Polymeric materials/polymers aramid

Composite In polymer technology a combination of a polymeric matrix and a reinforcing fiber with properties that the component materials do not have. The most common matrix resins are unsaturated thermosetting polyesters and epoxies, and reinforcing fibers are glass, carbon, and aramid fibers. The reinforcing fibers may be continuous or discontinuous. Some matrix resins are thermoplastics. 

Reichert and Mathias prepared related branched aramids, to those of Kim,t5-34] from 3,5-dibromoaniline (23) under Pd-catalyzed carbonylation conditions (Scheme 6.7). These brominated hyperbranched materials (24) were insoluble in solvents such as DMF, DMAc, and NMP, in contrast to the polyamine and polycarboxylic acid terminated polymers that Kim synthesized, which were soluble. This supports the observation that surface functionality plays a major role in determining the physical properties of hyperbranched and dendritic macromolecules J4,36 A high degree of cross-linking could also significantly effect solubility. When a four-directional core was incorporated into the polymerization via tetrakis(4-iodophenyl)adamantanc,1371 the resultant hyperbranched polybromide (e.g., 25) possessed enhanced solubility in the above solvents, possibly as a result of the disruption of crystallinity and increased porosity. 

Ultraflltraiion membranes are commonly asymmetric (skinned) polymeric membranes prepared by the phase inversion process. Materials commercially made into membranes include cellulose nitrate, cellulose acetate, polysulfone. aramids, polyvinylidene fluoride, and nctylonitrile polymers and copolymers. Inorganic meni-braues of hydrous zirconium oxide deposited on a tubular carbon backing are also commercially available. 

The chapter demonstrates that in spite of the incompatibility between hydrophilic natural fibres and hydrophobic polymeric matrices, the properties of natural fibre composites can be enhanced through chemical modifications. The chemical treatments have therefore played a key role in the increased applications of natural fibre composites in the automotive sector. Recent work has also shown that if some of the drawbacks of natural fibres can be adequately addressed, these materials can easily replace glass fibres in many applications. The chapter has also shown that there have been attempts to use natural fibre composites in structural applications, an area which has been hitherto the reserve of synthetic fibres like glass and aramid. The use of polymer nanocomposites in applications of natural fibre-reinforced composites, though at infancy, may provide means to address these efficiencies. Evidence-based life-cycle assessment of natural fibre-reinforced composites is required to build confidence in the green composites applications in automotive sector. 

Aramid yarns (Kevlar of DuPont, Twaron of Teijin-Twaron) are produced from poly(p-phenylene terephthalamide), PPTA (2), which is specially developed for fiber spinning and not used in any other application. DuPont had experience with poly(m-phenylene isophthalamide) in a fiber product called Nomex for high-temperature applications. The polymer is produced in dimethylacetamide and the solution is dry-spun. This cannot be done with the stiff-chain para-para analogue PPTA. The polymer does not dissolve in organic solvents. A special polymerization route had to be developed, and the discovery of lyotropic behavior of concentrated solutions in sulfuric acid then led the way to the production of a magnificent new fiber material. 

---