Methacrylates PMMA

Mixtures of polymers at surfaces provide the interesting possibility of exploring polymer miscibility in two dimensions. Baglioni and co-workers [17] have shown that polymers having the same orientation at the interface are compatible while those having different orientations are not. Some polymers have their hydrophobic portions parallel to the surface, while others have a perpendicular disposition. The surface orientation effect is also present in mixtures of poly(methyl methacrylate), PMMA, and fatty acids. 

Poly(methyl methacrylate) (PMMA) Ethylene-chlorotrifluoroethylene copolymer... 

Acrylics. Acetone is converted via the intermediate acetone cyanohydrin to the monomer methyl methacrylate (MMA) [80-62-6]. The MMA is polymerized to poly(methyl methacrylate) (PMMA) to make the familiar clear acryUc sheet. PMMA is also used in mol ding and extmsion powders. Hydrolysis of acetone cyanohydrin gives methacrylic acid (MAA), a monomer which goes direcdy into acryUc latexes, carboxylated styrene—butadiene polymers, or ethylene—MAA ionomers. As part of the methacrylic stmcture, acetone is found in the following major end use products acryUc sheet mol ding resins, impact modifiers and processing aids, acryUc film, ABS and polyester resin modifiers, surface coatings, acryUc lacquers, emulsion polymers, petroleum chemicals, and various copolymers (see METHACRYLIC ACID AND DERIVATIVES METHACRYLIC POLYMERS). 

The cured polymers are hard, clear, and glassy thermoplastic resins with high tensile strengths. The polymers, because of their highly polar stmcture, exhibit excellent adhesion to a wide variety of substrate combinations. They tend to be somewhat britde and have only low to moderate impact and peel strengths. The addition of fillers such as poly (methyl methacrylate) (PMMA) reduces the brittleness somewhat. Newer formulations are now available that contain dissolved elastomeric materials of various types. These mbber-modifted products have been found to offer adhesive bonds of considerably improved toughness (3,4). 

Unlike most crystalline polymers, PVDF exhibits thermodynamic compatibiUty with other polymers (133). Blends of PVDF and poly(methyl methacrylate) (PMMA) are compatible over a wide range of blend composition (134,135). SoHd-state nmr studies showed that isotactic PMMA is more miscible with PVDF than atactic and syndiotactic PMMA (136). MiscibiUty of PVDF and poly(alkyl acrylates) depends on a specific interaction between PVDF and oxygen within the acrylate and the effect of this interaction is diminished as the hydrocarbon content of the ester is increased (137). Strong dipolar interactions are important to achieve miscibility with poly(vinyhdene fluoride) (138). PVDF blends are the object of many papers and patents specific blends of PVDF and acryflc copolymers have seen large commercial use. 

Examples of photothermoplasts include polyacrylates, polyacrylamides, polystyrenes, polycarbonates, and their copolymers (169). An especially well-re searched photothermoplast is poly(methyl methacrylate) (PMMA), which is blended with methyl methacrylate (MMA) or styrene as a monomer, and titanium-bis(cyclopentadienyl) as a photoinitiator (170). 

Poly(methyl methacrylate). PMMA offers distinct advantages over BPA-PC with respect to significandy lower birefringence, higher modulus, and lower costs, but has not been successhil as a material for audio CDs and CD-ROM as well as a substrate material for WORM and EOD disks because of its high water absorption (which makes it prone to warp) and its unsuitabiUty for metallising, and less so because of its low resistance to... 

Fig. 26. Qualitative compatison of substrate materials for optical disks (187) An = birefringence IS = impact strength BM = bending modulus HDT = heat distortion temperature Met = metallizability WA = water absorption Proc = processibility. The materials are bisphenol A—polycarbonate (BPA-PC), copolymer (20 80) of BPA-PC and trimethylcyclohexane—polycarbonate (TMC-PC), poly(methyl methacrylate) (PMMA), uv-curable cross-linked polymer (uv-DM), cycHc polyolefins (CPO), and, for comparison, glass.

The cadmium chalcogenide semiconductors (qv) have found numerous appHcations ranging from rectifiers to photoconductive detectors in smoke alarms. Many Cd compounds, eg, sulfide, tungstate, selenide, teUuride, and oxide, are used as phosphors in luminescent screens and scintiUation counters. Glass colored with cadmium sulfoselenides is used as a color filter in spectroscopy and has recently attracted attention as a third-order, nonlinear optical switching material (see Nonlinear optical materials). DiaLkylcadmium compounds are polymerization catalysts for production of poly(vinyl chloride) (PVC), poly(vinyl acetate) (PVA), and poly(methyl methacrylate) (PMMA). Mixed with TiCl, they catalyze the polymerization of ethylene and propylene. 

