Lipase acid /poly

Poly(malic acid) is a biodegradable and bioadsorbable water-soluble polyester having a carboxylic acid in the side chain. The chemoenzymatic synthesis of poly(malic acid) was achieved by the lipase-catalyzed polymerization of benzyl (3-malolactonate, followed by the debenzylation. The molecular weight of poly(benzyl (3-malolactonate) increased on copolymerizafion with a small amount of (3-PL using lipase CR catalyst. ... 

Enzymatic synthesis of aliphatic polyesters was also achieved by the ringopening polymerization of cyclic diesters. Lactide was not enzymatically polymerized under mild reaction conditions however, poly(lacfic acid) with the molecular weight higher than 1 x 10" was formed using lipase BC as catalyst at higher temperatures (80-130°C). Protease (proteinase K) also induced the polymerization however, the catalytic activity was relatively low. 

Ester-thioester copolymers were enzymatically synthesized (Scheme 7). ° The lipase CA-catalyzed copolymerization of e-caprolactone with 11-mercaptoundecanoic acid or 3-mercaptopropionic acid under reduced pressure produced the polymer with molecular weight higher than 2 x 10". The thioester unit of the resulting polymer was lower than the feed ratio. The transesterification between poly(8-caprolactone) and 11-mercaptoundecanoic acid or 3-mercaptopropionic acid also took place by lipase CA catalyst. Recently, aliphatic polythioesters were synthesized by lipase CA-catalyzed polycondensation of diesters with 1,6-hexanedithiol. ... 

A methacryl-type polyester macromonomer was synthesized by lipase PF-catalyzed polymerizahon of DDL using vinyl methacrylate as terminator ( terminator method ), in which the vinyl ester terminator was present from the beginning of the reachon (Scheme 17). In using divinyl sebacate as terminator, the telechelic polyester having a carboxylic acid group at both ends was obtained. Various non-protected thiol compounds were used as inihator or terminator for the thiol end-funchonalizahon of poly(8-CL). ... 

The enzymatic polymerization of 12-hydroxydodecanoic acid in the presence of 11-methacryloylaminoundecanoic acid conveniently produced the methacrylamide-type polyester macromonomer. Lipases CA and CC were active for the macromonomer synthesis. Enzymatic selective monosubstitution of a hydroxy-functional dendrimer was demonstrated. Lipase CA-catalyzed polymerization of 8-CL in the presence of the first generation dendrimer gave the poly(8-CL)-monosubstituted dendrimer. 

Block copolymers were synthesized by a combination of fipase-catalyzed polymerization and atom transfer radical polymerization (ATRE). " " At first, the polymerization of 10-hydroxydecanoic acid was carried out by using lipase CA as catalyst. The terminal hydroxy group was modified by the reaction with a-bromopropionyl bromide, followed by ATRP of styrene using CuCE2,2 -bipyridine as catalyst system to give the polyester-polystyrene block copolymer. Trichloromethyl-terminated poly(e-CL), which was synthesized by lipase CA-catalyzed polymerization with 2,2,2-trichloroethanol initiator, was used as initiator for ATRP of styrene. 

In 1985, a lipase-catalyzed polymerization of 10-hydroxydecanoic acid was reported. The monomer was polymerized in benzene using poly(ethylene glycol) (PEG)-modified lipase soluble in the medium [12]. The degree of polymerization (DP) of the product was more than 5. PEG-modified esterase from hog Ever and lipase from Aspergillus niger (lipase A) induced the oligomerization of glycolic acid [13]. 

Lactide was polymerized by lipase PC in bulk at high temperature (80-130°C) to produce poly(lactic acid) with Mw up to 2.7 x 105 [64, 65]. The molecular weight of the polymer from the D,L-isomer was higher than that from the d,d- and L,L-ones. Protease (proteinase K) also induced the polymerization of lactide, however, the catalytic activity was relatively low. 

Chemoenzymatic synthesis of biodegradable poly(malic acid) was performed by lipase-catalyzed polymerization of benzyl /J-malolactone, followed by the debenzylation [72]. The addition of a small amount of /J-PL (17 mol % for the monomer) increased Mw up to 3 x 104 [73]. 

The i-poly(3HB) depolymerase of R. rubrum is the only i-poly(3HB) depolymerase that has been purified [174]. The enzyme consists of one polypeptide of 30-32 kDa and has a pH and temperature optimum of pH 9 and 55 °C, respectively. A specific activity of 4 mmol released 3-hydroxybutyrate/min x mg protein was determined (at 45 °C). The purified enzyme was inactive with denatured poly(3HB) and had no lipase-, protease-, or esterase activity with p-nitro-phenyl fatty acid esters (2-8 carbon atoms). Native poly(3HO) granules were not hydrolyzed by i-poly(3HB) depolymerase, indicating a high substrate specificity similar to extracellular poly(3HB) depolymerases. Recently, the DNA sequence of the i-poly(3HB) depolymerase of R. eutropha was published (AB07612). Surprisingly, the DNA-deduced amino acid sequence (47.3 kDa) did not contain a lipase box fingerprint. A more detailed investigation of the structure and function of bacterial i-poly(HA) depolymerases will be necessary in future. 

Ester synthesis of fatty acid ethyl ester. The lipase-catalyzed esterification of fatty acid and alcohol is well-known. It was also favorable for the esterification of poly unsaturated fatty acids under mild conditions with the enzyme. However, the activity of native lipase is lower in polar organic solvents, i.e. ethanol and methanol. The synthesis of Ae fatty acid ethyl ester was carried out in ethanol using the palmitic acid-modified lipase. As shown in Figure 7, the reactivity of the modified lipase in this system was much higher than that of the unmoditied lipase. 

Poly(s-caprolactone) Poly(e-caprolactone) is a semicrystalline polymer synthesized by anionic, cationic, free-radical, or ring-opening polymerization [94]. It is available in a range of molecular weights and degrades by bulk hydrolysis autocatalyzed by the carboxylic acid end groups. The presence of enzymes such as protease, amylase, and pancreatic lipase accelerates polymer degradation [95], The various methods of preparation of poly(e-caprolactone) nanoparticles include emulsion polymerization, interfacial deposition, emulsion-solvent evaporation, desolvation, and dialysis. These methods and various applications are extensively reviewed [94],... 

Lipases are of remarkable practical interest since they have been used in numerous biocatalytic applications, such as kinetic resolution of alcohols and carboxyl esters (both in water and in non-aqueous media) [1], regioselective acylations of poly-hydroxylated compounds, and the preparation of enantiopure amino acids and amides [2, 3]. Moreover, lipases are stable in organic solvents, do not require cofactors, possess broad substrate specificity, and exhibit, in general, a high enantioselectivity. All these features have contributed to make hpases the class of enzyme with the highest number of biocatalytic applications carried out in neat organic solvents. 

Lipase catalysts have been used for functionalization of polymers. A terminal hydroxy group of poly-(e-CL) was reacted with carboxylic acids using lipase CA catalyst to give end-functionalized polyesters.231 Lipase MM catalyzed the regioselective transesterification of the terminal ester group of oligo (methyl methacrylate) with allyl alcohol.232 In the PPL-catalyzed reaction of racemic 2,2,2-trichloroethyl 3,4-epoxybutanoate with hydroxy-terminated PEG, the... 

---