Block copolymers anionic polymerization

Since the anionically polymerized block copolymers are relatively expensive they have been more frequently used in blends with engineering than commodity resins. Owing to miscibility of styrene blocks with PPE, the SBS and SEBS are natural tougheners for this polymer. However, for blending with PEST, PC, POM or PA, the copolymer should be modified by incorporation of acidic, acid anhydride, or epoxy moieties. 

Keywords polysiloxanes, cyclotrisiloxanes, anionic polymerization siloxane copolymers, block copolymers, dendritic polymers... 

Styrene-Butadiene Copolymers. Styrene-butadiene polymers are block copolymers prepared from styrene and butadiene monomers. The polymerization is performed using sequential anionic polymerization. The copolymers are better known as thermoplastic elastomers, but copolymers with high styrene contents can be treated as thermo-... 

A brief review has appeared covering the use of metal-free initiators in living anionic polymerizations of acrylates and a comparison with Du Font s group-transfer polymerization method (149). Tetrabutylammonium thiolates mn room temperature polymerizations to quantitative conversions yielding polymers of narrow molecular weight distributions in dipolar aprotic solvents. Block copolymers are accessible through sequential monomer additions (149—151) and interfacial polymerizations (152,153). 

Polymerization ofiVIasked Disilenes. A novel approach, namely, the anionic polymerization of masked disilenes, has been used to synthesize a number of poly(dialkylsilanes) as well as the first dialkylamino substituted polysilanes (eq. 13) (111,112). The route is capable of providing monodisperse polymers with relatively high molecular weight M = lO" — 10 ), and holds promise of being a good method for the synthesis of alternating and block copolymers. 

Butadiene copolymers are mainly prepared to yield mbbers (see Styrene-butadiene rubber). Many commercially significant latex paints are based on styrene—butadiene copolymers (see Coatings Paint). In latex paint the weight ratio S B is usually 60 40 with high conversion. Most of the block copolymers prepared by anionic catalysts, eg, butyUithium, are also elastomers. However, some of these block copolymers are thermoplastic mbbers, which behave like cross-linked mbbers at room temperature but show regular thermoplastic flow at elevated temperatures (45,46). Diblock (styrene—butadiene (SB)) and triblock (styrene—butadiene—styrene (SBS)) copolymers are commercially available. Typically, they are blended with PS to achieve a desirable property, eg, improved clarity/flexibiHty (see Polymerblends) (46). These block copolymers represent a class of new and interesting polymeric materials (47,48). Of particular interest are their morphologies (49—52), solution properties (53,54), and mechanical behavior (55,56). 

Anionic polymerization, if carried out properly, can be truly a living polymerization (160). Addition of a second monomer to polystyryl anion results in the formation of a block polymer with no detectable free PS. This technique is of considerable importance in the commercial preparation of styrene—butadiene block copolymers, which are used either alone or blended with PS as thermoplastics. 

Thermoplastic Elastomers. These represent a whole class of synthetic elastomers, developed siace the 1960s, that ate permanently and reversibly thermoplastic, but behave as cross-linked networks at ambient temperature. One of the first was the triblock copolymer of the polystyrene—polybutadiene—polystyrene type (SheU s Kraton) prepared by anionic polymerization with organoHthium initiator. The stmcture and morphology is shown schematically in Figure 3. The incompatibiHty of the polystyrene and polybutadiene blocks leads to a dispersion of the spherical polystyrene domains (ca 20—30 nm) in the mbbery matrix of polybutadiene. Since each polybutadiene chain is anchored at both ends to a polystyrene domain, a network results. However, at elevated temperatures where the polystyrene softens, the elastomer can be molded like any thermoplastic, yet behaves much like a vulcanized mbber on cooling (see Elastomers, synthetic-thermoplastic elastomers). 

Commercially, anionic polymerization is limited to three monomers styrene, butadiene, and isoprene [78-79-5], therefore only two useful A—B—A block copolymers, S—B—S and S—I—S, can be produced direcdy. In both cases, the elastomer segments contain double bonds which are reactive and limit the stabhity of the product. To improve stabhity, the polybutadiene mid-segment can be polymerized as a random mixture of two stmctural forms, the 1,4 and 1,2 isomers, by addition of an inert polar material to the polymerization solvent ethers and amines have been suggested for this purpose (46). Upon hydrogenation, these isomers give a copolymer of ethylene and butylene. 

Block copolymer chemistry and architecture is well described in polymer textbooks and monographs [40]. The block copolymers of PSA interest consist of anionically polymerized styrene-isoprene or styrene-butadiene diblocks usually terminating with a second styrene block to form an SIS or SBS triblock, or terminating at a central nucleus to form a radial or star polymer (SI) . Representative structures are shown in Fig. 5. For most PSA formulations the softer SIS is preferred over SBS. In many respects, SIS may be treated as a thermoplastic, thermoprocessible natural rubber with a somewhat higher modulus due to filler effect of the polystyrene fraction. Two longer reviews [41,42] of styrenic block copolymer PSAs have been published. 

