Catalysts Raman spectroscopy

Bulk Mixed Oxide Catalysts. - Raman spectroscopy of bulk transition metal oxides encompasses a vast and well-established area of knowledge. Hie fundamental vibrational modes for many of the transitional metal oxide complexes have already been assigned and tabulated for systems in the solid and solution phases. Perhaps the most well-known and established of the metal oxides are the tungsten and molybdenum oxides because of their excellent Raman signals and applications in hydrotreating and oxidation catalysis. Examples of these two very important metal-oxide systems are presented below for bulk bismuth molybdate catalysts, in this section, and surface (two-dimensional) tungstate species in a later section. 

Vibrational Spectroscopy. Infrared absorption spectra may be obtained using convention IR or FTIR instrumentation the catalyst may be present as a compressed disk, allowing transmission spectroscopy. If the surface area is high, there can be enough chemisorbed species for their spectra to be recorded. This approach is widely used to follow actual catalyzed reactions see, for example. Refs. 26 (metal oxide catalysts) and 27 (zeolitic catalysts). Diffuse reflectance infrared reflection spectroscopy (DRIFT S) may be used on films [e.g.. Ref. 28—Si02 films on Mo(llO)]. Laser Raman spectroscopy (e.g.. Refs. 29, 30) and infrared emission spectroscopy may give greater detail [31]. 

Raman spectroscopy of catalysts [INFRARED TECHNOLOGY AND RAMAN SPECTROSCOPY - RAMAN SPECTROSCOPY] (Vol 14) -refractory coating for [REFRACTORY COATINGS] (Vol 21)... 

Lead Telluride. Lead teUuride [1314-91 -6] PbTe, forms white cubic crystals, mol wt 334.79, sp gr 8.16, and has a hardness of 3 on the Mohs scale. It is very slightly soluble in water, melts at 917°C, and is prepared by melting lead and tellurium together. Lead teUuride has semiconductive and photoconductive properties. It is used in pyrometry, in heat-sensing instmments such as bolometers and infrared spectroscopes (see Infrared technology AND RAMAN SPECTROSCOPY), and in thermoelectric elements to convert heat directly to electricity (33,34,83). Lead teUuride is also used in catalysts for oxygen reduction in fuel ceUs (qv) (84), as cathodes in primary batteries with lithium anodes (85), in electrical contacts for vacuum switches (86), in lead-ion selective electrodes (87), in tunable lasers (qv) (88), and in thermistors (89). 

Chemical Properties. MSA combines high acid strength with low molecular weight. Its pK (laser Raman spectroscopy) is —1.9, about twice the acid strength of HCl and half the strength of sulfuric acid. MSA finds use as catalyst for esterification, alkylation, and in the polymerisation and curing of coatings (402,404,405). The anhydrous acid is also usefijl as a solvent. 

The surfaces of porous materials, e. g. catalysts, molecular sieves, or adsorbents, are much more readily accessible than smooth surfaces to Raman spectroscopy, because larger amounts of adsorbed substance can be placed within the laser focus, thus contributing to the scattering process. 

Raman spectroscopy has provided information on catalytically active transition metal oxide species (e. g. V, Nb, Cr, Mo, W, and Re) present on the surface of different oxide supports (e.g. alumina, titania, zirconia, niobia, and silica). The structures of the surface metal oxide species were reflected in the terminal M=0 and bridging M-O-M vibrations. The location of the surface metal oxide species on the oxide supports was determined by monitoring the specific surface hydroxyls of the support that were being titrated. The surface coverage of the metal oxide species on the oxide supports could be quantitatively obtained, because at monolayer coverage all the reactive surface hydroxyls were titrated and additional metal oxide resulted in the formation of crystalline metal oxide particles. The nature of surface Lewis and Bronsted acid sites in supported metal oxide catalysts has been determined by adsorbing probe mole-... 

This review will endeavor to outline some of the advantages of Raman Spectroscopy and so stimulate interest among workers in the field of surface chemistry to utilize Raman Spectroscopy in the study of surface phenomena. Up to the present time, most of the work has been directed to adsorption on oxide surfaces such as silicas and aluminas. An examination of the spectrum of a molecule adsorbed on such a surface may reveal information as to whether the molecule is physically or chemically adsorbed and whether the adsorption site is a Lewis acid site (an electron deficient site which can accept electrons from the adsorbate molecule) or a Bronsted acid site (a site which can donate a proton to an adsorbate molecule). A specific example of a surface having both Lewis and Bronsted acid sites is provided by silica-aluminas which are used as cracking catalysts. 

Friedel-Crafts catalysts, 329, 331 Friedel-Crafts reaction, 297, 361 Front-end reactions, 235 FT Raman spectroscopy, 387 FTIR spectrometry. See Fourier transform infrared (FTIR) spectrometry Fuel cells, 272-273 Full prepolymers, 236, 237 Functionalized polyolefins, 459-460... 

The vibrations of molecular bonds provide insight into bonding and stmcture. This information can be obtained by infrared spectroscopy (IRS), laser Raman spectroscopy, or electron energy loss spectroscopy (EELS). IRS and EELS have provided a wealth of data about the stmcture of catalysts and the bonding of adsorbates. IRS has also been used under reaction conditions to follow the dynamics of adsorbed reactants, intermediates, and products. Raman spectroscopy has provided exciting information about the precursors involved in the synthesis of catalysts and the stmcture of adsorbates present on catalyst and electrode surfaces. 

