Atactic polymer chain

Figure 1.3 Isotaotio, syndiotactic, and atactic polymer chains.

Polymers without configurational regularity are called atactic. Configurationally regular polymers can fonn crystalline stmctures, while atactic polymers are almost always amorjihous. Many polymers consist of linear molecules, however, nonlinear chain architectures are also important (figure C2.1.2). 

In an atactic arrangement, substituents are in an unordered sequence along the polymer chains. 

Figure 1.2 Sections of polymer chains of differing tacticity (a) isotactic (b) syndiotactic (c) atactic.

Any of the four monomer residues can be arranged in a polymer chain in either head-to-head, head-to-tail, or tail-to-tail configurations. Each of the two head-to-tail vinyl forms can exist as syndiotactic or isotactic stmctures because of the presence of an asymmetric carbon atom (marked with an asterisk) in the monomer unit. Of course, the random mix of syndiotactic and isotactic, ie, atactic stmctures also exists. Of these possible stmctures, only... 

Homopolymerization of butadiene can proceed via 1,2- or 1,4-additions. The 1,4-addition produces the geometrically distinguishable trans or cis stmctures with internal double bonds on the polymer chains, 1,2-Addition, on the other hand, yields either atactic, isotactic, or syndiotactic polymer stmctures with pendent vinyl groups (Eig. 2). Commercial production of these polymers started in 1960 in the United States. Eirestone and Goodyear account for more than 60% of the current production capacity (see Elastomers, synthetic-polybutadiene). 

For the 1,2- and 3,4-addition, a chiral carbon (marked by an asterisk) is formed which has an R or 3 configuration, but there is no net optical activity, because equal amounts of the R and S configurations are formed. The R and S configurations along the polymer chains lead to diastereomeric isomers called isotactic, syndiotactic, and atactic. In isotactic polyisoprene all monomer units have the same configuration as illustrated for isotactic... 

The struetural element of a eoumarone-indene resin is relatively similar to that for aromatie hydroearbon resins, as they differ only in the proportion of indene-type struetures which are present in higher eoneentration in the eoumarone-indene resins. The main monomers in the aromatie resins are styrene and indene. Styrene produces the atactic conformation of the resins, whereas indene introduees rigidity into the polymer chain. A typical structural element of an aromatie resin is given in Fig. 11. 

The NMR spectrum of the polymer 14.16 shows two singlets of approximately equal intensities that differ in chemical shift by only 0.17 ppm. This observation is attributed to the formation of equal amounts of isotactic (14.16a, both S=0 groups on the same side of the polymer chain) and syndiotactic (14.16b, S=0 groups on opposite sides of the polymer chain) forms of the polymer. The atacticity is confirmed by the H and NMR spectra. Two resonances are observed for the McaP groups of 14.16a, whereas 14.16b gives rise to only one resonance. 

The term tactidty refers to the configuration of polymer chains when their constituent monomer residues contain a steric center. Figure 1.8 illustrates the three principal classes of tacticity as exemplified by polypropylene. In isotactic polypropylene, the methyl groups are all positioned on the same side of the chain, as shown in Fig. 1.8 a). In syndiotactic polypropylene, the methyl groups alternate from one side to the other, as shown in Fig. 1.8 b). Random placement of the methyl groups results in atactic polypropylene, which is shown in Fig. 1.8 c). We can readily observe the effects of tacticity on the properties of polypropylene isotactic polypropylene is hard and stiff at room temperature, syndiotactic polypropylene is soft and flexible, and atactic polypropylene is soft and rubbery. 

In atactic polymers, side groups are irregularly positioned on either side of the chain, as illustrated schematically in Fig. 1.8 c). A truly atactic polymer would comprise a random distribution of steric centers. In practice, atactic polymers typically show some preference for either meso or racemic placement The tendency towards stereoregularity is due to the fact that polymerization catalysts often contain steric centers, which tend to direct the incoming monomers and the growing chain into preferred configurations. 

