Thus, even though limited to relatively few monomers, anionic polymerizations exhibiting the foregoing features have attracted both academic and commercial interest. This review covers various aspects of these systems. 

The ring-opening polymerization of cyclic monomers can be performed by ionic chain polymerization, as is the case of epoxy monomers. Anionic polymerization of ethylene oxide propylene oxide, and caprolactone can be initiated by alkoxides ... 

However, this was not the case for the monomer anionically polymerized at a pH of 8.5, where the was found to be much higher than those at lower... 

In the case of anionic polymerization (with 2-isoprOpenylthiazole) there is a chain-monomer equilibrium. Furthermore, lowering the temperature of polymerization increases the conversion of monomer to polymer (314). 

The kinds of vinyl monomers which undergo anionic polymerization are those with electron-withdrawing substituents such as the nitrile, carboxyl, and phenyl groups. We represent the catalysts as AB in this discussion these are substances which break into a cation (A ) and an anion (B ) under the conditions of the reaction. In anionic polymerization it is the basic anion which adds across the double bond of the monomer to form the active center for polymerization ... 

The electron-releasing R group helps stabilize this cation. As with anionic polymerization, the separation of the ions and hence the ease of monomer insertion depends on the reaction medium. The propagation reaction may be written as... 

A brief review has appeared covering the use of metal-free initiators in living anionic polymerizations of acrylates and a comparison with Du Font s group-transfer polymerization method (149). Tetrabutylammonium thiolates mn room temperature polymerizations to quantitative conversions yielding polymers of narrow molecular weight distributions in dipolar aprotic solvents. Block copolymers are accessible through sequential monomer additions (149—151) and interfacial polymerizations (152,153). 

Although the anionic polymerization mechanism is the predominant one for the cyanoacryhc esters, the monomer will polymerize free-radically under prolonged exposure to heat or light. To extend the usable shelf life, free-radical stabilizers such as quinones or hindered phenols are a necessary part of the adhesive formulation. 

Cyanoacrylate adhesives (Super-Glues) are materials which rapidly polymerize at room temperature. The standard monomer for a cyanoacrylate adhesive is ethyl 2-cyanoacrylate [7085-85-0], which readily undergoes anionic polymerization. Very rapid cure of these materials has made them widely used in the electronics industry for speaker magnet mounting, as weU as for wire tacking and other apphcations requiring rapid assembly. Anionic polymerization of a cyanoacrylate adhesive is normally initiated by water. Therefore, atmospheric humidity or the surface moisture content must be at a certain level for polymerization to take place. These adhesives are not cross-linked as are the surface-activated acryhcs. Rather, the cyanoacrylate material is a thermoplastic, and thus, the adhesives typically have poor temperature resistance. 

The use of alkaU metals for anionic polymerization of diene monomers is primarily of historical interest. A patent disclosure issued in 1911 (16) detailed the use of metallic sodium to polymerize isoprene and other dienes. Independentiy and simultaneously, the use of sodium metal to polymerize butadiene, isoprene, and 2,3-dimethyl-l,3-butadiene was described (17). Interest in alkaU metal-initiated polymerization of 1,3-dienes culminated in the discovery (18) at Firestone Tire and Rubber Co. that polymerization of neat isoprene with lithium dispersion produced high i7j -l,4-polyisoprene, similar in stmcture and properties to Hevea natural mbber (see ELASTOLffiRS,SYNTHETic-POLYisoPRENE Rubber, natural). 

The mechanism of the anionic polymerization of styrenes and 1,3-dienes initiated by alkaU metals has been described in detail (3,20) as shown in equations 3—5 where Mt represents an alkaU metal and M is a monomer molecule. Initiation is a heterogeneous process occurring on the metal surface. The... 

