Thermogravimetric analysis measurements

Thermogravimetric analysis measurements have also provided information regarding dendrimer decomposition. Thermolysis of G40H dendrimers on a gold surface in both air and argon environments has shown that the greatest weight loss... 

Thermogravimetric analysis measurements were performed with a Netzsch STA 429. Flows ofH2 or O2 (10 ml/min) in argon (50 ml/min) were used and a heating rate was chosen of 5 C / minute. 

TGA ThermoGravimetric Analysis measures weight changes in a material as a function of temperature (or time) under a controlled atmosphere to determine the thermal stability and composition. 

Thermogravimetric analysis measures variations in the weight of a sample under consideration as a function of time or temperature. The technique is... 

Thermogravimetric analysis measures the amount and rate of weight change in a material as a function of temperature, or time, in a controlled atmosphere. These measurements are mainly used to determine the composition of polymer products and precursors (e.g. additive master batches), but can also be used to measure thermal stability and study the effects that additives such as antidegradants have on this property. 

About 10 g of the physical mixture, containing the polymer and the respective plasticizing substance at quantities from 0% to 25.5% (w/w), was prepared. The mixture was manually poured into the ram extruder and equilibrated for 10 min at 140°C. The stability of the polymer under the chosen conditions has previously been analyzed by thermogravimetric analysis measurements [35,42]. All mixtures were exkuded three times at a plunger velocity of 15 mm/min through a 2.0-mm orifice. 

The definition of polymer thermal stabiUty is not simple owing to the number of measurement techniques, desired properties, and factors that affect each (time, heating rate, atmosphere, etc). The easiest evaluation of thermal stabiUty is by the temperature at which a certain weight loss occurs as observed by thermogravimetric analysis (tga). Early work assigned a 7% loss as the point of stabiUty more recentiy a 10% value or the extrapolated break in the tga curve has been used. A more reaUstic view is to compare weight loss vs time at constant temperature, and better yet is to evaluate property retention time at temperature one set of criteria has been 177°C for 30,000 h, or 240°C for 1000 h, or 538°C for 1 h, or 816°C for 5 min (1). 

This phenomenon can be demonstrated by both measuring the changes of the thermal properties of the ECA homopolymer and in adhesion tests. The addition of only 1 wt.% of 9 to a sample of the ECA homopolymer significantly increases the onset of decomposition in the thermogravimetric analysis (TGA) of the polymer, as seen in Fig. 9 [29]. 

When solids react, we would like to know at what temperature the solid state reaction takes place. If the solid decomposes to a different composition, or phase, we would like to have this knowledge so that we can predict and use that knowledge In preparation of desired materials. Sometimes, intermediate compounds form before the final phase. In this chapter, we will detail some of the measurements used to characterize the solid state and methods used to foUow solid state reactions. This will consist of various types of thermal analysis (TA), including differentlEd thermal analysis (DTA), thermogravimetric analysis (TGA) and measurements of optical properties. 

Thermogravimetric analysis (TGA) measures changes in weight of a sample being heated. A typical Thermogravimetric analysis (TGA) apparatus is shown in the following diagram ... 

Thermal Properties. The glass transition temperature (Tg) and the decomposition temperature (Td) were measured with a DuPont 910 Differential Scanning Calorimeter (DSC) calibrated with indium. The standard heating rate for all polymers was 10 °C/min. Thermogravimetric analysis (TGA) was performed on a DuPont 951 Thermogravimetric Analyzer at a heating rate of 20 °C/min. 

In this study, we extend the range of inorganic materials produced from polymeric precursors to include copper composites. Soluble complexes between poly(2-vinylpyridine) (P2VPy) and cupric chloride were prepared in a mixed solvent of 95% methanol 5% water. Pyrolysis of the isolated complexes results in the formation of carbonaceous composites of copper. The decomposition mechanism of the complexes was studied by optical, infrared, x-ray photoelectron and pyrolysis mass spectroscopy as well as thermogravimetric analysis and magnetic susceptibility measurements. 

