Fiber reinforcement composites

Keywords Bast fibers Composite reinforcement Fiber modification Fiber properties Fiber structure... 

Flammability. PhenoHcs have inherently low flammabiHty and relatively low smoke generation. For this reason they are widely used in mass transit, tiinnel-building, and mining. Fiber glass-reinforced phenoHc composites are capable of attaining the 1990 U.S. Federal Aviation Administration (FAA) regulations for total heat release and peak heat release for aircraft interior facings (1,70). 

Carbon-Fiber Composites. Cured laminates of phenoHc resins and carbon-fiber reinforcement provide superior flammabiHty resistance and thermal resistance compared to unsaturated polyester and epoxy. Table 15 shows the dependence of flexural strength and modulus on phenoHc—carbon-fiber composites at 30—40% phenoHc resin (91). These composites also exhibit long-term elevated temperature stabiHty up to 230°C. 

Sophisticated stmctural analysis techniques make it possible to determine both the amount and exact orientation of reinforcement that the product wQl need to meet the critical stresses in actual service. Hybrid reinforcement systems containing different fiber compositions with different properties are being increasingly used. For example, hybrid carbon and glass fiber automotive drive shafts are in commercial use. 

A variety of materials has been proposed to modify the properties of asphaltic binders to enhance the properties of the mix (112), including fillers and fibers to reinforce the asphalt—aggregate mixture (114), sulfur to strengthen or harden the binder (115,116), polymers (98,117—121), mbber (122), epoxy—resin composites (123), antistripping agents (124), metal complexes (125,126), and lime (127,128). AH of these additives serve to improve the properties of the binder and, ultimately, the properties of the asphalt—aggregate mix. 

Because of their unique blend of properties, composites reinforced with high performance carbon fibers find use in many structural applications. However, it is possible to produce carbon fibers with very different properties, depending on the precursor used and processing conditions employed. Commercially, continuous high performance carbon fibers currently are formed from two precursor fibers, polyacrylonitrile (PAN) and mesophase pitch. The PAN-based carbon fiber dominates the ultra-high strength, high temperature fiber market (and represents about 90% of the total carbon fiber production), while the mesophase pitch fibers can achieve stiffnesses and thermal conductivities unsurpassed by any other continuous fiber. This chapter compares the processes, structures, and properties of these two classes of fibers. 

Baxter, W.J., The strength of metal matrix composites reinforced with randomly oriented discontinuous fibers, 1992, Metall Trans. 23A, 3045... 

Resin with an accelerator added but not catalyst. According to ASTM, those plastics having superior properties over those consisting of the base resin, due to the presence of high-strength fillers embedding in the composition. Reinforcing fillers are fibers, fabrics or mats made of fibers. 

The mechanical properties of composites reinforced with wood fibers and PVC or PS as resin can be improved by an isocyanate treatment of those cellulose fibers [41,50] or the polymer matrix [50]. Polymethylene-polyphenyl-isocianate (PMPPIC) in pure state or solution in plasticizer can be used. PMPPIC is chemically linked to the cellulose matrix through strong covalent bonds (Fig. 8). 

The lower thermal stability of natural fibers, up to 230°C, the thermal stability is only small, which limits the number of thermoplastics to be considered as matrix materials for natural fiber composites. Only those thermoplastics whose processing temperature does not exceed 230°C are usable for natural fiber reinforced composites. These are, most of all, polyolefines, such as polyethylene and polypropylene. Technical thermoplastics, such as poyamides, polyesters, and polycarbonates, require... 

The mechanical properties of composites are mainly influenced by the adhesion between matrix and fibers of the composite. As it is known from glass fibers, the adhesion properties could be changed by pretreatments of fibers. So special process, chemical and physical modification methods were developed. Moisture repel-lency, resistance to environmental effects, and, not at least, the mechanical properties are improved by these treatments. Various applications for natural fibers as reinforcement in plastics are encouraged. 

A discontinuous fiber composite is one that contains a relatively short length of fibers dispersed within the matrix. When an external load is applied to the composite, the fibers are loaded as a result of stress transfer from the matrix to the fiber across the fiber-matrix interface. The degree of reinforcement that may be attained is a function of fiber fraction (V/), the fiber orientation distribution, the fiber length distribution, and efficiency of... 

On the other hand, fiber reinforcement makes the composite strong. Moreover, the matrix can be reinforced in the required direction by design, which ensures the maximum utilization of the fiber-properties. A disadvantage in fiber composites is that the fibers are able to transmit loads only in the directions of their axis and there is less strengthening effect in the direction perpendicular to the axis, and in some cases even weakening may occur. 

---