The susceptibihty of dialkyl peroxides to acids and bases depends on peroxide stmcture and the type and strength of the acid or base. In dilute aqueous sulfuric acid (<50%) di-Z fZ-butyl peroxide is resistant to reaction whereas in concentrated sulfuric acid this peroxide gradually forms polyisobutylene. In 50 wt % methanolic sulfuric acid, Z fZ-butyl methyl ether is produced in high yield (66). In acidic environments, unsymmetrical acychc alkyl aralkyl peroxides undergo carbon—oxygen fission, forming acychc alkyl hydroperoxides and aralkyl carbonium ions. The latter react with nucleophiles,... 

The primary component of a fixation bath, thiosulfate, tends to decompose in acidic environments according to the following reaction ... 

Iodized Salt. Iodized table salt has been used to provide supplemental iodine to the U.S. population since 1924, when producers, in cooperation with the Michigan State Medical Society (24), began a voluntary program of salt iodization in Michigan that ultimately led to the elimination of iodine deficiency in the United States. More than 50% of the table salt sold in the United States is iodized. Potassium iodide in table salt at levels of 0.006% to 0.01% KI is one of two sources of iodine for food-grade salt approved by the U.S. Food and Dmg Administration. The other, cuprous iodide, is not used by U.S. salt producers. Iodine may be added to a food so that the daily intake does not exceed 225 p.g for adults and children over four years of age. Potassium iodide is unstable under conditions of extreme moisture and temperature, particularly in an acid environment. Sodium carbonate or sodium bicarbonate is added to increase alkalinity, and sodium thiosulfate or dextrose is added to stabilize potassium iodide. Without a stabilizer, potassium iodide is oxidized to iodine and lost by volatilization from the product. Potassium iodate, far more stable than potassium iodide, is widely used in other parts of the world, but is not approved for use in the United States. 

The solubihty characteristics of sodium acyl isethionates allow them to be used in synthetic detergent (syndet) bars. Complex blends of an isethionate and various soaps, free fatty acids, and small amounts of other surfactants reportedly are essentially nonirritant skin cleansers (66). As a rule, the more detersive surfactants, for example alkyl sulfates, a-olefin sulfonates, and alkylaryl sulfonates, are used in limited amounts in skin cleansers. Most skin cleansers are compounded to leave an emollient residue on the skin after rinsing with water. Free fatty acids, alkyl betaines, and some compatible cationic or quaternary compounds have been found to be especially useful. A mildly acidic environment on the skin helps control the growth of resident microbial species. Detergent-based skin cleansers can be formulated with abrasives to remove scaly or hard-to-remove materials from the skin. 

More than 95% of the cumene produced is used as feedstock for the production of phenol (qv) and its coproduct acetone (qv). The cumene oxidation process for phenol synthesis has been growing in popularity since the 1960s and is prominent today. The first step of this process is the formation of cumene hydroperoxide [80-15-9]. The hydroperoxide is then selectively cleaved to phenol [108-95-2] and acetone [67-64-1/ in an acidic environment (21). 

The mode of attack of electrophilic reagents (E ) at ring carbon atoms is jS to the heteroatoms as shown, for example, in (11) and (12) the intermediates usually revert to type by proton loss. Halogenation takes place more readily than it does in benzene (Section 4.02.1.4.5). Nitration and sulfonation also occur however, in the strongly acidic environment required the compounds are present mainly as less reactive hydroxyazolium ions, e.g. (13). 

Protonation or Lewis acid complexation of a heteroatom invites nucleophilic attack, including nucleophilic attack by a parent molecule. Oligomerization and polymerization are thus often the results of bringing heterocycles into an acid environment without making sure that all of the potentially nucleophilic sites are protonated. 

Lead, because of its history as an air emission, has been fairly mobile and is particularly soluble in acid environments. Silver is used widely in the electronics industry. Intake of silver compounds can result in permanent discoloration of the skin and may result in damage to kidneys, lungs, mucous membranes, and other organs. 

Limitations on the use of cast irons are similar to those for steel, since in many environments most cast iron has poor corrosion resistance. Most grades are also susceptible to graphitization (the loss of iron, leaving a weak structure of graphite) in acidic environments below a pH of approximately 5.5. This attack occurs in soils. 

Copper additions appear to have the particular effect of reducing the corrosion stimulating effect of the sulphur content of an iron exposed to acid and the effect is thus less marked in low sulphur irons. Because sulphur can stimulate corrosion in acidic environments, it is usually kept as low as possible in irons to be used under these conditions. A low sulphur content is in any case metallurgically desirable. 

In the chemical process industry molybdenum has found use as washers and bolts to patch glass-lined vessels used in sulphuric acid and acid environments where nascent hydrogen is produced. Molybdenum thermocouples and valves have also been used in sulphuric acid applications, and molybdenum alloys have been used as reactor linings in plant used for the production of n-butyl chloride by reactions involving hydrochloric and sulphuric acids at temperatures in excess of 170°C. Miscellaneous applications where molybdenum has been used include the liquid phase Zircex hydrochlorination process, the Van Arkel Iodide process for zirconium production and the Metal Hydrides process for the production of super-pure thorium from thorium iodide. 

In short, the current demand for cathodic protection varies according to the aggressiveness of the corrosive environment. It is for this reason that cathodic protection finds its greatest application where the pH is close to neutral. The more acid environments entail a current output that rapidly becomes uneconomic. The more alkaline environments prove less aggressive to the structure and therefore often do not justify cathodic protection. Table 10.5 provides some estimated current densities for cathodic protection that illustrate the point. 

Both iron- and copper-based alloys are corroded more easily on either side of the neutral pH band. In low pH conditions e.g. due to carbon dioxide, the acidic environments attack the alloys readily, causing damage both at the points of initial corrosion and perhaps, consequentially, further along the system, by screening the surface with corrosion products and permitting the development of differential aeration cells. 

One of the most important properties of commercial glasses is their great resistance to corrosion any chemical laboratory apparatus, any window or windscreen provides an excellent illustration. Windows remain virtually unchanged for centuries, resisting the influences of atmosphere and radiation. A vast range of products may be safely stored in glass for decades at ordinary temperatures, and the fact that gleiss can be used with alkaline, neutral and acid environments allows the same equipment to be used for a variety of processes. 

---