Dielectric loss properties

The anhydride hardened epoxies generally have better dielectric loss properties above the Tg than do the novolac epoxies. Consequently, a higher device Junction temperature can be tolerated because of less leakage at the plastic/chip interface and because the required heat dissipation can be obtained via the filler. This is, unfortunately, obtained at the expense of moisture resistance because the moisture resistance of the anhydride-hardened epoxies is not as good as the novolac epoxies. 

The time-temperature superpositioning principle was applied f to the maximum in dielectric loss factors measured on poly(vinyl acetate). Data collected at different temperatures were shifted to match at Tg = 28 C. The shift factors for the frequency (in hertz) at the maximum were found to obey the WLF equation in the following form log co + 6.9 = [ 19.6(T -28)]/[42 (T - 28)]. Estimate the fractional free volume at Tg and a. for the free volume from these data. Recalling from Chap. 3 that the loss factor for the mechanical properties occurs at cor = 1, estimate the relaxation time for poly(vinyl acetate) at 40 and 28.5 C. 

Electrica.1 Properties. The bulk electrical properties of the parylenes make them excellent candidates for use in electronic constmction. The dielectric constants and dielectric losses are low and unaffected by absorption of atmospheric water. The dielectric strength is quoted for specimens of 25 p.m thickness because substantially thicker specimens cannot be prepared by VDP. If the value appears to be high in comparison with other materials, however, it should be noted that the usual thickness for such a measurement is 3.18 mm. Dielectric strength declines with the square root of increasing... 

Electrical. Glasses are used in the electrical and electronic industries as insulators, lamp envelopes, cathode ray tubes, and encapsulators and protectors for microcircuit components, etc. Besides their abiUty to seal to metals and other glasses and to hold a vacuum and resist chemical attack, their electrical properties can be tailored to meet a wide range of needs. Generally, a glass has a high electrical resistivity, a high resistance to dielectric breakdown, and a low power factor and dielectric loss. 

Grade XXXPC is similar in electrical properties to Grade XXXP and suitable for punching at lower temperatures than Grade XXXP. This grade is recommended for apphcations requiring high insulation resistance and low dielectric losses under severe humidity conditions. 

Grade G-10, glass fabric with epoxy resin binder, has extremely high mechanical strength (flexural, impact, and bonding) at room temperature and good dielectric loss and electric strength properties under both dry and humid conditions. 

Electrical Properties. AH polyolefins have low dielectric constants and can be used as insulators in particular, PMP has the lowest dielectric constant among all synthetic resins. As a result, PMP has excellent dielectric properties and alow dielectric loss factor, surpassing those of other polyolefin resins and polytetrafluoroethylene (Teflon). These properties remain nearly constant over a wide temperature range. The dielectric characteristics of poly(vinylcyclohexane) are especially attractive its dielectric loss remains constant between —180 and 160°C, which makes it a prospective high frequency dielectric material of high thermal stabiUty. 

The moisture content of a plastic affects such conditions as electrical insulation resistance, dielectric losses, mechanical properties, dimensions, and appearances. The effect on the properties due to moisture content depends largely on the type of exposure (by immersion in water or by exposure to high humidity), the shape of the product, and the inherent behavior properties of the plastic material. The ultimate proof for tolerance of moisture in a product has to be a product test under extreme conditions of usage in which critical dimensions and needed properties are verified. Plastics with very low water-moisture absorption rates tend to have better dimensional stability. 

The heating characteristics of a particular material (for example, a solvent) under microwave irradiation conditions are dependent on the dielectric properties of the material. The ability of a specific substance to convert electromagnetic energy into heat at a given frequency and temperature is determined by the so-called loss tangent, tan <5. The loss factor is expressed as the quotient tan (3 = "/ , where e" is the dielectric loss, indicative of the efficiency with which electromagnetic radiation is... 

---