1,3-Butadiene anionic polymerization

Key words FT-NIR, kinetics, living polymerization, isobutylene, ethylene oxide, butadiene, anionic polymerization, cationic polymerization... 

The use of alkaU metals for anionic polymerization of diene monomers is primarily of historical interest. A patent disclosure issued in 1911 (16) detailed the use of metallic sodium to polymerize isoprene and other dienes. Independentiy and simultaneously, the use of sodium metal to polymerize butadiene, isoprene, and 2,3-dimethyl-l,3-butadiene was described (17). Interest in alkaU metal-initiated polymerization of 1,3-dienes culminated in the discovery (18) at Firestone Tire and Rubber Co. that polymerization of neat isoprene with lithium dispersion produced high i7j -l,4-polyisoprene, similar in stmcture and properties to Hevea natural mbber (see ELASTOLffiRS,SYNTHETic-POLYisoPRENE Rubber, natural). 

Other Organolithium Compounds. Organoddithium compounds have utiHty in anionic polymerization of butadiene and styrene. The lithium chain ends can then be converted to useflil functional groups, eg, carboxyl, hydroxyl, etc (139). Lewis bases are requHed for solubdity in hydrocarbon solvents. 

Anionic polymerization, if carried out properly, can be truly a living polymerization (160). Addition of a second monomer to polystyryl anion results in the formation of a block polymer with no detectable free PS. This technique is of considerable importance in the commercial preparation of styrene—butadiene block copolymers, which are used either alone or blended with PS as thermoplastics. 

Commercially, anionic polymerization is limited to three monomers styrene, butadiene, and isoprene [78-79-5], therefore only two useful A—B—A block copolymers, S—B—S and S—I—S, can be produced direcdy. In both cases, the elastomer segments contain double bonds which are reactive and limit the stabhity of the product. To improve stabhity, the polybutadiene mid-segment can be polymerized as a random mixture of two stmctural forms, the 1,4 and 1,2 isomers, by addition of an inert polar material to the polymerization solvent ethers and amines have been suggested for this purpose (46). Upon hydrogenation, these isomers give a copolymer of ethylene and butylene. 

Block copolymer chemistry and architecture is well described in polymer textbooks and monographs [40]. The block copolymers of PSA interest consist of anionically polymerized styrene-isoprene or styrene-butadiene diblocks usually terminating with a second styrene block to form an SIS or SBS triblock, or terminating at a central nucleus to form a radial or star polymer (SI) . Representative structures are shown in Fig. 5. For most PSA formulations the softer SIS is preferred over SBS. In many respects, SIS may be treated as a thermoplastic, thermoprocessible natural rubber with a somewhat higher modulus due to filler effect of the polystyrene fraction. Two longer reviews [41,42] of styrenic block copolymer PSAs have been published. 

Anionic polymerization is better for vinyl monomers with electron withdrawing groups that stabilize the intermediates. Typical monomers best polymerized by anionic initiators include acrylonitrile, styrene, and butadiene. As with cationic polymerization, a counter ion is present with the propagating chain. The propagation and the termination steps are similar to cationic polymerization. 

Polystyrene homopolymer produced by free radical initiators is highly amorphous (Tg = 100°C). The general purpose rubber (SBR), a block copolymer with 75% butadiene, is produced by anionic polymerization. 

A pilot scale plant, incorporating a three litre continuous stirred tank reactor, was used for an investigation into the n-butyl lithium initiated, anionic polymerization of butadiene in n-hexane solvent. The rig was capable of being operated at elevated temperatures and pressures, comparable with industrial operating conditions. 

Linear triblock copolymers of the type styrene-butadiene-styrene (SBS) and styrene-isoprene-styrene (SIS) are produced commercially by anionic polymerization through sequential addition of monomers in the reaction chamber [10] as shown below ... 

Ionic Polymerization. Ionic polymerizations, especially cationic polymerizations, are not as well understood as radical polymerizations because of experimental difficulties involved in their study. The nature of the reaction media is not always clear since heterogeneous initiators are often involved. Further, it is much more difficult to obtain reproducible data because ionic polymerizations proceed at very fast rates and are highly sensitive to small concentrations of impurities and adventitious materials. Butyl rubber, a polymer of isobutene and isoprene, is produced commercially by cationic polymerization. Anionic polymerization is used for various polymerizations of 1,3-butadiene and isoprene. 

Anionic polymerization can be initiated by a variety of anionic sources such as metal alkoxides, aryls, and alkyls. Alkyllithium initiators are among the most useful, being employed commercially in the polymerization of 1,3-butadiene and isoprene, due to their solubility in hydrocarbon solvents. Initiation involves addition of alkyl anion to monomer... 

Polymer Synthesis and Characterization. This topic has been extensively discussed in preceeding papers.(2,23,24) However, we will briefly outline the preparative route. The block copolymers were synthesized via the sequential addition method. "Living" anionic polymerization of butadiene, followed by isoprene and more butadiene, was conducted using sec-butyl lithium as the initiator in hydrocarbon solvents under high vacuum. Under these conditions, the mode of addition of butadiene is predominantly 1,4, with between 5-8 mole percent of 1,2 structure.(18) Exhaustive hydrogenation of polymers were carried out in the presence of p-toluenesulfonylhydrazide (19,25) in refluxing xylene. The relative block composition of the polymers were determined via NMR. 

The synthesis and characterization of a series of dendrigraft polymers based on polybutadiene segments was reported by Hempenius et al. [15], The synthesis begins with a linear-poly(butadiene) (PB) core obtained by the sec-butyllithium-initiated anionic polymerization of 1,3-butadiene in n-hexane, to give a microstructure containing approximately 6% 1,2-units (Scheme 3). The pendant vinyl moities are converted into electrophilic grafting sites by hydrosilylation with... 

