High-density ethylene

Low-density Medium-density High-density Ultra high-molecular-weight Glass-fiber- reinforced, high-density Ethylene-vinyl acetate copolymer... 

Equistar Chemicals L. D. Polyethylene, Petro high density Ethylene, isobutane, comonomer, catalyst Slurry loop HDPE technology for blow molding, injection molding and others 3 1985... 

Polyethylene films as packaging ma terial plastic squeeze bottles are molded from high density poly ethylene... 

HDPE, high density polyethylene PP, polypropylene EVA, ethylene—vinyl alcohol SMC, sheet-molding compound ERP, fiber-reinforced plastic LDPE, low density polyethylene PE, polyethylene BMC, bulk mol ding compound TPE, thermoplastic elastomer. 

Table 6 shows the sales estimates for principal film and sheet products for the year 1990 (14). Low density polyethylene films dominate the market in volume, followed by polystyrene and the vinyls. High density polyethylene, poly(ethylene terephthalate), and polypropylene are close in market share and complete the primary products. A number of specialty resins are used to produce 25,000—100,000 t of film or sheet, and then there are a large number of high priced, high performance materials that serve niche markets. The original clear film product, ceUophane, has faUen to about 25,000 t in the United States, with only one domestic producer. Table 7 Hsts some of the principal film and sheet material manufacturers in the United States.

Second, in the early 1950s, Hogan and Bank at Phillips Petroleum Company, discovered (3,4) that ethylene could be catalyticaHy polymerized into a sohd plastic under more moderate conditions at a pressure of 3—4 MPa (435—580 psi) and temperature of 70—100°C, with a catalyst containing chromium oxide supported on siUca (Phillips catalysts). PE resins prepared with these catalysts are linear, highly crystalline polymers of a much higher density of 0.960—0.970 g/cnr (as opposed to 0.920—0.930 g/cnf for LDPE). These resins, or HDPE, are currentiy produced on a large scale, (see Olefin polymers, HIGH DENSITY POLYETHYLENE). 

High density polyethylene (HDPE) is defined by ASTM D1248-84 as a product of ethylene polymerisation with a density of 0.940 g/cm or higher. This range includes both homopolymers of ethylene and its copolymers with small amounts of a-olefins. The first commercial processes for HDPE manufacture were developed in the early 1950s and utilised a variety of transition-metal polymerisation catalysts based on molybdenum (1), chromium (2,3), and titanium (4). Commercial production of HDPE was started in 1956 in the United States by Phillips Petroleum Company and in Europe by Hoechst (5). HDPE is one of the largest volume commodity plastics produced in the world, with a worldwide capacity in 1994 of over 14 x 10 t/yr and a 32% share of the total polyethylene production. 

The chemical iadustry manufactures a large variety of semicrystalline ethylene copolymers containing small amounts of a-olefins. These copolymers are produced ia catalytic polymerisation reactions and have densities lower than those of ethylene homopolymers known as high density polyethylene (HDPE). Ethylene copolymers produced ia catalytic polymerisation reactions are usually described as linear ethylene polymers, to distiaguish them from ethylene polymers containing long branches which are produced ia radical polymerisation reactions at high pressures (see Olefin POLYMERS, LOWDENSITY polyethylene). 

Polypropylene polymers are typically modified with ethylene to obtain desirable properties for specific applications. Specifically, ethylene—propylene mbbers are introduced as a discrete phase in heterophasic copolymers to improve toughness and low temperature impact resistance (see Elastomers, ETHYLENE-PROPYLENE rubber). This is done by sequential polymerisation of homopolymer polypropylene and ethylene—propylene mbber in a multistage reactor process or by the extmsion compounding of ethylene—propylene mbber with a homopolymer. Addition of high density polyethylene, by polymerisation or compounding, is sometimes used to reduce stress whitening. In all cases, a superior balance of properties is obtained when the sise of the discrete mbber phase is approximately one micrometer. Examples of these polymers and their properties are shown in Table 2. Mineral fillers, such as talc or calcium carbonate, can be added to polypropylene to increase stiffness and high temperature properties, as shown in Table 3. 

In the early 1950s, Ziegler observed that certain heterogeneous catalysts based on transition metals polymerized ethylene to a linear, high density material at modest pressures and temperatures. Natta showed that these catalysts also could produce highly stereospecific poly-a-olefins, notably isotactic polypropylene, and polydienes. They shared the 1963 Nobel Prize in chemistry for their work. 

Nor is it tme that poly(ethylene terephthalate) (PET) and high density polyethylene (HDPE) packaging are hsted as 1 and 2 in the Society of the Plastics Industry (SPI) recycling coding system because they are the most recyclable. The numbers assigned to each plastic in the SPI coding system are purely arbitrary and do not redect the material s recyclabihty. 

HDPE melts at about 135°C, is over 90% crystalline, and is quite linear, with more than 100 ethylene units per side chain. It is harder and more rigid than low density polyethylene and has a higher melting point, tensile strength, and heat-defiection temperature. The molecular weight distribution can be varied considerably with consequent changes in properties. Typically, polymers of high density polyethylene are more difficult to process than those of low density polyethylene. 

Following the considerable commercial success of Ziegler-Natta polymerisation systems which made possible high density polyethylene, polypropylene, ethylene-propylene rubbers and a number of speciality materials, a considerable... 

Tension Above materials plus High-density polyethylene Polypropylene Acetal polymers Aliphatic polyamides (nylons) PPO Poly(ethylene terephthalate) Polysulphones... 

The Phillips process for the manufacture of high-density polyethylene may be adapted to produce copolymers of ethylene with small amounts of propylene or but-l-ene and copolymers of this type have been available since 1958. These soon found application in blown containers and for injection moulding. Properties of two grades of such copolymers are compared with two grades of Phillips-type homopolymer in Table 11.11. 

Pdlysulphortes High-density polyethylene ftilyphenyiene oxide Propylene -ethylene copolymers ABS... 

High-pressure polymerization of ethylene was introduced in the 1930s. The discovery of a new titanium catalyst hy Karl Ziegler in 1953 revolutionized the production of linear unhranched polyethylene at lower pressures. The two most widely used grades of polyethylene are low-density polyethylene (LDPE) and high-density polyethylene (HDPE). Currently,... 

---