Anionic polymerization of vinyl monomers can be effected with a variety of organometaUic compounds alkyllithium compounds are the most useful class (1,33—35). A variety of simple alkyllithium compounds are available commercially. Most simple alkyllithium compounds are soluble in hydrocarbon solvents such as hexane and cyclohexane and they can be prepared by reaction of the corresponding alkyl chlorides with lithium metal. Methyllithium [917-54-4] and phenyllithium [591-51-5] are available in diethyl ether and cyclohexane—ether solutions, respectively, because they are not soluble in hydrocarbon solvents vinyllithium [917-57-7] and allyllithium [3052-45-7] are also insoluble in hydrocarbon solutions and can only be prepared in ether solutions (38,39). Hydrocarbon-soluble alkyllithium initiators are used directiy to initiate polymerization of styrene and diene monomers quantitatively one unique aspect of hthium-based initiators in hydrocarbon solution is that elastomeric polydienes with high 1,4-microstmcture are obtained (1,24,33—37). Certain alkyllithium compounds can be purified by recrystallization (ethyllithium), sublimation (ethyllithium, /-butyUithium [594-19-4] isopropyllithium [2417-93-8] or distillation (j -butyUithium) (40,41). Unfortunately, / -butyUithium is noncrystaUine and too high boiling to be purified by distiUation (38). Since methyllithium and phenyllithium are crystalline soUds which are insoluble in hydrocarbon solution, they can be precipitated into these solutions and then redissolved in appropriate polar solvents (42,43). OrganometaUic compounds of other alkaU metals are insoluble in hydrocarbon solution and possess negligible vapor pressures as expected for salt-like compounds. 

Nylon-6 can also be produced from molten caprolactam using strong bases as catalysts (anionic polymerization) this is used as the basis of monomer casting and reaction injection mol ding (RIM). Anionic polymerization proceeds much faster than the hydrolytic route but products retain catalysts which may need to be extracted. 

Anionic polymerization, if carried out properly, can be truly a living polymerization (160). Addition of a second monomer to polystyryl anion results in the formation of a block polymer with no detectable free PS. This technique is of considerable importance in the commercial preparation of styrene—butadiene block copolymers, which are used either alone or blended with PS as thermoplastics. 

Commercially, the poly(styrene-Aelastomer-Astyrene) materials are made by anionic polymerization (7,45—47). An alkyllithium initiator (RLi) first reacts with styrene [100-42-5] monomer ... 

Commercially, anionic polymerization is limited to three monomers styrene, butadiene, and isoprene [78-79-5], therefore only two useful A—B—A block copolymers, S—B—S and S—I—S, can be produced direcdy. In both cases, the elastomer segments contain double bonds which are reactive and limit the stabhity of the product. To improve stabhity, the polybutadiene mid-segment can be polymerized as a random mixture of two stmctural forms, the 1,4 and 1,2 isomers, by addition of an inert polar material to the polymerization solvent ethers and amines have been suggested for this purpose (46). Upon hydrogenation, these isomers give a copolymer of ethylene and butylene. 

Radical copolymerization is used in the manufacturing of random copolymers of acrylamide with vinyl monomers. Anionic copolymers are obtained by copolymerization of acrylamide with acrylic, methacrylic, maleic, fu-maric, styrenesulfonic, 2-acrylamide-2-methylpro-panesulfonic acids and its salts, etc., as well as by hydrolysis and sulfomethylation of polyacrylamide Cationic copolymers are obtained by copolymerization of acrylamide with jV-dialkylaminoalkyl acrylates and methacrylates, l,2-dimethyl-5-vinylpyridinum sulfate, etc. or by postreactions of polyacrylamide (the Mannich reaction and Hofmann degradation). Nonionic copolymers are obtained by copolymerization of acrylamide with acrylates, methacrylates, styrene derivatives, acrylonitrile, etc. Copolymerization methods are the same as the polymerization of acrylamide. 

Photoinitiators provide a convenient route for synthesizing vinyl polymers with a variety of different reactive end groups. Under suitable conditions, and in the presence of a vinyl monomer, a block AB or ABA copolymer can be produced which would otherwise be difficult or impossible to produce by another polymerization method. Moreover, synthesis of block copolymers by this route is much more versatile than those based on anionic polymerization, since a wider range of a monomers can be incorporated into the blocks. 

The block copolymer produced by Bamford s metal carbonyl/halide-terminated polymers photoinitiating systems are, therefore, more versatile than those based on anionic polymerization, since a wide range of monomers may be incorporated into the block. Although the mean block length is controllable through the parameters that normally determine the mean kinetic chain length in a free radical polymerization, the molecular weight distributions are, of course, much broader than with ionic polymerization and the polymers are, therefore, less well defined,... 

Anionic polymerization is better for vinyl monomers with electron withdrawing groups that stabilize the intermediates. Typical monomers best polymerized by anionic initiators include acrylonitrile, styrene, and butadiene. As with cationic polymerization, a counter ion is present with the propagating chain. The propagation and the termination steps are similar to cationic polymerization. 

---