Oxidation in degradable

The Role of Oxidation in Degradation of Polymers The Relation of Oxidation to the Light Emission from Oxidized Polymers... 

Hydroxyethyl cellulose (HEC), a nonionic thickening agent, is prepared from alkali cellulose and ethylene oxide in the presence of isopropyl alcohol (46). HEC is used in drilling muds, but more commonly in completion fluids where its acid-degradable nature is advantageous. Magnesium oxide stabilizes the viscosity-building action of HEC in salt brines up to 135°C (47). HEC concentrations are ca 0.6—6 kg/m (0.2—21b/bbl). 

Tendering Effects. CeUulosic materials dyed with sulfur black have been known to suffer degradation by acid tendering when stored under moist warm conditions. This effect may result from the Hberation of small quantities of sulfuric acid which occurs when some of the polysulfide links of the sulfur dye are mptured. A buffer, such as sodium acetate, or a dilute alkaH in the final rinse, especially after oxidation in acidic conditions, may prevent this occurrence. Copper salts should never be used with sulfur black dyes because they cataly2e sulfuric acid generation. Few instances of tendering with sulfur dyes other than black occur and the problem is largely confined to cotton. 

Ethoxylated andSulfatedAlkylphenols. Because these aLkylphenols degrade less readily than the sulfated alcohol ethoxylates, their anticipated expansion failed to materialize, although by 1965 they were widely used in retail detergent products. Sulfated alkylphenol ethoxylates are used in hospital cleaning products, textile processing, and emulsion polymerization. Sulfated alkyphenol ethoxylates are sold as colorless, odorless aqueous solutions at concentrations of >30%. The presence of ethylene oxide in the molecule increases resistance to hardness ions and reduces skin irritation. Representative commercial sulfated alkylphenol ethoxylates are given in Table 12. 

Applications of ISS to polymer analysis can provide some extremely useful and unique information that cannot be obtained by other means. This makes it extremely complementary to use ISS with other techniques, such as XPS and static SIMS. Some particularly important applications include the analysis of oxidation or degradation of polymers, adhesive failures, delaminations, silicone contamination, discolorations, and contamination by both organic or inorganic materials within the very outer layers of a sample. XPS and static SIMS are extremely comple-mentar when used in these studies, although these contaminants often are undetected by XPS and too complex because of interferences in SIMS. The concentration, and especially the thickness, of these thin surfiice layers has been found to have profound affects on adhesion. Besides problems in adhesion, ISS has proven very useful in studies related to printing operations, which are extremely sensitive to surface chemistry in the very outer layers. 

Polypropylene differs from polyethylene in its chemical reactivity because of the presence of tertiary carbon atoms occurring alternately on the chain backbone. Of particular significance is the susceptibility of the polymer to oxidation at elevated temperatures. Some estimate of the difference between the two polymers can be obtained from Figure 1J.7, which compares- the rates of oxygen uptake of eaeh polymer at 93°C. Substantial improvements can be made by the inclusion of antioxidants and such additives are used in all commercial compounds. Whereas polyethylene cross-links on oxidation, polypropylene degrades to form lower molecular weight products. Similar effects are noted... 

The first step in the manufacture of the foil involves the production of alkali cellulose. This is then shredded and allowed to age in order that oxidation will degrade the polymer to the desired extent. The alkali cellulose is then treated with carbon disulphide in xanthating chums at 20-28°C for about three hours. 

Acrylate polymers also have fully saturated polymer backbones free of any heteroatoms in the main chain. This makes the polymers highly resistant to oxidation, photo-degradation and chemical attack. The acrylate groups are esters, which could be hydrolyzed under severe conditions. However, the hydrophobic nature of most acrylic polymers minimizes the risk for hydrolysis and, even if this reaction happened to some extent, the polymer backbone would still be intact. Other desirable acrylate properties include the following ... 

Acid acceptor. This is the main function of metal oxides in CR adhesive formulations. Upon age, small amounts of hydrochloric acid are released which may cause discolouration and substrate degradation. Magnesium oxide (4 phr) and zinc oxide (5 phr) act synergistically in the stabilization of solvent-borne polychloroprene adhesives against dehydrochlorination. 

Fatty acids with odd numbers of carbon atoms are rare in mammals, but fairly common in plants and marine organisms. Humans and animals whose diets include these food sources metabolize odd-carbon fatty acids via the /3-oxida-tion pathway. The final product of /3-oxidation in this case is the 3-carbon pro-pionyl-CoA instead of acetyl-CoA. Three specialized enzymes then carry out the reactions that convert propionyl-CoA to succinyl-CoA, a TCA cycle intermediate. (Because propionyl-CoA is a degradation product of methionine, valine, and isoleucine, this sequence of reactions is also important in amino acid catabolism, as we shall see in Chapter 26.) The pathway involves an initial carboxylation at the a-carbon of propionyl-CoA to produce D-methylmalonyl-CoA (Figure 24.19). The reaction is catalyzed by a biotin-dependent enzyme, propionyl-CoA carboxylase. The mechanism involves ATP-driven carboxylation of biotin at Nj, followed by nucleophilic attack by the a-carbanion of propi-onyl-CoA in a stereo-specific manner. 

The next three steps—reduction of the /3-carbonyl group to form a /3-alcohol, followed by dehydration and reduction to saturate the chain (Figure 25.7) — look very similar to the fatty acid degradation pathway in reverse. However, there are two crucial differences between fatty acid biosynthesis and fatty acid oxidation (besides the fact that different enzymes are involved) First, the alcohol formed in the first step has the D configuration rather than the L form seen in catabolism, and, second, the reducing coenzyme is NADPH, although NAD and FAD are the oxidants in the catabolic pathway. 

The smaller c/oio-dianions (n = 6, 7, 8) can then be obtained (in smaller yield) by the oxidative (air) degradation of BgHg " salts in the presence of EtOH, thf or 1,2-dimethoxyethane. 

Modern additive-treated oils are so stable that deposits and sludge formation in normal conditions have been almost eliminated. Consequently, the service life of the oils which is affected by oxidation thermal degradation and moisture is extended. 

---