By oxidation with permanganate it forms pinonic acid, C,oH,<503, a monobasic acid derived from cyclobutane. With strong sulphuric acid it forms a mixture of limonene, dipentene, terpinolene, terpinene, camphene and p-cymene. Hydrogen chloride reacts with turpentine oil to give CioHijCl, bomyl chloride, artificial camphor . 

A carbon atom in a ring can be a chirality center if it bears two different sub stituents and the path traced around the ring from that carbon m one direction is differ ent from that traced m the other The carbon atom that bears the methyl group m 1 2 epoxypropane for example is a chirality center The sequence of groups is O—CH2 as one proceeds clockwise around the ring from that atom but is CH2—O m the counter clockwise direction Similarly C 4 is a chirality center m limonene... 

Loss of a proton from the tertiary carbocation formed m this step gives limonene an abundant natural product found m many citrus fruits Capture of the carbocation by water gives a terpmeol also a known natural product... 

In a chromatographic analysis of lemon oil a peak for limonene has a retention time of 8.36 min with a baseline width of 0.96 min. y-Terpinene elutes at 9.54 min, with a baseline width of 0.64 min. What is the resolution between the two peaks ... 

Two experiments are described in this paper. In the first experiment students determine the %w/w orange oil in a prepared sample by analyzing for d-limonene using anisole as an internal standard. Separations are accomplished using... 

In this pyrolysis, sub atmospheric partial pressures are achieved by employing a diluent such as steam. Because of the corrosive nature of the acids (HE and HCl) formed, the reactor design should include a platinum-lined tubular reactor made of nickel to allow atmospheric pressure reactions to be mn in the presence of a diluent. Because the pyrolysate contains numerous by-products that adversely affect polymerization, the TFE must be purified. Refinement of TFE is an extremely complex process, which contributes to the high cost of the monomer. Inhibitors are added to the purified monomer to avoid polymerization during storage terpenes such as t7-limonene and terpene B are effective (10). 

Among chiral dialkylboranes, diisopinocampheylborane (8) is the most important and best-studied asymmetric hydroborating agent. It is obtained in both enantiomeric forms from naturally occurring a-pinene. Several procedures for its synthesis have been developed (151—153). The most convenient one, providing product of essentially 100% ee, involves the hydroboration of a-pinene with borane—dimethyl sulfide in tetrahydrofuran (154). Other chiral dialkylboranes derived from terpenes, eg, 2- and 3-carene (155), limonene (156), and longifolene (157,158), can also be prepared by controlled hydroboration. A more tedious approach to chiral dialkylboranes is based on the resolution of racemates. /n j -2,5-Dimethylborolane, which shows excellent enantioselectivity in the hydroboration of all principal classes of prochiral alkenes except 1,1-disubstituted terminal double bonds, has been... 

Terpene-based hydrocarbon resins are typically based on natural products such as a-pinene, P-pinene, and ti-limonene [5989-27-5] which are obtained from the wood and citms industries, respectively. These resins, which were originally the preferred tackifiers for natural mbber appHcations, possess similar properties to aHphatic petroleum resins, which were developed later. Terpene-based resins have been available since the mid-1930s and are primarily used in the adhesives industry. 

Terpenes, specifically monoterpenes, are naturally occurring monomers that are usually obtained as by-products of the paper and citms industries. Monoterpenes that are typically employed in hydrocarbon resins are shown in Figure 2. Optically active tf-limonene is obtained from various natural oils, particularly citms oils (81). a and P-pinenes are obtained from sulfate turpentine produced in the kraft (sulfate) pulping process. Southeastern U.S. sulfate turpentine contains approximately 60—70 wt % a-pinene and 20—25 wt % P-pinene (see Terpenoids). Dipentene, which is a complex mixture of if,/-Hmonene, a- and P-pheUandrene, a- and y-terpinene, and terpinolene, is also obtained from the processing of sulfate Hquor (82). 

Boron tritiuoride etherate— -hexanol complexes have successfully been used to polymerize P-pinene, as well as dipentene, to yield resins with softening points >70° C (82). Limonene or dipentene sulfate has been polymerized with aluminum chloride in a mixed toluene/high boiling aUphatic naphtha to give high yields of light colored resins (96). For the polymerization of dipentene or limonene, 4—8 wt % of AlCl has been used. Polymerization of P-pinene typically requires lower levels of catalyst relative to limonene or dipentene. 

Heteroatom functionalized terpene resins are also utilized in hot melt adhesive and ink appHcations. Diels-Alder reaction of terpenic dienes or trienes with acrylates, methacrylates, or other a, P-unsaturated esters of polyhydric alcohols has been shown to yield resins with superior pressure sensitive adhesive properties relative to petroleum and unmodified polyterpene resins (107). Limonene—phenol resins, produced by the BF etherate-catalyzed condensation of 1.4—2.0 moles of limonene with 1.0 mole of phenol have been shown to impart improved tack, elongation, and tensile strength to ethylene—vinyl acetate and ethylene—methyl acrylate-based hot melt adhesive systems (108). Terpene polyol ethers have been shown to be particularly effective tackifiers in pressure sensitive adhesive appHcations (109). 

---