Metal infrared spectroscopy

Studies to determine the nature of intermediate species have been made on a variety of transition metals, and especially on Pt, with emphasis on the Pt(lll) surface. Techniques such as TPD (temperature-programmed desorption), SIMS, NEXAFS (see Table VIII-1) and RAIRS (reflection absorption infrared spectroscopy) have been used, as well as all kinds of isotopic labeling (see Refs. 286 and 289). On Pt(III) the surface is covered with C2H3, ethylidyne, tightly bound to a three-fold hollow site, see Fig. XVIII-25, and Ref. 290. A current mechanism is that of the figure, in which ethylidyne acts as a kind of surface catalyst, allowing surface H atoms to add to a second, perhaps physically adsorbed layer of ethylene this is, in effect, a kind of Eley-Rideal mechanism. 

Whereas ATR spectroscopy is most commonly applied in obtaining infrared absorption spectra of opaque materials, reflection-absorption infrared spectroscopy (RAIRS) is usually used to obtain the absorption spectrum of a thin layer of material adsorbed on an opaque metal surface. An example would be carbon monoxide adsorbed on copper. The metal surface may be either in the form of a film or, of greaf imporfance in fhe sfudy of cafalysfs, one of fhe parficular crysfal faces of fhe mefal. 

Transmission Fourier Transform Infrared Spectroscopy. The most straightforward method for the acquisition of in spectra of surface layers is standard transmission spectroscopy (35,36). This approach can only be used for samples which are partially in transparent or which can be diluted with an in transparent medium such as KBr and pressed into a transmissive pellet. The extent to which the in spectral region (typically ca 600 4000 cm ) is available for study depends on the in absorption characteristics of the soHd support material. Transmission ftir spectroscopy is most often used to study surface species on metal oxides. These soHds leave reasonably large spectral windows within which the spectral behavior of the surface species can be viewed. 

Polyester composition can be determined by hydrolytic depolymerization followed by gas chromatography (28) to analyze for monomers, comonomers, oligomers, and other components including side-reaction products (ie, DEG, vinyl groups, aldehydes), plasticizers, and finishes. Mass spectroscopy and infrared spectroscopy can provide valuable composition information, including end group analysis (47,101,102). X-ray fluorescence is commonly used to determine metals content of polymers, from sources including catalysts, delusterants, or tracer materials added for fiber identification purposes (28,102,103). 

Impurities in bromine may be deterrnined quantitatively (54). Weighing the residue after evaporation of a bromine sample yields the total nonvolatile matter. After removing the bromine, chloride ion may be deterrnined by titration with mercuric nitrate, and iodide ion by titration with thiosulfate water and organic compounds may be detected by infrared spectroscopy sulfur may be deterrnined turbidimetricaHy as barium sulfate and heavy metals may be deterrnined colorimetricaHy after conversion to sulfides. 

Surface analysis has made enormous contributions to the field of adhesion science. It enabled investigators to probe fundamental aspects of adhesion such as the composition of anodic oxides on metals, the surface composition of polymers that have been pretreated by etching, the nature of reactions occurring at the interface between a primer and a substrate or between a primer and an adhesive, and the orientation of molecules adsorbed onto substrates. Surface analysis has also enabled adhesion scientists to determine the mechanisms responsible for failure of adhesive bonds, especially after exposure to aggressive environments. The objective of this chapter is to review the principals of surface analysis techniques including attenuated total reflection (ATR) and reflection-absorption (RAIR) infrared spectroscopy. X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), and secondary ion mass spectrometry (SIMS) and to present examples of the application of each technique to important problems in adhesion science. 

Deprotonation of H2O2 yields OOH , and hydroperoxides of the alkali metals are known in solution. Liquid ammonia can also effect deprotonation and NH4OOH is a white solid, mp 25° infrared spectroscopy shows the presence of NH4+ and OOH ions in the solid phase but the melt appears to contain only the H-bonded species NH3 and H202. " Double deprotonation yields the peroxide ion 02 , and this is a standard route to transition metal peroxides. 

