High-density polyethylene chromium catalyst

Second, in the early 1950s, Hogan and Bank at Phillips Petroleum Company, discovered (3,4) that ethylene could be catalyticaHy polymerized into a sohd plastic under more moderate conditions at a pressure of 3—4 MPa (435—580 psi) and temperature of 70—100°C, with a catalyst containing chromium oxide supported on siUca (Phillips catalysts). PE resins prepared with these catalysts are linear, highly crystalline polymers of a much higher density of 0.960—0.970 g/cnr (as opposed to 0.920—0.930 g/cnf for LDPE). These resins, or HDPE, are currentiy produced on a large scale, (see Olefin polymers, HIGH DENSITY POLYETHYLENE). 

High density polyethylene (HDPE) is defined by ASTM D1248-84 as a product of ethylene polymerisation with a density of 0.940 g/cm or higher. This range includes both homopolymers of ethylene and its copolymers with small amounts of a-olefins. The first commercial processes for HDPE manufacture were developed in the early 1950s and utilised a variety of transition-metal polymerisation catalysts based on molybdenum (1), chromium (2,3), and titanium (4). Commercial production of HDPE was started in 1956 in the United States by Phillips Petroleum Company and in Europe by Hoechst (5). HDPE is one of the largest volume commodity plastics produced in the world, with a worldwide capacity in 1994 of over 14 x 10 t/yr and a 32% share of the total polyethylene production. 

Low pressure (0.1 to 20 MPa) and temperatures of 50 to 300°C using heterogeneous catalysts such as molybdenum oxide or chromium oxide supported on inorganic carriers to produce high density polyethylene (HDPE), which is more linear in nature, with densities of 0.94 to 0.97 g/cm. ... 

High-density polyethylene (HDPE) is produced by a low-pressure process in a fluid-bed reactor. Catalysts used for HDPE are either of the Zieglar-type (a complex of A1(C2H5)3 and a-TiCl4) or silica-alumina impregnated with a metal oxide such as chromium oxide or molybdenum oxide. 

The metal catalyzed production of polyolefins such as high density polyethylene (HDPE), linear low density polyethylene (LLDPE) and polypropylene (PP) has grown into an enormous industry. Heterogeneous transition metal catalysts are used for the vast majority of PE and all of the PP production. These catalysts fall generally within two broad classes. Most commercial PP is isotactic and is produced with a catalyst based on a combination of titanium chloride and alkylaluminum chlorides. HDPE and LLDPE are produced with either a titanium catalyst or one based on chromium supported on silica. Most commercial titanium-based PE catalysts are supported on MgCl2. 

High-density polyethylene (HDPE) is a commodity chemical that is produced on a very large scale in one of two catalytic processes the Ziegler-Natta and the Phillips process. The latter accounts for about one third of all polyethylene. It uses a catalyst consisting of small amounts of chromium (0.2-1.0 wt% Cr) on a silica support, developed by Hogan and Banks at the Phillips Petroleum Company in the early 1950s [84,85]. 

The high-density polyethylene is linear and can be manufactured by (i) coordination polymerisation of monomer by triethyl aluminium and tritanium chloride, (ii) polymerisation with supported Metal Oxide Catalysts. Such as chromium or molybdenum oxides supported over alumina-silica bases. 

The commercial production of high-density polyethylene started almost at the same time in late 1956 by Phillips using a chromium-based catalyst in a medium-pressure process and by Hoechst using a Ziegler catalyst in a low-pressure process. Polypropylene production began in Montecatini and Hercules plants in 1957. Poly(l-butene) and poly(4-methyl-1-pentene) have been produced in small commercial quantities since about 1965. The commercial production of ethylene/propylene-based rubbers started in 1960 [241]. 

Polymerization with Complex Catalysts. High density polyethylene reached a domestic production of 1.25 billion pounds in 1968. It is made either with a stereospecific Ziegler-Natta catalyst or on a supported chromium oxide catalyst. The latter forms a complex with the silica-alumina and is activated by treatment with air and steam at elevated temperature. The mechanism is such that electrons are donated to the catalyst in order to be returned under polymerizational-promoting conditions, consequently lowering the energy of the system ... 

Application The Innovene G (gas phase) process produces linear-low-density polyethylene (LLDPE) and high-density polyethylene (HDPE) using either Ziegler-Natta, chromium or metallocene catalysts. 

Medium Density High Density Polyethylene MDPE (or MDHDPE) is produced by copolymerization of ethylene with a-olefins using Ziegler-Natta, supported chromium or single site catalysts. MDPE cannot be produced by free radical polymerization. MDPE has a linear structure similar to LLDPE, but comonomer content is lower. Density is typically 0.93-0.94 g/cm. MDPE is used in geomembrane and pipe applications. 

Commercial linear polyethylene, the most commonly used type of plastic, was bom more than half a century ago with the accidental discovery at Phillips Petroleum Company that chromium oxide supported on silica can polymerize a-olefins.1 The same catalyst system, modified and evolved, is used even today by dozens of companies throughout the world, and it accounts for a large share of the world s high-density polyethylene (HDPE) supply, as well as some low-density polymers. The catalyst is now more active and has been tailored in numerous ways for many specialized modem applications. This chapter provides a review of our understanding of the complex chemistry associated with this catalyst system, and it also provides examples of how the chemistry has been exploited commercially. It is written from an industrial perspective, drawing especially on the commercial experience and the research of numerous scientists working at Phillips Petroleum... 

The use of fluidized beds for gas-phase polymerization started in 1968 with the UNIPOL process, which was developed by Union Carbide to make high-density polyethylene. This process has now been adapted to produce other grades of polyethylene as well as polypropylene and various copolymers. The fluid bed is composed of porous particles, which are aggregates of polymer containing fine grains of titanium, chromium, or other metal catalyst. Polymerization takes place at the polymer-catalyst interface, and the particles grow larger over a period of several hours. Some of the polymer is withdrawn continuously or at intervals to maintain the bed... 

Phillips supported chromium (II) catalyst, the most commonly used for high density polyethylene (HDPE) manufacture, possibly behaves in a similar manner, but the olefin insertion reaction is faster by several orders of magnitude. In the original Zeigler catalyst systems for HDPE, an aluminium alkyl is used to reductively alkylate the primary component, most frequently a titanium compound, to give the true catalytic species. 

Gas-phase polymerization n. A polymerization process developed by Union Carbide for high-density polyethylene, particularly for a grade for making paper-like films. Purified ethylene and a highly active chromium-containing catalyst in dry-powder form are fed continuously into a fluidized-bed reactor. The resin forms as a powder, thereby avoiding the gel, discoloration, and contamination problems often associated with conventional polymerization processes. 

Other Early Developments. In addition to the breakthrough by Ziegler, two other discoveries of ethylene polymerization catalysts were made in the early 1950s. A patent by Standard Oil of Indiana, filed in 1951, disclosed reduced molybdenum oxide or cobalt molybdate on alumina (13). At the same time, Phillips discovered supported chromium oxide catalysts, prepared by impregnation of a silica-alumina support with Cr03 (14 16). Both the Phillips catalyst and titanium chloride based Ziegler catalysts are widely used in the production of high density polyethylene (HDPE). 

---