Anionic polymerization polar solvents

Currently this technology is of minor commercial significance, but stereoregular forms of numerous polyacrylates have been prepared and characterized These include poly(/-butyl acrylate) (138—141), poly(isopropyl acrylate) (142), and poly(isobutyl acrylate) (143,144). Carefully controlled reaction conditions are usually required to obtain polymers with some measurable degree of crystallinity. In nonpolar solvents the anionic polymerization of acrylates generally yields isotactic polymer, whereas in polar solvents syndiotactie polymerization is favored. The physical and chemical properties of the various forms are often quite different. A general review covers these and other aspects of the anionic polymerization of acrylates (145). [Pg.170]

It is possible to polymerize conjugated dienes into polymers with more cu-1,4 segments using ionic initiators. In particular it is found anionic initiators such as lithium or organolithium compounds in non-polar solvents will polymerize isoprene to produce a product which is very similar in structure to natural rubber (c -l,4-polyisoprene). It is thought that the Li ion holds the isoprene molecule in a cisoid conformation through the formation of a rr-complex type of structure. [Pg.78]

Anionic polymerization of vinyl monomers can be effected with a variety of organometaUic compounds alkyllithium compounds are the most useful class (1,33—35). A variety of simple alkyllithium compounds are available commercially. Most simple alkyllithium compounds are soluble in hydrocarbon solvents such as hexane and cyclohexane and they can be prepared by reaction of the corresponding alkyl chlorides with lithium metal. Methyllithium [917-54-4] and phenyllithium [591-51-5] are available in diethyl ether and cyclohexane—ether solutions, respectively, because they are not soluble in hydrocarbon solvents vinyllithium [917-57-7] and allyllithium [3052-45-7] are also insoluble in hydrocarbon solutions and can only be prepared in ether solutions (38,39). Hydrocarbon-soluble alkyllithium initiators are used directiy to initiate polymerization of styrene and diene monomers quantitatively one unique aspect of hthium-based initiators in hydrocarbon solution is that elastomeric polydienes with high 1,4-microstmcture are obtained (1,24,33—37). Certain alkyllithium compounds can be purified by recrystallization (ethyllithium), sublimation (ethyllithium, /-butyUithium [594-19-4] isopropyllithium [2417-93-8] or distillation (j -butyUithium) (40,41). Unfortunately, / -butyUithium is noncrystaUine and too high boiling to be purified by distiUation (38). Since methyllithium and phenyllithium are crystalline soUds which are insoluble in hydrocarbon solution, they can be precipitated into these solutions and then redissolved in appropriate polar solvents (42,43). OrganometaUic compounds of other alkaU metals are insoluble in hydrocarbon solution and possess negligible vapor pressures as expected for salt-like compounds. [Pg.238]

Aromatic radical anions, such as lithium naphthalene or sodium naphthalene, are efficient difunctional initiators (eqs. 6,7) (3,20,64). However, the necessity of using polar solvents for their formation and use limits their utility for diene polymerization, since the unique abiUty of lithium to provide high 1,4-polydiene microstmcture is lost in polar media (1,33,34,57,63,64). Consequentiy, a significant research challenge has been to discover a hydrocarbon-soluble dilithium initiator which would initiate the polymerization of styrene and diene monomers to form monomodal a, CO-dianionic polymers at rates which are faster or comparable to the rates of polymerization, ie, to form narrow molecular weight distribution polymers (61,65,66). [Pg.239]

Commercially, anionic polymerization is limited to three monomers styrene, butadiene, and isoprene [78-79-5], therefore only two useful A—B—A block copolymers, S—B—S and S—I—S, can be produced direcdy. In both cases, the elastomer segments contain double bonds which are reactive and limit the stabhity of the product. To improve stabhity, the polybutadiene mid-segment can be polymerized as a random mixture of two stmctural forms, the 1,4 and 1,2 isomers, by addition of an inert polar material to the polymerization solvent ethers and amines have been suggested for this purpose (46). Upon hydrogenation, these isomers give a copolymer of ethylene and butylene. [Pg.15]