Recent developments in the mechanisms of corrosion inhibition have been discussed in reviews dealing with acid solutions " and neutral solu-tions - . Novel and improved experimental techniques, e.g. surface enhanced Raman spectroscopy , infrared spectroscopy. Auger electron spectroscopyX-ray photoelectron spectroscopyand a.c. impedance analysis have been used to study the adsorption, interaction and reaction of inhibitors at metal surfaces. 

The participation of siloxane groups in the reaction increases with the temperature of dehydration of Si02 and quantity of organometallic compound introduced in the reaction. According to the data of infrared spectroscopy (139), the allyl ligands formed in the surface organometallic complexes of Ni and Cr keep the 7r-allyl character of the metal-ligand bond. 

Work has also been conducted that involved the investigation, via infrared spectroscopy, of matrix-isolated, plutonium oxides (40), with the appropriate precautions being taken because of the toxicity of plutonium and its compounds. A sputtering technique was used to vaporize the metal. The IR spectra of PuO and PUO2 in both Ar and Kr matrices were identified, with the observed frequencies for the latter (794.25 and 786.80 cm", respectively) assigned to the stretchingmode of Pu 02. Normal-coordinate analysis of the PUO2 isotopomers, Pu 02, Pu 02, and Pu 0 0 in Ar showed that the molecule is linear. The PuO molecule was observed in multiple sites in Ar matrices, but not in Kr, with Pu 0 at 822.28 cm" in the most stable, Ar site, and at 817.27 cm" in Kr. No evidence for PuOa was observed. 

A. A. Davydov, Infrared spectroscopy of adsorbed species on the surfaces of transition metal oxides, Wiley, Chichester, 1990. 

Ellis Wilson (1991, 1992) examined cement formation between a large number of metal oxides and PVPA solutions. They concluded that setting behaviour was to be explained mainly in terms of basicity and reactivity, noting that cements were formed by reactive basic or amphoteric oxides and not by inert or acidic ones (Table 8.3). Using infrared spectroscopy they found that, with one exception, cement formation was associated with salt formation the phosphonic add band at 990 cm diminished as the phosphonate band at 1060 cm" developed. The anomalous result was that the acidic boric oxide formed a cement which, however, was soluble in water. This was the result, not of an add-base readion, but of complex formation. Infrared spectroscopy showed a shift in the P=0 band from 1160 cm" to 1130 cm", indicative of an interaction of the type... 

In situ infrared spectroscopy allows one to obtain stracture-specific information at the electrode-solution interface. It is particularly useful in the study of electrocat-alytic reactions, molecular adsorption, and the adsorption of ions at metal surfaces. 

Interfacial water molecules play important roles in many physical, chemical and biological processes. A molecular-level understanding of the structural arrangement of water molecules at electrode/electrolyte solution interfaces is one of the most important issues in electrochemistry. The presence of oriented water molecules, induced by interactions between water dipoles and electrode and by the strong electric field within the double layer has been proposed [39-41]. It has also been proposed that water molecules are present at electrode surfaces in the form of clusters [42, 43]. Despite the numerous studies on the structure of water at metal electrode surfaces using various techniques such as surface enhanced Raman spectroscopy [44, 45], surface infrared spectroscopy [46, 47[, surface enhanced infrared spectroscopy [7, 8] and X-ray diffraction [48, 49[, the exact nature of the structure of water at an electrode/solution interface is still not fully understood. 

Stamenkovic V, Arenz M, Ross PN, Markovic NM. 2004. Temperature-induced deposition method for anchoring metallic nanoparticles onto reflective substrates for in situ electrochemical infrared spectroscopy. J Phys Chem B 108 17915-17920. 

Chang SC, Roth JD, Ho YH, Weaver MJ. 1990. New developments in electrochemical infrared-spectroscopy— Adlayer structures of carbon-monoxide on monocrystalline metal-electrodes. J Electron Spectrosc Relat Phenom 54 1185-1203. 

---