Hard lenses can be defined as plastic lenses that contain no water, have moduli in excess of 5 MPa (500 g/mm ), and have T well above the temperature of the ocular environment. Poly(methyl methacrylate) (PMMA) has excellent optical and mechanical properties and scratch resistance and was the first and only plastic used as a hard lens material before higher oxygen-permeable materials were developed. PMMA lenses also show excellent wetting in the ocular environment even though they are hydrophobic, eg, the contact angle is 66°. 

The toughness of interfaces between immiscible amorphous polymers without any coupling agent has been the subject of a number of recent studies [15-18]. The width of a polymer/polymer interface is known to be controlled by the Flory-Huggins interaction parameter x between the two polymers. The value of x between a random copolymer and a homopolymer can be adjusted by changing the copolymer composition, so the main experimental protocol has been to measure the interface toughness between a copolymer and a homopolymer as a function of copolymer composition. In addition, the interface width has been measured by neutron reflection. Four different experimental systems have been used, all containing styrene. Schnell et al. studied PS joined to random copolymers of styrene with bromostyrene and styrene with paramethyl styrene [17,18]. Benkoski et al. joined polystyrene to a random copolymer of styrene with vinyl pyridine (PS/PS-r-PVP) [16], whilst Brown joined PMMA to a random copolymer of styrene with methacrylate (PMMA/PS-r-PMMA) [15]. The results of the latter study are shown in Fig. 9. 

An example of this improvement in toughness can be demonstrated by the addition of Vamac B-124, an ethylene/methyl acrylate copolymer from DuPont, to ethyl cyanoacrylate [24-26]. Three model instant adhesive formulations, a control without any polymeric additive (A), a formulation with poly(methyl methacrylate) (PMMA) (B), and a formulation with Vamac B-124 (C), are shown in Table 4. The formulation with PMMA, a thermoplastic which is added to modify viscosity, was included to determine if the addition of any polymer, not only rubbers, could improve the toughness properties of an alkyl cyanoacrylate instant adhesive. To demonstrate an improvement in toughness, the three formulations were tested for impact strength, 180° peel strength, and lapshear adhesive strength on steel specimens, before and after thermal exposure at 121°C. 

Polymethyl Methacrylate (PMMA), This material has exceptional optical clarity and resistance to outdoor exposure. It is resistant to alkalis, detergents, oils and dilute acids but is attacked by most solvents. Its peculiar property of total internal reflection is useful in advertising signs and some medical applications. 

In this stage of the investigation, poly(methyl methacrylates) (PMMAs) were selected as the polymeric probes of intermediate polarity. Polymers of medium broad molar mass distribution and of low tacticity (14) were a gift of Dr. W. Wunderlich of Rohm Co., Darmstadt, Germany. Their molar masses ranged from 1.6 X 10" to 6.13 X 10 g-mol. For some comparative tests, narrow polystyrene standards from Pressure Co. (Pittsburgh, PA) were used. 

Molecular weight calibration from a monomer to several million daltons can be carried out by a variety of techniques. Because narrow standards of p(methyl methacrylate) (pMMA) are available, these are often used. Narrow standards of p(styrene) (pSty) are also available and can be used. Using the Mark-Houwink-Sakurada equation and the parameters for pSty and pMMA, a system calibrated with pSty can give pMMA-equivalent values, and vice versa. 

Acrylic These polymethyl methacrylate (PMMA) plastics have high optical clarity,... 

This molecule is a copolymer with polymethyl methacrylate (PMMA) in acrylic latex paints, where the hydrophobic PMMA is surrounded by hydrophilic polyvinyl acetate molecules. Such a suspension of a hydrophobic polymer wrapped in a hydrophilic polymer is called a latex. 

Polymethyl methacrylate (PMMA) octylacrylamide/acrylates/butyl-aminoethyl methacrylate copolymer Plexiglas... 

An idea of the range of materials and applications for polymers in medicine can be gained from the information in Table 10.1. As can be seen from this table a number of polymers are used in medical applications. One particular such polymer is poly (methyl methacrylate), PMMA. Early on it was used as the material for fabricating dentures later other biomedical applications developed. For example, PMMA is now used as the cement in the majority of hip replacement operations worldwide. 

Atlanta, Ga., 26th-30th April 1998, p.2942-5. 012 FEEDSTOCK RECYCLING OF POLYMETHYL METHACRYLATE (PMMA) BY DEPOLYMERISING IN A REACTIVE EXTRUSION PROCESS Breyer K Michaeli W IKV (SPE)... 

---