Effects of solvent polarity, counter-anion nucleophilidty, temperature, and monomer concentration on the carbenium ion polymerization chemistry have been extensively studied29,36 38,49. Based on previous knowledge26"29 Me3Al was chosen because with this coinitiator undesired chain transfer to monomer processes are absent. Preliminary experiments showed that Et3Al coinitiator did not yield PaMeSt, possibly because the nuc-leophilicity of the counter-anion Et3AlQe is too high and thus termination by hydrida-tion is faster than propagation36. ... [Pg.31]

Two-shot techniques for acyclic diene metathesis, 435-445 for polyamides, 149-164 for polyimides, 287-300 for polyurethanes, 241-246 for transition metal coupling, 483-490 Anionic deactivation, 360 Anionic polymerization, 149, 174 of lactam, 177-178 Apolar solvents, 90 Aprotic polar solvents, 185, 338 Aprotic solvents, low-temperature condensation in, 302 Aqueous coating formulations, 235 Aqueous polyoxymethylene glycol, depolymerization of, 377 Aqueous systems, 206 Ardel, 20, 22... [Pg.577]

The situation changes dramatically when anionic polymerizations are carried out under reaction conditions such that there is strong coordination among the counter-ion, propagating center, and monomer. Thus, when lithium is the counter-ion and polymerization takes place in a solvent of low polarity, the... [Pg.22]

Anions of the type [M(C2B9H11)2] (M = Fe, Cp, Ni) were also used as noncoordinating anions with [Cp2ZrMe] +, which are active for the polymerization and copolymerization of ethylene and oc-olefins in non-polar solvents such as toluene and hexane [54]. By using the same anions, cationic actinide complexes have also been prepared [110]. [Pg.16]

A bulky methacrylate, triphenylmethyl methacrylate (TrMA), is a unique monomer which gives an almost 100% isotactic polymer in anionic polymerization with n-butyllithium both in nonpolar and polar solvents. Moreover, even free-radical polymerization affords a highly isotactic polymer from this monomer.23 The isotactic specificity of TrMA polymerization is ascribed to the helical formation of the main chain. When TrMA is polymerized in toluene at —78°C... [Pg.161]

As seen, the anionic and cationic polymerizations are analogous differing mainly on the nature of the active species. The stereochemistry associated with anionic polymerization is also similar to that observed with cationic polymerization. For soluble anionic initiators at low temperatures, syndiotactic formation is favored in polar solvents, whereas isotactic formation is favored in nonpolar solvents. Thus, the stereochemistry of anionic polymerizations appears to be largely dependent on the amount of association the growing chain has with the counterion, analogous with the cationic polymerizations. [Pg.147]

A polymer similar to natural hevea rubber is obtained using the anionic polymerization of isoprene under these conditions. In more polar solvents employing sodium and potassium initiators the amount of cA-1,4 units decreases and trans-, A and trans- i,4 units predominate. [Pg.148]

The reaction involves the transfer of an electron from the alkali metal to naphthalene. The radical nature of the anion-radical has been established from electron spin resonance spectroscopy and the carbanion nature by their reaction with carbon dioxide to form the carboxylic acid derivative. The equilibrium in Eq. 5-65 depends on the electron affinity of the hydrocarbon and the donor properties of the solvent. Biphenyl is less useful than naphthalene since its equilibrium is far less toward the anion-radical than for naphthalene. Anthracene is also less useful even though it easily forms the anion-radical. The anthracene anion-radical is too stable to initiate polymerization. Polar solvents are needed to stabilize the anion-radical, primarily via solvation of the cation. Sodium naphthalene is formed quantitatively in tetrahy-drofuran (THF), but dilution with hydrocarbons results in precipitation of sodium and regeneration of naphthalene. For the less electropositive alkaline-earth metals, an even more polar solent than THF [e.g., hexamethylphosphoramide (HMPA)] is needed. [Pg.414]