In a study on the thermal and UV ageing of two commercial polyfoxymethy-lene) (POM) samples, one of which was a copolymer (see related study discussed later under Section 4.3, thermogravimetric analysis (TGA)), used in car interior applications, involving both DSC and TGA, isothermal OIT measurements were made at several different temperatures [8]. One conclusion from this study was that "extrapolation of the OIT data from high temperatures (molten state) to ambient temperatures in the solid state does not reflect effective antioxidant performance at room temperature", and thus measurements close to the melting point are not appropriate for reliable lifetime estimations. 

Nitrogen adsorption was performed at -196 °C in a Micromeritics ASAP 2010 volumetric instrument. The samples were outgassed at 80 °C prior to the adsorption measurement until a 3.10 3 Torr static vacuum was reached. The surface area was calculated by the Brunauer-Emmett-Teller (BET) method. Micropore volume and external surface area were evaluated by the alpha-S method using a standard isotherm measured on Aerosil 200 fumed silica [8]. Powder X-ray diffraction (XRD) patterns of samples dried at 80 °C were collected at room temperature on a Broker AXS D-8 diffractometer with Cu Ka radiation. Thermogravimetric analysis was carried out in air flow with heating rate 10 °C min"1 up to 900 °C in a Netzsch TG 209 C thermal balance. SEM micrographs were recorded on a Hitachi S4500 microscope. 

When heated, many solids evolve a gas. For example, most carbonates lose carbon dioxide when heated. Because there is a mass loss, it is possible to determine the extent of the reaction by following the mass of the sample. The technique of thermogravimetric analysis involves heating the sample in a pan surrounded by a furnace. The sample pan is suspended from a microbalance so its mass can be monitored continuously as the temperature is raised (usually as a linear function of time). A recorder provides a graph showing the mass as a function of temperature. From the mass loss, it is often possible to establish the stoichiometry of the reaction. Because the extent of the reaction can be followed, kinetic analysis of the data can be performed. Because mass is the property measured, TGA is useful for... 

For this purpose, all three catalyst supports were initially synthesized by a chemical vapor deposition (CVD) process and thereafter, using a wet impregnation method, loaded with cobalt as the active component for FTS. The as-synthesized Co/nanocatalysts were then characterized by applying electron microscopic analysis as well as temperature-programmed desorption, chemi- and physisorption measurements, thermogravimetric analysis, and inductively coupled plasma... 

Thermogravimetry (TG) is a measure of the thermally induced weight loss of a material as a function of the applied temperature [45]. Thermogravimetric analysis is restricted to studies that involve either a mass gain or loss, and it is most commonly used to study desolvation processes and compound decomposition. The major use of TG analysis is in the quantitative determination of the total volatile content of a solid. When a solid can decompose by means of several... 

Thermogravimetric analysis (TGA) measures cellulose pyrolytic mass loss rates and activation parameters. The technique is relatively simple, straightforward and fast, but it does have disadvantages. One disadvantage is that determination of the kinetic rate constants from TGA data is dependent on the interpretation/analysis technique used. Another disadvantage of TGA is that the rate of mass loss is probably not equivalent to the cellulose pyrolysis rate. 

Dynamic mechanical anlaysis (DMA) measurements were done on a Rheometrics RDS-7700 rheometer in torsional rectangular geometry mode using 60 x 12 x 3 mm samples at 0.05% strain and 1 Hz. Differential scanning calorimetry (DSC), thermomechanical analysis (TMA), and thermogravimetric analysis (TGA) were performed on a Perkin-Elmer 7000 thermal analysis system. 

Apart from the qualitative observations made previously about suitable solvents for study, the subject of solvates has two important bearings on the topics of thermochemistry which form the main body of this review. The first is that measured solubilities relate to the appropriate hydrate in equilibrium with the saturated solution, rather than to the anhydrous halide. Obviously, therefore, any estimate of enthalpy of solution from temperature dependence of solubility will refer to the appropriate solvate. The second area of relevance is to halide-solvent bonding strengths. These may be gauged to some extent from differential thermal analysis (DTA), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC) solvates of "aprotic solvents such as pyridine, tetrahydrofuran, and acetonitrile will give clearer pictures here than solvates of "protic solvents such as water or alcohols. 

---