not contain solvents so that physiological harm and fire ha2ards are eliminated they are odorless they are easy to apply with spray gun, roUer-coater, or bmsh and they dry rapidly. The paint can be thinned with water, and bmshes or coaters can be cleaned with soap and tepid water. The paint is usually dry in 20 minutes to two hours, and two coats may be applied the same day. 

Often poly(ethylene glycol)s or derivatives thereof can be used instead of crowns or onium salts advantageously, although their catalytic activity frequently tends to be somewhat lower. The possible toxicity of crowns and cryptands and the price difference between these compounds and onium salts (100 1 to 10 1) are other important factors to be considered. Thus (1) [17455-13-9] (2) [14187-32-7] and (3) [16069-36-6] and cryptands are used more often in laboratory work, whereas onium salts are more important for industrial processes. 

Miscellaneous Commercial Applications. Dimer acids are components of "downweU" corrosion inhibitors for oil-drilling equipment (see Petroleum Corrosion and corrosion inhibitors). This may account for 10% of current dimer acid use (71). The acids, alkyl esters, and polyoxyalkylene dimer esters are used commercially as components of metal-working lubricants (see Lubrication). Dimer esters have achieved some use in specialty lubricant appHcations such as gear oils and compressor lubricants. The dimer esters, compared to dibasic acid esters, polyol esters and poly(a-olefin)s, are higher in cost and of higher viscosity. The higher viscosity, however, is an advantage in some specialties, and the dimer esters are very stable thermally and can be made quite oxidatively stable by choice of proper additives. 

Another type of membrane is the dynamic membrane, formed by dynamically coating a selective membrane layer on a finely porous support. Advantages for these membranes are high water flux, generation and regeneration in situ abiUty to withstand elevated temperatures and corrosive feeds, and relatively low capital and operating costs. Several membrane materials are available, but most of the work has been done with composites of hydrous zirconium oxide and poly(acryhc acid) on porous stainless steel or ceramic tubes. 

The use of a catalytic quantity of alkah equivalent to only a small fraction of the acetate has the advantage that contamination of the poly(vinyl alcohol) with salts, which are difficult to remove, is minimized. A variant of the process is the use of a mixture of alcohol with the acetate ester produced by the alcoholysis as the alcoholyzing agent. This provides a means of controlling the completeness of removal of the acetate groups from the poly(vinyl acetate) (111). 

The polymers are of interest as water-soluble packaging films for a wide variety of domestic and industrial materials. (Additional advantages of the poly(ethylene oxide)s are that they remain dry to the feel at high humidities and may be heat sealed.) The materials are also of use in a number of solution application such as textile sizes and thickening agents. As a water-soluble film they are competitive with poly(vinyl alcohol) whereas in their solution applications they meet competition from many longer established natural and synthetic water-soluble polymers. 

---