Mechanical silicon carbides

Properties of Dense Silicon Carbide. Properties of the SiC stmctural ceramics are shown in Table 1. These properties are for representative materials. Variations can exist within a given form depending on the manufacturer. Figure 2 shows the flexure strength of the SiC as a function of temperature. Sintered or sinter/HIP SiC is the preferred material for appHcations at temperatures over 1400°C and the Hquid-phase densified materials show best performance at low temperatures. The reaction-bonded form is utilized primarily for its ease of manufacture and not for superior mechanical properties. 

Note The principal reinforcement, with respect to quantity, is glass fibers, but many other types are used (cotton, rayon, polyester/TP, nylon, aluminum, etc.). Of very limited use because of their cost and processing difficulty are whishers (single crystals of alumina, silicon carbide, copper, or others), which have superior mechanical properties. 

Figure 3.5. Schematic representation of the ROTACAT concept a homogeneous complex, immobilised on monoliths, and the implementation of these monoliths in the blades of a mechanical stirrer. Inset a picture of the stirrer with a silicon-carbide monolith...

Source of Heat Industrial furnaces are either fuel-fired or electric, and the first decision that a prospective furnace user must make is between these two. Although electric furnaces are uniquely suited to a few appheations in the chemical industry (manufacture of silicon carbide, calcium carbide, and graphite, for example), their principal use is in the metallurgical and metal-treatment industries. In most cases the choice between electric and fuel-fired is economic or custom-dictated, because most tasks that can be done in one can be done equally well in the other. Except for an occasional passing reference, electric furnaces will not be considered further here. The interested reader will find useful reviews of them in Kirk-Othmer Encyclopedia of Chemical Technology (4th ed., vol. 12, articles by Cotchen, Sommer, and Walton, pp. 228-265, Wiley, New York, 1994) and in Marks Standard Handbook for Mechanical Engineers (9th ed., article by Lewis, pp. 7.59-7.68, McGraw-Hill, New York, 1987). 

Reaction bonded silicon carbide (RBSiC) or self sintered silicon carbide (SSSiC)—see API Standard 682 for SiC application guidelines in mechanical seals... 

Most structural PMCs consist of a relatively soft matrix, such as a thermosetting plastic of polyester, phenolic, or epoxy, sometimes referred to as resin-matrix composites. Some typical polymers used as matrices in PMCs are listed in Table 1.28. The list of metals used in MMCs is much shorter. Aluminum, magnesium, titanium, and iron- and nickel-based alloys are the most common (see Table 1.29). These metals are typically utilized due to their combination of low density and good mechanical properties. Matrix materials for CMCs generally fall into fonr categories glass ceramics like lithium aluminosilicate oxide ceramics like aluminnm oxide (alnmina) and mullite nitride ceramics such as silicon nitride and carbide ceramics such as silicon carbide. 

Sintered silicon carbide retains its strength at elevated temperatures and shows excellent time-dependent properties such as creep and slow crack growth resistance. Reaction-bonded SiC, because of the presence of free silicon in its microstructure, exhibits slightly inferior elevated temperature properties as compared to sintered silicon carbide. Table 2 (11,43) and Table 3 (44) show selected mechanical properties of silicon carbide at room and elevated temperatures. 

Resistivity measurements of doped, alpha-silicon carbide single crystals from —195 to 725°C showed a negative coefficient of resistivity below room temperature, which gradually changed to positive above room temperature (45). The temperature at which the changeover occurred increased as the ionization of the donor impurity increased. This is believed to be caused by a change in conduction mechanism. 

E. H. Kraft and G. I. Dooher, "Mechanical Response of High Performance Silicon Carbides," presented at the Second International Conference on... 

Two principal mechanisms that may be responsible for mass loss from red giants are considered shock wave-driven winds and radiatively (dust)-dr iven winds. Effect of the periodic shocks accompanying nonlinear oscillations of red giants is most prominent in the outer layers of the stellar atmosphere where shocks are able not only to expel gas but also increase gas density so that some molecular components become supersaturated. In 0-rich stars the most abundant condensible species are silicon monoxide and iron, whereas in C-rich stars these are carbon, silicon carbide and iron. 

The carbides and nitrides are well known for their hardness and strength, and this section will briefly compare a number of these properties with those of the pure metals. Concentration will be placed here on the first row compounds, since these constitute a complete series, and Mo and W, since these are the most commonly studied metals. As will be shown, the physical and mechanical properties of carbides and nitrides resemble those of ceramics not those of metals. Comparisons will be made with boron carbide (B4C), silicon carbide (SiC), aluminium nitride (AIN), silicon nitride (Si3N4), aluminium oxide (A1203), and diamond, as representative ceramic materials. 

NISTCERAM National Institute of Standards and Techology Gas Research Institute, Ceramics Division mechanical, physical, electrical, thermal, corrosive, and oxidation properties for alumina nitride, beryllia, boron nitride, silicon carbide, silicon nitride, and zirconia... 

Silicon nitride is prized for its hardness (9 out of 10 on the Mohr scale), its wear resistance, and its mechanical strength at elevated temperatures. It melts and dissociates into the elements at 1,900 °C, and has a maximum use temperature near 1,800 °C in the absence of oxygen and near 1,500 °C under oxidizing conditions.41 It also has a relatively low density (3.185 g/cm3). Unlike silicon carbide, silicon nitride is an electrical insulator. The bulk material has a relatively good stability to aggressive chemicals. This combination of properties underlies its uses in internal combustion engines and jet engines. 

Although few applications have so far been found for ceramic matrix composites, they have shown considerable promise for certain military applications, especially in the manufacture of armor for personnel protection and military vehicles. Historically, monolithic ("pure") ceramics such as aluminum oxide (Al203), boron carbide (B4C), silicon carbide (SiC), tungsten carbide (WC), and titanium diboride (TiB2) have been used as basic components of armor systems. Research has now shown that embedding some type of reinforcement, such as silicon boride (SiBg) or silicon carbide (SiC), can improve the mechanical properties of any of these ceramics. 

---