Molecular weight cationic chain polymerization

The theoretical molecular weight distributions for cationic chain polymerizations are the same as those described in Sec. 3-11 for radical chain polymerizations terminating by reactions in which each propagating chain is converted to one dead polymer molecule, that is, not including the formation of a dead polymer molecule by bimolecular coupling of two propagating chains. Equations 2-86 through 2-89, 2-27, 2-96, and 2-97 withp defined by Eq. 3-185... 

The theoretical molecular weight distributions for cationic chain polymerizations (see Problem 8.30) are the same as those described in Chapter 6 for radical chain polymerizations terminating by disproportionation, i.e., where each propagating chain yields one dead polymer molecule. The poly-dispersity index (PDI = DP /DPn) has a limit of 2. Many cationic polymerizations proceed with rapid initiation, which narrows the molecular weight distribution (MDI). In the extreme case where termination and transfer reactions are very slow or nonexistent, this would yield a very narrow MDI with PDI close to one (p. 681). 

The theoretical molecular weight distributions for cationic chain polymerizations (see Problem 8.25) are the same as those described in Chapter 6 for radical chain polymerizations terminating by disproportionation, i.e., where each propagating... 

High-molecular-weight polyisobutylene (PIB) is produced by cationic chain polymerization in methyl chloride solution at — 70°C using aluminum chloride as the catalyst. Such polymers are currently available from Esso (Vistanex) and BASF (Oppanol). 

The addition polymerization of a vinyl monomer CH2=CHX involves three distinctly different steps. First, the reactive center must be initiated by a suitable reaction to produce a free radical or an anion or cation reaction site. Next, this reactive entity adds consecutive monomer units to propagate the polymer chain. Finally, the active site is capped off, terminating the polymer formation. If one assumes that the polymer produced is truly a high molecular weight substance, the lack of uniformity at the two ends of the chain—arising in one case from the initiation, and in the other from the termination-can be neglected. Accordingly, the overall reaction can be written... 

Butyl mbber, a copolymer of isobutjiene with 0.5—2.5% isoprene to make vulcanization possible, is the most important commercial polymer made by cationic polymerization (see Elastomers, synthetic-butyl rubber). The polymerization is initiated by water in conjunction with AlCl and carried out at low temperature (—90 to —100° C) to prevent chain transfer that limits the molecular weight (1). Another important commercial appHcation of cationic polymerization is the manufacture of polybutenes, low molecular weight copolymers of isobutylene and a smaller amount of other butenes (1) used in adhesives, sealants, lubricants, viscosity improvers, etc. 

Acyclic C5. The C5 petroleum feed stream consists mainly of isoprene which is used to produce rubber. In a separate stream the linear C5 diolefin, piperylene (trans and cis), is isolated. Piperylene is the primary monomer in what are commonly termed simply C5 resins. Small amounts of other monomers such as isoprene and methyl-2-butene are also present. The latter serves as a chain terminator added to control molecular weight. Polymerization is cationic using Friedel-Crafts chemistry. Because most of the monomers are diolefins, residual backbone unsaturation is present, which can lead to some crosslinking and cyclization. Primarily, however, these are linear acyclic materials. Acyclic C5 resins are sometimes referred to as synthetic polyterpenes , because of their similar polarity. However, the cyclic structures within polyterpenes provide them with better solvency power and thus a broader range of compatibility than acyclic C5s. 

Radical polymerization of diallylamine derivatives produce water-soluble polymers of low molecular weight [22,55-57]. In order to increase the molecular weight, acrylamide has been copolymerized with these diallylamine derivatives to produce cationic polymers with variable charge density depending on the content of the structural units of pyrrolidinium rings and acrylamide in polymeric chains [22,55,58-61]. 

In general, the activation energies for both cationic and anionic polymerization are small. For this reason, low-temperature conditions are normally used to reduce side reactions. Low temperatures also minimize chain transfer reactions. These reactions produce low-molecular weight polymers by disproportionation of the propagating polymer ... 

Interest in anionic polymerizations arises in part from the reactivity of the living carbanionic sites4 7) Access can be provided to polymers with a functional chain end. Such species are difficult to obtain by other methods. Polycondensations yield ro-functional polymers but they provide neither accurate molecular weight control nor low polydispersity. Recently Kennedy51) developed the inifer technique which is based upon selective transfer to fit vinylic polymers obtained cationically with functions at chain end. Also some cationic ring-opening polymerizations52) without spontaneous termination can yield re-functional polymers upon induced deactivation. Anionic polymerization remains however the most versatile and widely used method to synthesize tailor made re-functional macromolecules. 

A special case of the internal stabilization of a cationic chain end is the intramolecular solvation of the cationic centre. This can proceed with the assistance of suitable substituents at the polymeric backbone which possess donor ability (for instance methoxy groups 109)). This stabilization can lead to an increase in molecular weight and to a decrease in non-uniformity of the products. The two effects named above were obtained during the transition from vinyl ethers U0) to the cis-l,2-dimethoxy ethylene (DME)1U). An intramolecular stabilization is discussed for the case of vinyl ether polymerization by assuming a six-membered cyclic oxonium ion 2) as well as for the case of cationic polymerization of oxygen heterocycles112). Contrary to normal vinyl ethers, DME can form 5- and 7-membe red cyclic intermediates beside 6-membered ringsIl2). 

Analogous principles should apply to ionically propagated polymerizations. The terminus of the growing chain, whether cation or anion, can be expected to exhibit preferential addition to one or the other carbon of the vinyl group. Poly isobutylene, normally prepared by cationic polymerization, possesses the head-to-tail structure, as already mentioned. Polystyrenes prepared by cationic or anionic polymerization are not noticeably different from free-radical-poly-merized products of the same molecular weights, which fact indicates a similar chain structure irrespective of the method of synthesis. In the polymerization of 1,3-dienes, however, the structure and arrangement of the units depends markedly on the chain-propagating mechanism (see Sec. 2b). 

---