Adhesive, resorcinol-formaldehyde

NF 176-117 1984 Water based adhesives. Resorcinol formaldehyde, resorcinol-phenol formaldehyde. Conventional determination of gel setting time at 23 degrees C. 

Both melamine—formaldehyde (MF) and resorcinol—formaldehyde (RF) foUowed the eadier developments of phenol—, and urea—formaldehyde. Melamine has a more complex stmcture than urea and is also more expensive. Melamine-base resins requite heat to cure, produce colorless gluelines, and are much more water-resistant than urea resins but stiU are not quite waterproof. Because of melamine s similarity to urea, it is often used in fairly small amounts with urea to produce melamine—urea—formaldehyde (MUF) resins. Thus, the improved characteristics of melamine can be combined with the economy of urea to provide an improved adhesive at a moderate increase in cost. The improvement is roughly proportional to the amount of melamine used the range of addition may be from 5 to 35%, with 5—10% most common. 

Resorcinol is to phenol as melamine is to urea. Resorcinol—formaldehyde (RF) is very expensive, produces dark and waterproof gluelines, but will cure at room temperature. As with melamine and urea, resorcinol is often combined with phenol to produce phenol—resorcinol—formaldehyde (PRF) adhesives, thus producing an exceUent adhesive with some of the economy of phenol. These adhesives are the mainstay of the laminated timber industry which generally requites a room-temperature cure with durable, waterproof gluelines. 

For exterior appHcations, where water exposure is expected, phenol—formaldehyde (PF) or phenol—resorcinol—formaldehyde (PRF) adhesives are used. Only small quantities of this type of hardwood plywood are made, primarily for marine use. 

Tire Cord. Melamine resins are also used to improve the adhesion of mbber to reinforcing cord in tires. Textile cord is normally coated with a latex dip solution composed of a vinylpyridine—styrene—butadiene latex mbber containing resorcinol—formaldehyde resin.. The dip coat is cured prior to use. The dip coat improves the adhesion of the textile cord to mbber. Further improvement in adhesion is provided by adding resorcinol and hexa(methoxymethyl) melamine [3089-11 -0] (HMMM) to the mbber compound which is in contact with the textile cord. The HMMM resin and resorcinol cross-link during mbber vulcanization and cure to form an interpenetrating polymer within the mbber matrix which strengthens or reinforces the mbber and increases adhesion to the textile cord. Brass-coated steel cord is also widely used in tires for reinforcement. Steel belts and bead wire are common apphcations. Again, HMMM resins and resorcinol [108-46-3] are used in the mbber compound which is in contact with the steel cord to reinforce the mbber and increase the adhesion of the mbber to the steel cord. This use of melamine resins is described in the patent Hterature (49). 

Nitrile rubber is compatible with phenol-formaldehyde resins, resorcinol-formaldehyde resins, vinyl chloride resins, alkyd resins, coumarone-indene resins, chlorinated rubber, epoxies and other resins, forming compositions which can be cured providing excellent adhesives of high strength, high oil resistance and high resilience. On the other hand, NBR adhesives are compatible with polar adherends such as fibres, textiles, paper and wood. Specific formulations of NBR adhesives can be found in [12]. 

Resorcinol-formaldehyde (RF) and phenol-resorcinol-formaldehyde (PRF) coldsetting adhesives are used primarily in the manufacture of structural, exterior-... 

The condensation reaction of resorcinol with formaldehyde, on an equal molar basis and under identical conditions, also proceeds at a rate which is approximately 10 to 15 times faster than that of the equivalent phenol-formaldehyde system [16-18,123]. The high reactivity of the resorcinol-formaldehyde system renders it impossible to have these adhesives in resol form. Therefore, only resorcinol-formaldehyde novolaks, i.e. resins not containing methylol groups can be produced. All the resorcinol nuclei are linked together through methylene... 

In the manufacture of pure resorcinol resins, the reaction can be violently exothermic unless controlled by the addition of alcohols. Because the alcohols perform other useful functions in the glue mix, they are left in the liquid adhesive. PRF adhesives are generally prepared firstly by reaction of phenol with formaldehyde to form a PF resol polymer, that has been proved to be in the greatest percentage, and often completely, linear [95], In the reaction step that follows the resorcinol chemical is added in excess to the PF-resol to react it with the PF-resin -CH2OH groups to form PRF polymers in which the resorcinol groups can be resorcinol chemical or any type of resorcinol-formaldehyde polymer. 

Where resorcinol adhesives are not suitable, resins can be prepared from modified resorcinol [128], Characteristic of these types of resins arc those used for tyre cord adhesives, in which a pure resorcinol-formaldehyde resin is used, or alternatively, alkyl resorcinol or oil-soluble resins suitable for rubber compounding are obtained by prereaction of resorcinol with fatty acids in the presence of sulfuric acid at high temperature followed by reaction with formaldehyde. Worldwide more than 90% of resorcinol adhesives are used as cold-setting wood adhesives. The other most notable application is as tyre cord adhesives, which constitutes less than 5% of the total use. 

PRF adhesives in which a liquid phenol-resorcinol-formaldehyde adhesive and a powder or liquid hardener are used are currently the most commonly used industrially. Pure resorcinol-formaldehyde (RF) adhesives were used extensively... 

More recently, a modification of the system described by Kreibich has been used extensively in industry with good success. Part A of the adhesive is again a standard phenol-resorcinol-formaldehyde (PRF) cold-setting adhesive, with powder hardener added at its standard pH. Part B can be either the same PRF adhesive with no hardener and the pH adjusted to 12, or a 50 to 55% tannin extract solution at a pH of 12-13, provided that the tannin is of the condensed or flavonoid type, such as mimosa, quebracho, or pine bark extract, with no hardener [118,135-137], The results obtained with these two systems are good and the resin not only has all the advantages desired but also the use of vegetable tannins and the halving of the resorcinol content makes the system considerably cheaper [118,135-137]. 

The most common adhesive system used for bonding continuous fibers and fabrics to rubber is resorcinol-formaldehyde latex (RFL) system. In general, RFL system is a water-based material. Different lattices including nitrile and SBR are used as the latex for the adhesive system. 2-Vinylpyridine-butadiene-styrene is the common latex used in the adhesive recipe. RFL system is widely being used in tires, diaphragms, power transmission belts, hoses, and conveyor belts because of its dynamic properties, adhesion, heat resistance, and the capacity to bond a wide range of fabrics and mbbers. 

A mixture of rubber latex and resorcinol-formaldehyde resin used to treat man-made and synthetic textiles to improve rubber/textile adhesion. 

Resorcinol formaldehyde latex (RFL) cord dips have only a limited application within the general rubber goods industry and for adhesion to be achieved with synthetic fibres it is necessary to use the systems developed by Bayer and Degussa. These systems are based upon a combination of resorcinol, a formaldehyde donor and a hydrated silica filler (commonly called the RFK system). This system is incorporated as dry ingredients into the rubber compound and is activated by the application of heat. 

---