The vinyl chloride monomer polymerizes via addition polymerization to form polyvinyl chloride. The final polymer has the chemical composition shown in Fig. 22.1. The polymer exhibits limited crystallinity, though this property is not often considered as important in defining its performance. It tends to be atactic or regionally syndiotactic, surrounded by extended atactic runs. When exposed to temperatures above 100 °C, polyvinyl chloride decomposes, creating free radicals that further attack the polymer chain, as we shall discuss in more detail later. For this reason, the degradation of polyvinyl chloride is autocatalytic... 

There are still some non-explained observations. For example, syndiotactic PP was reported [45,46] as being more stable than isotactic polymer. At 140°C, the maximum chemiluminescence intensity was achieved after 2,835 min for syndiotactic PP, while isotactic polymer attained the maximum after only 45 min. Atactic PP was reported to be more stable than the isotactic polymer [46]. An explanation has been offered that the structure of isotactic PP is much more favourable for autooxidation, which proceeds easier via a back-biting mechanism where peroxyl radicals abstract adjacent tertiary hydrogens on the same polymer chain. 

Very active catalysts for the preparation of strictly alternating butadiene-propylene copolymers (BPR) consist of V0(0R)2C1/i-Bu Al (R = neopentyl). The CH3 side groups in BPR stiffen the polymer chain and were expected to promote the formation of strain-induced structures. The fact that we could not detect strain-induced crystallization is probably due to an atactic configuration of the propylene units. 

On the basis of the X-ray structural data as well as the mode of polymerization, Yasuda et al. [3a] proposed a coordination anionic mechanism involving an eight membered transition state for the organolanthanide-initiated polymerization of MM A (Fig. 6). The steric control of the polymerization reaction may be ascribed to the intermolecular repulsion between C(7) and C(9) (or the polymer chain), since completely atactic polymerization occurred when the monomer was methyl or ethyl acrylate. 

Based on Chien s research results, Collins et al. modified the basic structure of the catalysts and also achieved elastic material [8,18,19]. In both cases the elastic properties of the polymers are justified in a block structure with isotactic and atactic sequences. In 1999 Rieger et al. presented a couple of asymmetric, highly active metallocene catalysts, e.g., the dual-side catalyst rac-[l-(9-r 5-fluorenyl)-2-(5,6-cyclo-penta-2-methyl-l-q5-indenyl)ethane]zirconium dichloride (Fig. 3). These catalysts allowed building of isolated stereoerrors in the polymer chain to control the tacticity and therefore the material properties of the polymers [9],... 

As stated above, we postulated that fast, reversible chain transfer between two different catalysts would be an excellent way to make block copolymers catalytically. While CCTP is well established, the use of main-group metals to exchange polymer chains between two different catalysts has much less precedent. Chien and coworkers reported propylene polymerizations with a dual catalyst system comprising either of two isospecific metallocenes 5 and 6 with an aspecific metallocene 7 [20], They reported that the combinations gave polypropylene (PP) alloys composed of isotactic polypropylene (iPP), atactic polypropylene (aPP), and a small fraction (7-10%) claimed by 13C NMR to have a stereoblock structure. Chien later reported a product made from mixtures of isospecific and syndiospecific polypropylene precatalysts 5 and 8 [21] (detailed analysis using WAXS, NMR, SEC/FT-IR, and AFM were said to be done and details to be published in Makromolecular Chemistry... 

Although the definitions of isotactic, syndiotactic, and atactic polymers according to International Union of Pure and Applied Chemistry (IUPAC) rules are well established in terms of succession of mesa (m) or racemic (r) dyads,12 the symbolism of (+) and (—) bonds allows the easy treatments of possible configurations in cases of any complexity.1 Moreover, the (+) or (—) character of the bonds in a polymer chain is strictly related to the accessibility of gauche+ or gauche conformations of the bonds and, therefore, to the formation of right-handed or left-handed helical conformations.1... 

---