Lactones bearing functions inside the ring that do not interfere with the ROP mechanism, such an ether [106-113], an amine [114,115], an amide [116-118], an unsaturation [119-122], or a ketone [123] are shown in Fig. 27. If the functional group is not tolerated by the polymerization mechanism, it has then to be protected as is the case for amines [114, 115]. 

Many of the common condensation polymers are listed in Table 1-1. In all instances the polymerization reactions shown are those proceeding by the step polymerization mechanism. This chapter will consider the characteristics of step polymerization in detail. The synthesis of condensation polymers by ring-opening polymerization will be subsequently treated in Chap. 7. A number of different chemical reactions may be used to synthesize polymeric materials by step polymerization. These include esterification, amidation, the formation of urethanes, aromatic substitution, and others. Polymerization usually proceeds by the reactions between two different functional groups, for example, hydroxyl and carboxyl groups, or isocyanate and hydroxyl groups. 

Electron-transfer initiation from other radical-anions, such as those formed by reaction of sodium with nonenolizable ketones, azomthines, nitriles, azo and azoxy compounds, has also been studied. In addition to radical-anions, initiation by electron transfer has been observed when one uses certain alkali metals in liquid ammonia. Polymerizations initiated by alkali metals in liquid ammonia proceed by two different mechanisms. In some systems, such as the polymerizations of styrene and methacrylonitrile by potassium, the initiation is due to amide ion formed in the system [Overberger et al., I960]. Such polymerizations are analogous to those initiated by alkali amides. Polymerization in other systems cannot be due to amide ion. Thus, polymerization of methacrylonitrile by lithium in liquid ammonia proceeds at a much faster rate than that initiated by lithium amide in liquid ammonia [Overberger et al., 1959]. The mechanism of polymerization is considered to involve the formation of a solvated electron ... 

The action of bases on caprolactam or amide groups of the polymer molecule is not limited to the disproportionation and transamidation reactions which are directly involved in the polymerization mechanism. A more detailed study of the polymerization kinetics has shown that the... 

There are two fundamental polymerization mechanisms. Classically, they have been differentiated as addition polymerization and condensation polymerization. In the addition process, no by-product is evolved, as in the polymerization of vinyl chloride (see below) whereas in the condensation process, just as in various condensation reactions (e.g., esterification, etherification, amidation, etc.) of organic chemistry, a low-molecular-weight by-product (e.g., H2O, HCl, etc.) is evolved. Polymers formed by addition polymerization do so by the successive addition of unsaturated monomer units in a chain reaction promoted by the active center. Therefore, addition polymerization is called chain polymerization. Similarly, condensation polymerization is referred to as step polymerization since the polymers in this case are formed by stepwise, intermolecular condensation of reactive groups. (The terms condensation and step are commonly used synonymously, as we shall do in this book, and so are the terms addition and chain. However, as it will be shown later in this section, these terms cannot always be used synonymously. In fact, the condensation-addition classification is primarily applicable to the composition or structure of polymers, whereas the step-chain classification applies to the mechanism of polymerization reactions.)... 

This polymer has a melting point of 276 °C and is soluble in DMSO, from which clear films could be cast. A proton-transfer polymerization mechanism was suggested by Yoda and Marvel as operative in this case74, similar to that first proposed by Breslow and coworkers75 for carbonyl amides, as follows ... 

The polymerization mechanism proposed involves a coordination of the isocyanate with the titanium catalyst and its insertion to form a titanium-amidate end group speeies. The titanium end group stays active imtil quenched by the addition of a protonic source. The addition of other monoalkyl isocyanates gives a block copolymer. 

The term acrylic apphes to a family of copolymers of monomers that are polymerized by a chain growth mechanism. Most often, the mechanism of polymerization is by free radical initiation. Other mechanisms of polymerization, such as ionic and group transfer polymerization, are possible but will not be discussed in this publication. For a description of other polymerization mechanisms, polymer textbooks are available (5,6). Technically, acrylic monomers are derivatives of acrylic or methacrylic acid. These derivatives are nonfunctional esters (methyl methacrylate, butyl acrylate, etc.), amides (acrylamide), nitrile (acrylonitrile), and esters that contain functional groups (hydroxyethyl acrylate, glycidyl methacrylate, dimethylaminoethyl acrylate). Other monomers that are not acryhc derivatives are often included as components of acryhc resins because they are readily copolymerized with the acryhc derivatives. Styrene is often used in significant quantities in acryhc copolymers. 

As normally polymerized, PVF melts between IH5 and 210 °C and contains 12 18% inverted monomer units ft is normally considered a thermoplastic, but because of its instability above its melting point, it cannot be processed by conventional thermoplastic techniques Instead it is generally extruded into films in a solvent swollen (organosol) form and the solvent is subsequently evaporated and recovered Such films can be onented further to achieve specific mechanical properties PVF films are exceptionally weather and radiabon resistant considenng their modest fluonne content PVF is insoluble below 100 °C but, at higher temperatures, it dissolves in polar solvents like amides, ketones, tetramethylene sulfone, and tetramethylurea Resistance to acids and bases at room temperature IS good [1, 29 ... 

Amine-terminated siloxane oligomers have also been utilized in the synthesis of various siloxane-amide and siloxane-imide copolymers, High molecular weight siloxane-amide copolymers have been synthesized by the solution or interfacial co-polymerization of siloxane oligomers with sebacoyl chloride or terephthaloyl chloride respectively 1S5,165). In some reactions diamine chain extenders have also been utilized. Thermal and dynamic mechanical characterization of these copolymers have shown the formation of multiphase systems160). Compression molded films displayed very good elastomeric properties. 

This is a highly polar polymer and crystalline due to the presence of amide linkages. To achieve effective intercalation and exfoliation, the nanoclay has to be modified with some functional polar group. Most commonly, amino acid treatment is done for the nanoclays. Nanocomposites have been prepared using in situ polymerization [85] and melt-intercalation methods [113-117]. Crystallization behavior [118-122], mechanical [123,124], thermal, and barrier properties, and kinetic study [125,126] have been carried out. Nylon-based nanocomposites are now being produced commercially. 

---