The propagation rate constant and the polymerization rate for anionic polymerization are dramatically affected by the nature of both the solvent and the counterion. Thus the data in Table 5-10 show the pronounced effect of solvent in the polymerization of styrene by sodium naphthalene (3 x 1CT3 M) at 25°C. The apparent propagation rate constant is increased by 2 and 3 orders of magnitude in tetrahydrofuran and 1,2-dimethoxyethane, respectively, compared to the rate constants in benzene and dioxane. The polymerization is much faster in the more polar solvents. That the dielectric constant is not a quantitative measure of solvating power is shown by the higher rate in 1,2-dimethoxyethane (DME) compared to tetrahydrofuran (THF). The faster rate in DME may be due to a specific solvation effect arising from the presence of two ether functions in the same molecule. [Pg.423]

The need for solvation in anionic polymerization manifests itself in some instances by other deviations from the normal reaction rate expressions. Thus the butyllithium polymerization of methyl methacrylate in toluene at — 60°C shows a second-order dependence of Rp on monomer concentration [L Abbe and Smets, 1967]. In the nonpolar toulene, monomer is involved in solvating the propagating species [Busson and Van Beylen, 1978]. When polymerization is carried out in the mixed solvent dioxane-toluene (a more polar solvent than toluene), the normal first-order dependence of Rp on [M] is observed. The lithium diethylamide, LiN(C2H5)2, polymerization of styrene at 25°C in THF-benzene similarly shows an increased order of dependence of Rp on [M] as the amount of tetrahydrofuran is decreased [Hurley and Tait, 1976]. [Pg.435]

Copolymerizations of nonpolar monomers with polar monomers such as methyl methacrylate and acrylonitrile are especially comphcated. The effects of solvent and counterion may be unimportant compared to the side reactions characteristic of anionic polymerization of polar monomers (Sec. 5-3b-4). In addition, copolymerization is often hindered by the very low tendency of one of the cross-propagation reactions. For example, polystyryl anions easily add methyl methacrylate but there is little tendency for poly(methyl methacrylate) anions to add styrene. Many reports of styrene-methyl methacrylate (and similar comonomer pairs) copolymerizations are not copolymerizations in the sense discussed in this chapter. [Pg.511]

The anionic polymerization of 1,3-dienes yields different polymer structures depending on whether the propagating center is free or coordinated to a counterion [Morton, 1983 Quirk, 2002 Senyek, 1987 Tate and Bethea, 1985 Van Beylen et al., 1988 Young et al., 1984] Table 8-9 shows typical data for 1,3-butadiene and isoprene polymerizations. Polymerization of 1,3-butadiene in polar solvents, proceeding via the free anion and/or solvent-separated ion pair, favors 1,2-polymerization over 1,4-polymerization. The anionic center at carbon 2 is not extensively delocalized onto carbon 4 since the double bond is not a strong electron acceptor. The same trend is seen for isoprene, except that 3,4-polymerization occurs instead of 1,2-polymerization. The 3,4-double bond is sterically more accessible and has a lower electron density relative to the 1,2-double bond. Polymerization in nonpolar solvents takes place with an increased tendency toward 1,4-polymerization. The effect is most pronounced with... [Pg.691]


See other pages where Anionic polymerization polar solvents is mentioned: [Pg.170]    [Pg.269]    [Pg.170]    [Pg.298]    [Pg.4]    [Pg.4]    [Pg.87]    [Pg.98]    [Pg.152]    [Pg.164]    [Pg.199]    [Pg.308]    [Pg.270]    [Pg.17]    [Pg.22]    [Pg.205]    [Pg.1457]    [Pg.150]    [Pg.493]    [Pg.48]    [Pg.50]    [Pg.147]    [Pg.165]    [Pg.136]    [Pg.115]    [Pg.289]    [Pg.374]    [Pg.412]    [Pg.419]    [Pg.419]    [Pg.430]    [Pg.448]   


SEARCH



Acrylate anionic polymerization polar solvents

Polar polymerization

Polar solvents

Polar solvents, anionic polymerization methacrylates/acrylates

Polar solvents, polymerization

Polarity, solvent

Polarity/polarization solvent

Polarization solvent

Polarization, anion

Polymeric solvents

Polymerization, anionic polar solvent effects

Polymerizing solvent

Solvent polar solvents

Solvents polymerization

© 2024 chempedia.info