Cross-linked polymers 1-8 INDEX

LDPE homopolymers in the 0.2—150 melt index or 100, 000 20,000 mPa s(= cP) viscosity range. Specialty polymers such as greases and waxes or highly cross-linked polymers are not included. 

Critical Oxygen Index (COI), 853 Critical size, 704-705 Critical spherical nucleus, 710, 711 Critical strain, 867, 868 Critical stress energy factor, 474 Critical surface tension of wetting, 232 Critical temperature, 655 Cross-linked polymers, 29 Cross-linking, 148 Cross model, 731 Cross polarisation, 376, 377 Crystallinity, 728, 732, 815 Crystallites/Crystallisation, 690, 725 of rigid macromolecules, 739 Cyclical chain length, 782... 

Usually, the chiroptical properties of highly cross-linked polymers cannot be measured. The asymmetry of the empty cavities can be deduced from their excellent racemate resolution ability, but under special conditions it can also be directly detected by optical activity measurements [41]. For this, the polymer is suspended in a solvent that has the same refractive index as the polymer, a technique which was developed for other types of insoluble polymers. The values of molar optical rotation thus determined are shown in Table 4.3. 

Fire retardancy of fabrics treated by using the same procedure as given above was evaluated by limiting oxygen index (LOI) measurements according to ISO 4589-2 (Tsafack et al., 2004). The results obtained for the acrylates phosphates and phosphonates monomers show that LOI values increase with the relative phosphorus content in the monomer and therefore in the grafted polymer. This can be explained by the fact that phosphate monomers compared to phosphonate monomers are subject to more chain transfers that lead to highly cross-linked polymers and decrease the flammability (Tsafack et al., 2(X)4). 

The method of choice for the determination of these quantities on HDPE resin is gel permeation chromatography. In this chromatographic method a solvent with the dissolved polyethylene flows through a column filled with a porous material. It is usually a gel of cross-linked polymers. Depending upon the size of the polyethylene coils in the solution, they can fit to the pores of the gel, stick there and block them whereby the transport is retarded. Larger polyethylene chains are transported unhindered with the solvent flow. Thus a size-dependent retardation occurs which justifies the other term size exclusion chromatography (SEC). In the chromatogram, which shows polymer concentration (determined for example via optical measurements (refractive index)) as a function of time, the time coordinate corresponds to a polymer molecular mass coordinate and the concentration... 

The Index Guide (2) gives no information on how cross-linked polymers are indexed, because CAS treats them as copolymers. 

The major use of vinylpyrrohdinone is as a monomer in manufacture of poly(vinylpyrrohdinone) (PVP) homopolymer and in various copolymers, where it frequendy imparts hydrophilic properties. When PVP was first produced, its principal use was as a blood plasma substitute and extender, a use no longer sanctioned. These polymers are used in pharmaceutical and cosmetic appHcations, soft contact lenses, and viscosity index improvers. The monomer serves as a component in radiation-cured polymer compositions, serving as a reactive diluent that reduces viscosity and increases cross-linking rates (see... 

The mineral talc is extremely soft (Mohs hardness = 1), has good sHp, a density of 2.7 to 2.8 g/cm, and a refractive index of 1.58. It is relatively inert and nonreactive with conventional acids and bases. It is soluble in hydroduoric acid. Although it has a pH in water of 9.0 to 9.5, talc has Lewis acid sites on its surface and at elevated temperatures is a mild catalyst for oxidation, depolymerization, and cross-linking of polymers. 

The commercial grades available in the 1970s used either zinc or sodium as the cross-linking ion and ranged in melt flow index from 0.4 to 14. The main application of the ionomer resins has been for packaging film. The polymer is particularly useful in composite structures to provide an outer layer with good heat sealability. The puncture resistance of film based on ionomer film has the puncture resistance of a LDPE film of twice the gauge. 

In an alternate synthesis, the formation of thermoplastic vulcanizate (TPV) is accomplished with two polymers, wherein one polymer is grafted with a carboxylic acid anhydride, which then is reacted with an aminosilane, which reacts with the acid anhydride and then cross-links with moismre. The vulcanizates exhibit good mechanical properties and lower melt-flow index than the starting polymers. 

Cross-linked pre-polymers having fractionalized molecular weights between 35,000 and 70,000 daltons with polydispersity indexes of less than 3.4 have been prepared by the free radical addition of 2-hydroxethyl methacrylate, HEMA, with 2% methacrylic acid or glycerol methacrylate. Once crosslinked, these materials are particularly useful as contact lenses because of their limited shrinkage and expansion. 

---