Those steps or reactions within chain reactions that generate one or more reactive intermediates (often free radicals). In such propagation reactions, the newly formed reactive intermediate (c.g., free radical) can then react with another molecule to produce another reactive intermediate. See Chain Reaction Chain Transfer Initiation Termination... 

FLUORESCENCE PROPAGATION CHAIN REACTION CHAIN TRANSFER INITIATION TERMINATION Propanal, synthesis of,... 

This same principle of chain transfer initiation can be used for the preparation of graft and (or) block copolymers if a polymer of one kind is dissolved in the presence of a monomer of another kind, and if the mixture is then subjected to polymerization conditions (49, 50, 203). 

Grafting by chain transfer initiation has been carried out not only in homogenous medium but also by emulsion polymerization techniques, where the monomer and the catalyst are added to a latex containing the original backbone polymer (99). The efficiency of grafting increases with an increase of temperature of polymerization and with an increase of initiator concentration (generally potassium persulfate) these results indicate not only that the chain transfer reaction has a higher activation... 

Radical Polymerization. Free radical polymerization consists of three steps, initiation, propagation, and termination or chain transfer. Initiation consists of two steps, decomposition of the initiator to form a radical species, followed by addition of the initiator to the first monomer unit. 

Chain transfer initiation may be promoted by immobilizing one of the components (usually the reducing agent) on cellulose in order to diminish the probability of reaction between the low molecular weight radical and the monomer. The best results were obtained with systems generating a highly active, small amount of OH radical63. ... 

Inhibitors slow or stop polymerization by reacting with the initiator or the growing polymer chain. The free radical formed from an inhibitor must be sufficiently unreactive that it does not function as a chain-transfer agent and begin another growing chain. Benzoquinone is a typical free-radical chain inhibitor. The resonance-stabilized free radical usually dimerizes or disproportionates to produce inert products and end the chain process. 

Elsewhere in this chapter we shall see that other reactions-notably, chain transfer and chain inhibition-also need to be considered to give a more fully developed picture of chain-growth polymerization, but we shall omit these for the time being. Much of the argumentation of this chapter is based on the kinetics of these three mechanistic steps. We shall describe the rates of the three general kinds of reactions by the notation Rj, Rp, and R for initiation, propagation, and termination, respectively. 

In the next three sections we consider initiation, termination, and propagation steps in the free-radical mechanism for addition polymerization. One should bear in mind that two additional steps, inhibition and chain transfer, are being ignored at this point. We shall take up these latter topics in Sec. 6.8. 

Throughout this section we have used mostly p and u to describe the distribution of molecular weights. It should be remembered that these quantities are defined in terms of various concentrations and therefore change as the reactions proceed. Accordingly, the results presented here are most simply applied at the start of the polymerization reaction when the initial concentrations of monomer and initiator can be used to evaluate p or u. The termination constants are known to decrease with the extent of conversion of monomer to polymer, and this effect also complicates the picture at high conversions. Note, also, that chain transfer has been excluded from consideration in this section, as elsewhere in the chapter. We shall consider chain transfer reactions in the next section. 

This suggests that polymerizations should be conducted at different ratios of [SX]/[M] and the molecular weight measured for each. Equation (6.89) shows that a plot of l/E j. versus [SX]/[M] should be a straight line of slope sx Figure 6.8 shows this type of plot for the polymerization of styrene at 100°C in the presence of four different solvents. The fact that all show a common intercept as required by Eq. (6.89) shows that the rate of initiation is unaffected by the nature of the solvent. The following example examines chain transfer constants evaluated in this situation. 

Chain transfer to initiator or monomer cannot always be ignored. It may be possible, however, to evaluate the transfer constants to these substances by investigating a polymerization without added solvent or in the presence of a solvent for which Cgj is known to be negligibly small. In this case the transfer constants Cjj and Cj determined from experiments in which (via... 

In ionic polymerizations termination by combination does not occur, since all of the polymer ions have the same charge. In addition, there are solvents such as dioxane and tetrahydrofuran in which chain transfer reactions are unimportant for anionic polymers. Therefore it is possible for these reactions to continue without transfer or termination until all monomer has reacted. Evidence for this comes from the fact that the polymerization can be reactivated if a second batch of monomer is added after the initial reaction has gone to completion. In this case the molecular weight of the polymer increases, since no new growth centers are initiated. Because of this absence of termination, such polymers are called living polymers. 

In production, anhydrous formaldehyde is continuously fed to a reactor containing well-agitated inert solvent, especially a hydrocarbon, in which monomer is sparingly soluble. Initiator, especially amine, and chain-transfer agent are also fed to the reactor (5,16,17). The reaction is quite exothermic and polymerisation temperature is maintained below 75°C (typically near 40°C) by evaporation of the solvent. Polymer is not soluble in the solvent and precipitates early in the reaction. 