The fairly broad most probable distribution for the rays may be considered as an undesirable imperfection of regular stars. Corresponding measurements with much narrower arm length distributions were made later, mainly by the research groups of Fetters [20, 30, 31] and Roovers [25, 26] which were obtained by living anionic polymerization of styrene, isoprene and butadiene respective-... 

Hence measurements have been made on unsubstituted allyl alkali-metal compounds, and also on neopentylallyl (I, 5,5-dimethylhexen-2-) and neopentylmethallyl (II, 2,5,5-trimethyl-hexen-2-) alkali-metal compounds which are models of the polymerizing chain end in the anionic polymerization of butadiene and isoprene respectively. 

Over 5.5 billion pounds of synthetic rubber is produced annually in the United States. The principle elastomer is the copolymer of butadiene (75%) and styrene (25) (SBR) produced at an annual rate of over 1 million tons by the emulsion polymerization of butadiene and styrene. The copolymer of butadiene and acrylonitrile (Buna-H, NBR) is also produced by the emulsion process at an annual rate of about 200 million pounds. Likewise, neoprene is produced by the emulsion polymerization of chloroprene at an annual rate of over 125,000 t. Butyl rubber is produced by the low-temperature cationic copolymerization of isobutylene (90%) and isoprene (10%) at an annual rate of about 150,000 t. Polybutadiene, polyisoprene, and EPDM are produced by the anionic polymerization of about 600,000, 100,000, and 350,000 t, respectively. Many other elastomers are also produced. 

Auguste S, Edwards HGM, Johnson AF et al. (1996) Anionic polymerization of styrene and butadiene initiated by n-butyllithium in ethylbenzene determination of the propagation rate constants using Raman spectroscopy and gel permeation chromatography. Polymer 37 3665-3673... 

The annual worlwide production of triblock thermoplastic elastomers, clear impact-resistant polystyrene, and other styrene-diene products produced by anionic polymerization exceeds a couple of billion pounds. (Commercial utilization of anionic polymerization also includes the polymerization of 1,3-butadiene alone.)... 

Penultimate effects have been observed for many comonomer pairs. Among these are the radical copolymerizations of styrene-fumaronitrile, styrene-diethyl fumarate, ethyl methacrylate-styrene, methyl methacrylate l-vinylpyridine, methyl acrylate-1,3-butadiene, methyl methacrylate-methyl acrylate, styrene-dimethyl itaconate, hexafluoroisobutylene-vinyl acetate, 2,4-dicyano-l-butene-isoprene, and other comonomer pairs [Barb, 1953 Brown and Fujimori, 1987 Buback et al., 2001 Burke et al., 1994a,b, 1995 Cowie et al., 1990 Davis et al., 1990 Fordyce and Ham, 1951 Fukuda et al., 2002 Guyot and Guillot, 1967 Hecht and Ojha, 1969 Hill et al., 1982, 1985 Ma et al., 2001 Motoc et al., 1978 Natansohn et al., 1978 Prementine and Tirrell, 1987 Rounsefell and Pittman, 1979 Van Der Meer et al., 1979 Wu et al., 1990 Yee et al., 2001 Zetterlund et al., 2002]. Although ionic copolymerizations have not been as extensively studied, penultimate effects have been found in some cases. Thus in the anionic polymerization of styrene t-vinylpyri-dine, 4-vinylpyridine adds faster to chains ending in 4-vinylpyridine if the penultimate unit is styrene [Lee et al., 1963]. 

Most polystyrene products are not homopolystyrene since the latter is relatively brittle with low impact and solvent resistance (Secs. 3-14b, 6-la). Various combinations of copolymerization and blending are used to improve the properties of polystyrene [Moore, 1989]. Copolymerization of styrene with 1,3-butadiene imparts sufficient flexibility to yield elastomeric products [styrene-1,3-butadiene rubbers (SBR)]. Most SBR rubbers (trade names Buna, GR-S, Philprene) are about 25% styrene-75% 1,3-butadiene copolymer produced by emulsion polymerization some are produced by anionic polymerization. About 2 billion pounds per year are produced in the United States. SBR is similar to natural rubber in tensile strength, has somewhat better ozone resistance and weatherability but has poorer resilience and greater heat buildup. SBR can be blended with oil (referred to as oil-extended SBR) to lower raw material costs without excessive loss of physical properties. SBR is also blended with other polymers to combine properties. The major use for SBR is in tires. Other uses include belting, hose, molded and extruded goods, flooring, shoe soles, coated fabrics, and electrical insulation. 

The anionic polymerization of 1,3-dienes yields different polymer structures depending on whether the propagating center is free or coordinated to a counterion [Morton, 1983 Quirk, 2002 Senyek, 1987 Tate and Bethea, 1985 Van Beylen et al., 1988 Young et al., 1984] Table 8-9 shows typical data for 1,3-butadiene and isoprene polymerizations. Polymerization of 1,3-butadiene in polar solvents, proceeding via the free anion and/or solvent-separated ion pair, favors 1,2-polymerization over 1,4-polymerization. The anionic center at carbon 2 is not extensively delocalized onto carbon 4 since the double bond is not a strong electron acceptor. The same trend is seen for isoprene, except that 3,4-polymerization occurs instead of 1,2-polymerization. The 3,4-double bond is sterically more accessible and has a lower electron density relative to the 1,2-double bond. Polymerization in nonpolar solvents takes place with an increased tendency toward 1,4-polymerization. The effect is most pronounced with... 

What reaction conditions determine the relative amounts of 1,2-, cis 1,4-, and trans 1,4-polymerization in the radical and anionic polymerizations of 1,3-butadiene Indicate... 

---