Ethylene metallocene catalysts

Side chains (short branches) can be intentionally added to low pressure polyethylene. To achieve this, a certain amotmt of longer alkenes (olefins) such as butene-1 or octene-1 are mixed into the ethylene. Metallocene catalysts then insert them in... 

Abstract. This paper presents results from quantum molecular dynamics Simula tions applied to catalytic reactions, focusing on ethylene polymerization by metallocene catalysts. The entire reaction path could be monitored, showing the full molecular dynamics of the reaction. Detailed information on, e.g., the importance of the so-called agostic interaction could be obtained. Also presented are results of static simulations of the Car-Parrinello type, applied to orthorhombic crystalline polyethylene. These simulations for the first time led to a first principles value for the ultimate Young s modulus of a synthetic polymer with demonstrated basis set convergence, taking into account the full three-dimensional structure of the crystal. 

Commercial production of PE resias with densities of 0.925 and 0.935 g/cm was started ia 1968 ia the United States by Phillips Petroleum Co. Over time, these resias, particularly LLDPE, became large volume commodity products. Their combiaed worldwide productioa ia 1994 reached 13 X 10 metric t/yr, accouatiag for some 30% market share of all PE resias ia the year 2000, LLDPE productioa is expected to iacrease by 50%. A aew type of LLDPE, compositioaaHy uniform ethylene—a-olefin copolymers produced with metallocene catalysts, was first introduced by Exxon Chemical Company in 1990. The initial production volume was 13,500 t/yr but its growth has been rapid indeed, in 1995 its combiaed production by several companies exceeded 800,000 tons. 

As a rule, LLDPE resins do not contain long-chain branches. However, some copolymers produced with metallocene catalysts in solution processes can contain about 0.002 long-chain branches per 100 ethylene units (1). These branches are formed in auto-copolymerisation reactions of ethylene with polymer molecules containing vinyl double bonds on their ends (2). 

The second type of solution polymerization concept uses mixtures of supercritical ethylene and molten PE as the medium for ethylene polymerization. Some reactors previously used for free-radical ethylene polymerization in supercritical ethylene at high pressure (see Olefin POLYMERS,LOW DENSITY polyethylene) were converted for the catalytic synthesis of LLDPE. Both stirred and tubular autoclaves operating at 30—200 MPa (4,500—30,000 psig) and 170—350°C can also be used for this purpose. Residence times in these reactors are short, from 1 to 5 minutes. Three types of catalysts are used in these processes. The first type includes pseudo-homogeneous Ziegler catalysts. In this case, all catalyst components are introduced into a reactor as hquids or solutions but form soHd catalysts when combined in the reactor. Examples of such catalysts include titanium tetrachloride as well as its mixtures with vanadium oxytrichloride and a trialkyl aluminum compound (53,54). The second type of catalysts are soHd Ziegler catalysts (55). Both of these catalysts produce compositionaHy nonuniform LLDPE resins. Exxon Chemical Company uses a third type of catalysts, metallocene catalysts, in a similar solution process to produce uniformly branched ethylene copolymers with 1-butene and 1-hexene called Exact resins (56). 

Metallocene Catalysts. Polymerization of cycloolefins with Kaminsky catalysts (combinations of metallocenes and methylaluminoxane) produces polymers with a completely different stmcture. The reactions proceeds via the double-bond opening in cycloolefins and the formation of C—C bonds between adjacent rings (31,32). If the metallocene complexes contain bridged and substituted cyclopentadienyl rings, such as ethylene(hisindenyl)zirconium dichloride, the polymers are stereoregular and have the i j -diisotactic stmcture. 

The Ticona materials are prepared by continuous polymerisation in solution using metallocene catalysts and a co-catalyst. The ethylene is dissolved in a solvent which may be the comonomer 2-norbomene itself or another hydrocarbon solvent. The comonomer ratio in the reactor is kept constant by continuous feeding of both monomers. After polymerisation the catalyst is deactivated and separated to give polymers of a low residual ash content and the filtration is followed by several degassing steps with monomers and solvents being recycled. 

Since the last edition several new materials have been aimounced. Many of these are based on metallocene catalyst technology. Besides the more obvious materials such as metallocene-catalysed polyethylene and polypropylene these also include syndiotactic polystyrenes, ethylene-styrene copolymers and cycloolefin polymers. Developments also continue with condensation polymers with several new polyester-type materials of interest for bottle-blowing and/or degradable plastics. New phenolic-type resins have also been announced. As with previous editions I have tried to explain the properties of these new materials in terms of their structure and morphology involving the principles laid down in the earlier chapters. 

Novel polyethylene materials have been synthesized by copolymerization of ethylene with 1-butene, 1-hexene, and/or 1-octene using metallocene catalyst systems [9]. 

U. Moll and M. Lux, Manufacture of ethylene/alpha olefin copolymers with metallocene catalysts in slurry loop... 

A. Akimoto and A. Yano, Production of ethylene copolymers with metallocene catalysts at high pressure and its properties, MetCon 94 Proceedings, USA, May 1994. 

The successful polymerization of a, >-dienes via ADMET continually produces a small molecule, typically ethylene, and the removal of this small molecule drives the reaction. When Schrock s [W] and [Mo] alkylidenes (14) are used, care has to be taken in maintaining an inert atmosphere devoid of both moisture and air in order to avoid decomposition of the catalyst. For this reason, Schlenk line techniques such as those used to handle Ziegler-Natta or metallocene catalysts and high purity monomers are important. 

Polymerizatioii of ethylene with embedded metallocene catalysts... 

The sterically unencumbered catalyst active site allows the copolymerization of a wide variety of olefins with ethylene. Conventional heterogeneous Ziegler/Natta catalysts as well as most metallocene catalysts are much more reactive to ethylene than higher olefins. With constrained geometry catalysts, a-olefins such as propylene, butene, hexene, and octene are readily incorporated in large amounts. The kinetic reactivity ratio, rl, is approximately... 

Several copolymers of or-olelins are used as drag reducers. Suggested recipes are summarized in Table 12-1. Linear low-density polyethylene is a copolymer of ethylene and a-olefins. It is obtained by copolymerization utilizing Ziegler-Natta catalysts or metallocene catalysts. Concentrates may be prepared by... 

Figure 19 (a) Peak melting temperature as a function of the branch content in ethylene-octene copolymers (labelled -O, and symbol —B (symbol, ) and -P (symbol, A) are for ethylene-butene and ethylene-propylene copolymers, respectively) and obtained from homogeneous metallocene catalysts show a linear profile, (b) Ziegler-Natta ethylene-octene copolymers do not show a linear relationship between peak melting point and branch content [125]. Reproduced from Kim and Phillips [125]. Reprinted with permission of John Wiley Sons, Inc. 

These are some key advantages that the metallocene catalysts have over conventional Ziegler-Natta catalysts and hence it is highly probable that inter-and intra-chain heterogeneity expected in ethylene-a-olefins copolymers can be controlled through the use of the metallocene system. 

---