The enthalpy of the copolymerization of trioxane is such that bulk polymerization is feasible. For production, molten trioxane, initiator, and comonomer are fed to the reactor a chain-transfer agent is in eluded if desired. Polymerization proceeds in bulk with precipitation of polymer and the reactor must supply enough shearing to continually break up the polymer bed, reduce particle size, and provide good heat transfer. The mixing requirements for the bulk polymerization of trioxane have been reviewed (22). Raw copolymer is obtained as fine emmb or flake containing imbibed formaldehyde and trioxane which are substantially removed in subsequent treatments which may be combined with removal of unstable end groups. 

The molecular weight of a polymer can be controlled through the use of a chain-transfer agent, as well as by initiator concentration and type, monomer concentration, and solvent type and temperature. Chlorinated aUphatic compounds and thiols are particularly effective chain-transfer agents used for regulating the molecular weight of acryUc polymers (94). Chain-transfer constants (C at 60°C) for some typical agents for poly(methyl acrylate) are as follows (87) ... 

Emulsion Process. The emulsion polymerization process utilizes water as a continuous phase with the reactants suspended as microscopic particles. This low viscosity system allows facile mixing and heat transfer for control purposes. An emulsifier is generally employed to stabilize the water insoluble monomers and other reactants, and to prevent reactor fouling. With SAN the system is composed of water, monomers, chain-transfer agents for molecular weight control, emulsifiers, and initiators. Both batch and semibatch processes are employed. Copolymerization is normally carried out at 60 to 100°C to conversions of - 97%. Lower temperature polymerization can be achieved with redox-initiator systems (51). 

In addition to the monomers, the polymerization ingredients include an emulsifier, a polymerization initiator, and usually a chain-transfer agent for molecular weight control. 

If a linear mbber is used as a feedstock for the mass process (85), the mbber becomes insoluble in the mixture of monomers and SAN polymer which is formed in the reactors, and discrete mbber particles are formed. This is referred to as phase inversion since the continuous phase shifts from mbber to SAN. Grafting of some of the SAN onto the mbber particles occurs as in the emulsion process. Typically, the mass-produced mbber particles are larger (0.5 to 5 llm) than those of emulsion-based ABS (0.1 to 1 llm) and contain much larger internal occlusions of SAN polymer. The reaction recipe can include polymerization initiators, chain-transfer agents, and other additives. Diluents are sometimes used to reduce the viscosity of the monomer and polymer mixture to faciUtate processing at high conversion. The product from the reactor system is devolatilized to remove the unreacted monomers and is then pelletized. Equipment used for devolatilization includes single- and twin-screw extmders, and flash and thin film evaporators. Unreacted monomers are recovered for recycle to the reactors to improve the process yield. 

Suitable catalysts are /-butylphenylmethyl peracetate and phenylacetjdperoxide or redox catalyst systems consisting of an organic hydroperoxide and an oxidizable sulfoxy compound. One such redox initiator is cumene—hydroperoxide, sulfur dioxide, and a nucleophilic compound, such as water. Sulfoxy compounds are preferred because they incorporate dyeable end groups in the polymer by a chain-transfer mechanism. Common thermally activated initiators, such as BPO and AIBN, are too slow for use in this process. 

Tetiafluoioethylene—peifluoiopiopyl vinyl ethei copolymeis [26655-00-5] aie made in aqueous (1,2) oi nonaqueous media (3). In aqueous copolymerizations water-soluble initiators and a perfluorinated emulsifying agent are used. Molecular weight and molecular weight distribution are controlled by a chain-transfer agent. Sometimes a second phase is added to the reaction medium to improve the distribution of the vinyl ether in the poljmier (11) a buffer is also added. 

In nonaqueous copolymerization, fluorinated acyl peroxides are used as initiators that are soluble in the medium (12) a chain-transfer agent may be added for molecular weight control. 

Suspension polymerization of VDE in water are batch processes in autoclaves designed to limit scale formation (91). Most systems operate from 30 to 100°C and are initiated with monomer-soluble organic free-radical initiators such as diisopropyl peroxydicarbonate (92—96), tert-huty peroxypivalate (97), or / fZ-amyl peroxypivalate (98). Usually water-soluble polymers, eg, cellulose derivatives or poly(vinyl alcohol), are used as suspending agents to reduce coalescence of polymer particles. Organic solvents that may act as a reaction accelerator or chain-transfer agent are often employed. The reactor product is a slurry of suspended polymer particles, usually spheres of 30—100 pm in diameter they are separated from the water phase thoroughly washed and dried. Size and internal stmcture of beads, ie, porosity, and dispersant residues affect how the resin performs in appHcations. 

Butyl mbber, a copolymer of isobutjiene with 0.5—2.5% isoprene to make vulcanization possible, is the most important commercial polymer made by cationic polymerization (see Elastomers, synthetic-butyl rubber). The polymerization is initiated by water in conjunction with AlCl and carried out at low temperature (—90 to —100° C) to prevent chain transfer that limits the molecular weight (1). Another important commercial appHcation of cationic polymerization is the manufacture of polybutenes, low molecular weight copolymers of isobutylene and a smaller amount of other butenes (1) used in adhesives, sealants, lubricants, viscosity improvers, etc. 

---