In this chapter we have limited ourselves to the most common techniques in catalyst characterization. Of course, there are several other methods available, such as nuclear magnetic resonance (NMR), which is very useful in the study of zeolites, electron spin resonance (ESR) and Raman spectroscopy, which may be of interest for certain oxide catalysts. Also, all of the more generic tools from analytical chemistry, such as elemental analysis, UV-vis spectroscopy, atomic absorption, calorimetry, thermogravimetry, etc. are often used on a routine basis. 

However, we have found that reaction induced restructuring of Bi2FeMo20]2 produces a narked enhancement in catalytic behavior (Table II . X-ray diffraction, in-situ Raman spectroscopy, and photoelectron spectroscopy reveal that the restructuring produces a multiphase system consisting of unreacted Bi FeMo20.2, in combination with Bi2MOj0.2, 0-FeHoO and a small amount of Bi2MoO. The key features of the Raman spectra of the activated catalyst are summarized in Table III. 

In the early 1990s Raman spectroscopy was applied to the characterization of TS-1 catalysts [55,56]. In such experiments, beside the 960 cm band, already observed by IR spectroscopy (see Sect. 3.5), a new component at 1125 cm was detected by Scarano et al. [55] (see Fig. 2f). The 1125 cm band was recognized to be a fingerprint of the insertion of Ti atoms in the ze-olitic framework [55]. This band could not be observed in the IR studies as totally overshadowed by an extremely intense band around 1000 cm due to Si02 framework modes (Fig. 2e). 

It will be shown that, upon interaction with water or ammonia, the T -like symmetry of the Ti(IV) centers in TS-1 is strongly distorted, as testified by UV-Vis, XANES, resonant Raman spectroscopies [45,48,52,58,64,83,84], and by ab initio calculations [52,64,74-76,88]. As in Sect. 3 for the dehydrated catalyst, the discussion follows the different techniques used to investigate the interaction. 

Possible applications include optical coatings [98], catalysts [99-101], substrates for Surface Enhanced Raman spectroscopy [102] or biosensor electrodes [103], Mesoporous gold can be prepared by de-aHoying a suitable precursor such as a... 

The identification of surface adsorbed species has been carried out with FT-IR [69] and Raman spectroscopy [70] during reaction and with GC-MS after epoxidation reaction [72]. The aggregation of gold NPs is not appreciable during reaction at temperatures below 473 K [69,72]. Catalyst deactivation, which happens within a few hours causing a decrease in C3FI6 conversion by about 50%, can be accounted for by the accumulation of successively oxidized compounds after isomerization and cracking of... 

Raman spectroscopy has been used for a long time in order to study supported and promoted metal catalysts and oxide catalysts [84] since many information can be obtained (1) identification of different metal oxide phases (2) structural transformations of metal oxide phases (3) location of the supported oxide on the oxide substrate and... 

Bruckner, A. and Kondratenko, E. (2006) Simultaneous operando EPR/UV-vis/laser-Raman spectroscopy - A powerful tool for monitoring transition metal oxide catalysts during reaction, Catal. Today, 113, 16. 

V-Mo-Zeolite catalysts prepared by solid-state ion exchange were studied in the selective catalytic reduction of NOx by ammonia. The catalysts were characterized by chemical analysis, X-ray powder diffraction, N2 adsorption (BET), DRIFT, UV-Vis and Raman, spectroscopy and H2 TPR. Catalytic results show that upon addition of Mo to V-ZSM-5, catalytic performance was enhanced compared to V-ZSM-5. 

In addition to the characteristic XRD patterns and photoluminescence, UV-visible and X-ray absorption spectra, another fingerprint thought to indicate lattice substitution of titanium sites was the vibrational band at 960 cm-1, which has been recorded by infrared and Raman spectroscopy (33,34). Although there is some controversy about the origin of this band, its presence is usually characteristic of a good TS-1 catalyst, although it turned out to be experimentally extremely difficult to establish quantitative correlations between the intensity of the 960 cm-1 band and the Ti content of a Ti silicate and/or its catalytic activity. 

Note that in all the examples discussed so far, infrared spectroscopy gives its information on the catalyst in an indirect way, via hydroxyl groups on the support, or via the adsorption of probe molecules such as CO and NO. The reason why it is often difficult to measure the metal-oxide or metal-sulfide vibrations of the catalytically active phase in transmission infrared spectroscopy is that the frequencies are well below 1000 cm-1, where measurements are difficult because of absorption by the support. Infrared emission and Raman spectroscopy, discussed later on in this chapter, offer better opportunities in this respect. 

An interesting and powerful new development in Raman spectroscopy of catalysts is the use of a UV laser to excite the sample. This has two major advantages. First, the scattering cross section, which varies with the fourth power of the frequency, is substantially increased. Second, the Raman peaks shift out of the visible region of the spectrum where fluorescence occurs. The reader is referred to Li and Stair for applications of UV Raman spectroscopy on catalysts [40]. 

Raman spectroscopy has been successfully applied to the investigation of oxidic catalysts. According to Wachs, the number of Raman publications rose to about 80-100 per year at the end of the nineties, with typically two thirds of the papers devoted to oxides [41]. Raman spectroscopy provides insight into the structure of oxides, their crystallinity, the coordination of metal oxide sites, and even the spatial distribution of phases through a sample when the technique is used in microprobe mode. As the frequencies of metal-oxygen vibrations found in a lattice are typically between a few hundred and 1000 cm 1 and are thus difficult to investigate in infrared, Raman spectroscopy is clearly the indicated technique for this purpose. 

---