Reverse osmosis module seawater desalination

The first reverse osmosis modules made from cellulose diacetate had a salt rejection of approximately 97—98%. This was enough to produce potable water (ie, water containing less than 500 ppm salt) from brackish water sources, but was not enough to desalinate seawater efficiently. In the 1970s, interfacial composite membranes with salt rejections greater than 99.5% were developed, making seawater desalination possible (29,30) a number of large plants are in operation worldwide. 

As Figure 5.12 shows, Toray s PEC-1000 crosslinked furfuryl alcohol membrane has by far the best sodium chloride rejection combined with good fluxes. This explains the sustained interest in this membrane despite its extreme sensitivity to dissolved chlorine and oxygen in the feed water. Hollow fine fiber membranes made from cellulose triacetate by Toyobo or aromatic polyamides by Permasep (Du Pont) are also comfortably in the one-stage seawater desalination performance range, but the water fluxes of these membranes are low. However, because large-surface-area, hollow fine fiber reverse osmosis modules can be... 

Albany International Research Co. has developed an advanced hollow fiber composite reverse osmosis membrane and module under the name of Quantro II . This composite membrane is comprised of a porous hollow fiber substrate on which has been deposited a rejection barrier capable of fluxes of commercial importance at high rejection of dissolved salts at elevated temperatures. Resistance to active chlorine has been demonstrated. Proprietary processes have been developed for spinning of the fiber, establishment of the rejection barrier and processing of the fiber to prepare modules of commercial size. Prototype modules are currently in field trials against brackish and seawater feed solutions. Applications under consideration for this membrane include brackish and seawater desalination as well as selected industrial concentration processes. 

Membrane research and development started in Du Pont in 1962 and culminated in the introduction of the first B-9 Permasep permeator for desalination of brackish water by reverse osmosis (RO) in 1969. The membrane in this B-9 Permasep module consisted of aramid hollow fibers. In 1969, proponents of RO technology had ambitious dreams and hopes. Today, RO is a major desalination process used worldwide to provide potable water from brackish and seawater feeds. Du Font s membrane modules for RO are sold under the trademark Permasep permeators. The RO business is a virtually autonomous profit center that resides in the Polymer Products Department. The growth and success of the Permasep products business is a direct result of Du Font s sustained research and development commitment to polyamides, a commitment that dates back to the 1930 s and the classic polymer researches of Wallace H. Carothers. Since 1969, improved and new Permasep permeators have been introduced six times, as shown in Table I. 

To overcome the problems of cellulose acetate membranes, many synthetic polymeric materials for reverse osmosis were proposed, but except for one material, none of them proved successful. The only one material, which could remain on the market, was the linear aromatic polyamide with pendant sulfonic acid groups, as shown in Figure 1.2. This material was proposed by DuPont, which fabricated very fine hollow fiber membranes the modules of this membrane were designated B-9 and B-10. They have a high rejection performance, which can be used for single-stage seawater desalination. They were widely used for mainly seawater or brackish water desalination and recovery of valuable materials such as electric deposition paints, until DuPont withdrew them from the market in 2001. 

A new application area for membranes is energy production. Reverse electrodialysis and pressure retarded osmosis could provide significant quantities of energy from the mixing of fresh water with seawater or mixing the concentrated brine effluent of desalination plants with seawater. However, these applications will require significant reduction in membrane and module costs. 

---