Thermoset elastomers mechanical properties

The classification given in Table 1 is based on the process, ie, thermosetting or thermoplastic, by which polymers in general are formed into usehil articles and on the mechanical properties, ie, rigid, flexible, or mbbery, of the final product. AH commercial polymers used for molding, extmsion, etc, fit into one of these six classifications the thermoplastic elastomers are the newest. 

The PGS obtained by Wang and coworkers was a kind of thermoset elastomer with the Young s modulus of 0.282 0.025 MPa, a tensile strain of at least 267 zE 59.4%, and a tensUe strength was at least 0.5 MPa. The mechanical properties of PGS were well consisted with that of some common soft tissues. Although PGS is a thermoset polymer, its prepolymer can be processed into various shapes by solving it in common organic solvents such as 1,3-dioxolane, tetrahydrofuran, isopropanol, ethanol, and iV,M-dimethylformamide. Porous scaffolds can be fabricated by salt leaching. 

Uniaxial deformations give prolate (needle-shaped) ellipsoids, and biaxial deformations give oblate (disc-shaped) ellipsoids [220,221], Prolate particles can be thought of as a conceptual bridge between the roughly spherical particles used to reinforce elastomers and the long fibers frequently used for this purpose in thermoplastics and thermosets. Similarly, oblate particles can be considered as analogues of the much-studied clay platelets used to reinforce a variety of materials [70-73], but with dimensions that are controllable. In the case of non-spherical particles, their orientations are also of considerable importance. One interest here is the anisotropic reinforcements such particles provide, and there have been simulations to better understand the mechanical properties of such composites [86,222],... 

Thermosets are generally used in advanced composites due to their excellent thermal and dimensional stability, high modulus, and good mechanical properties. Because thermoset resins are inherently brittle, however, some applications require improved fracture resistance. Toughening of thermosets has been achieved through various methods, such as incorporation of reactive liquid rubber [1-9], elastomer [10], or rigid thermoplastics [11-25], and IPN formation with ductile component [26]. 

Organic matrices are divided into thermosets and thermoplastics. The main thermoset matrices are polyesters, epoxies, phenolics, and polyimides, polyesters being the most widely used in commercial applications (3,4). Epoxy and polyimide resins are applied in advanced composites for structural aerospace applications (1,5). Thermoplastics Uke polyolefins, nylons, and polyesters are reinforced with short fibers (3). They are known as traditional polymeric matrices. Advanced thermoplastic polymeric matrices like poly(ether ketones) and polysulfones have a higher service temperature than the traditional ones (1,6). They have service properties similar to those of thermoset matrices and are reinforced with continuous fibers. Of course, composites reinforced with discontinuous fibers have weaker mechanical properties than those with continuous fibers. Elastomers are generally reinforced by the addition of carbon black or silica. Although they are reinforced polymers, traditionally they are studied separately due to their singular properties (see Chap. 3). 

It will be shown in Chapter 11 that the correlations developed in this monograph can be combined with other correlations that are found in the literature (preferably with the equations developed by Seitz in the case of thermoplastics, and with the equations of rubber elasticity theory with finite chain extensibility for elastomers), to predict many of the key mechanical properties of polymers. These properties include the elastic (bulk, shear and tensile) moduli as well as the shear yield stress and the brittle fracture stress. In addition, new correlations in terms of connectivity indices will be developed for the molar Rao function and the molar Hartmann function whose importance in our opinion is more of a historical nature. A large amount of the most reliable literature data on the mechanical properties of polymers will also be listed. The observed trends for the mechanical properties of thermosets will also be discussed. Finally, the important and challenging topic of the durability of polymers under mechanical deformation will be addressed, to review the state-of-the-art in this area where the existing modeling tools are of a correlative (rather than truly predictive) nature at this time. 

It is necessary to define precisely what is reinforcement, because this word covers very different meanings when applied to thermoplastics, thermosets, or elastomers. Confusion is mainly due to the fact that reinforcement qualifies an increase in mechanical properties, but what is expected as mechanical properties is very different considering the different matrices and applications. 

Silicones and polyurethanes are the two classes of elastomers used for in vivo applications. Both are versatile polymers with a wide range of mechanical properties. Polyuredianes tend to be stiffer and stronger than silicones, whereas silicones are more inert and have the advantage of being oxygen-permeable. Polyurethanes are more versatile from a processing standpoint since many polyurethanes are thermoplastics, whereas silicones rely on covalent cross-linking and are therefore thermosets. 

Although thermoplastics, thermosets and elastomers can be used as matrix of polymer composites, thermosets are more widely used mainly due to the processing techniques employed in their manufactme, that allow for the easy use of long fibers, mats and fabrics as reinforcement. Thermosets are also generally more thermally stable than thermoplastics, and these two reasons lead to products with significantly higher mechanical properties which are less affected by thermal variations than thermoplastic composites [1,2,12],... 

---