The earliest SIS block copolymers used in PSAs were nominally 15 wt% styrene, with an overall molecular weight on the order of 200,000 Da. The preparation by living anionic polymerization starts with the formation of polystyryl lithium, followed by isoprene addition to form the diblock anion, which is then coupled with a difunctional agent, such as 1,2-dibromoethane to form the triblock (Fig. 5a, path i). Some diblock material is inherently present in the final polymer due to inefficient coupling. The diblock is compatible with the triblock and acts... 

Of the amorphous block copolymers, styrenic block copolymers are the vast majority. These are synthesized anionically in solution, with butyl lithium commonly employed as the initiator [4]. There are three processes for this polymerization ... 

Photoinitiators provide a convenient route for synthesizing vinyl polymers with a variety of different reactive end groups. Under suitable conditions, and in the presence of a vinyl monomer, a block AB or ABA copolymer can be produced which would otherwise be difficult or impossible to produce by another polymerization method. Moreover, synthesis of block copolymers by this route is much more versatile than those based on anionic polymerization, since a wider range of a monomers can be incorporated into the blocks. 

The block copolymer produced by Bamford s metal carbonyl/halide-terminated polymers photoinitiating systems are, therefore, more versatile than those based on anionic polymerization, since a wide range of monomers may be incorporated into the block. Although the mean block length is controllable through the parameters that normally determine the mean kinetic chain length in a free radical polymerization, the molecular weight distributions are, of course, much broader than with ionic polymerization and the polymers are, therefore, less well defined,... 

Block copolymer—These copolymers are built of chemically dissimilar terminally connected segments. Block copolymers are generally prepared by sequential anionic addition or ring opening or step growth polymerization. 

As previously described, all microspheres discussed in this chapter were synthesized from AB type diblock copolymers. Precursor block copolymers, poly(styrene-b-4-vinyl pyridine) (P[S-b-4VP]) diblock copolymers, were synthesized using the additional anionic polymerization technique [13]. The basic properties of the block copolymers were determined elsewhere [24,25] and are listed... 

As these block copolymers were synthesized using the anionic polymerization technique, their molecular weight distributions were narrow. The microspheres with narrower size distribution are better for well-ordered self-organization. Actually, all block copolymers synthesized for these works formed poly(4-vinyl pyridine) (P4VP) spheres in the PS matrices with narrow size distributions. 

The poly(styrene-b-isoprene) (P(S-b-IP)) and poly(-styrene-b-2-vinyl pyridine) (P(S-b-2VP)) block copolymers with narrow molecular weight distributions for blending with the microspheres were also synthesized using the additional anionic polymerization technique. The number-average molecular weights (Mns) and PS contents are also shown in Table 1. 

Block copolymers have been synthesized on an industrial scale mainly by anionic or cationic polymerization, although monomers for block components are limited to ones capable of the process. Intensive academic and technological interest in radical block copolymerization using macroinitiators is growing. This process can be implemented in plants with easier handling of materials, milder conditions of operation, and a variety of materials to give various kinds of block copolymers to develop a wide application area [1-3]. 

Polystyrene homopolymer produced by free radical initiators is highly amorphous (Tg = 100°C). The general purpose rubber (SBR), a block copolymer with 75% butadiene, is produced by anionic polymerization. 

Currently, more SBR is produced by copolymerizing the two monomers with anionic or coordination catalysts. The formed copolymer has better mechanical properties and a narrower molecular weight distribution. A random copolymer with ordered sequence can also be made in solution using butyllithium, provided that the two monomers are charged slowly. Block copolymers of butadiene and styrene may be produced in solution using coordination or anionic catalysts. Butadiene polymerizes first until it is consumed, then styrene starts to polymerize. SBR produced by coordinaton catalysts has better tensile strength than that produced by free radical initiators. 

The reactions of polymeric anions with appropriate azo-compounds or peroxides to form polymeric initiators provide other examples of anion-radical transformation (e.g. Scheme 7. 6). ""7i However, the polymeric azo and peroxy compounds have limited utility in block copolymer synthesis because of the poor efficiency of radical generation from the polymeric initiators (7.5.1). 

Tung et al21> have reported on the use of a polymeric thiol transfer agent for use in block copolymer production. Various methods have been used for the anion thiol conversion. Near quantitative yields of thiol arc reported to have been obtained by terminating anionic polymerization with ethylene sulfide and derivatives (Scheme 7.27). Transfer constants for the polymeric thiols are reported to be similar to those of analogous low molecular weight compounds.273... 

The generic features of these approaches are known from experience in anionic polymerization. However, radical polymerization brings some issues and some advantages. Combinations of strategies (a-d) are also known. Following star formation and with appropriate experimental design to ensure dormant chain end functionality is retained, the arms may be chain extended to give star block copolymers (321). In other cases the dormant functionality can be retained in the core in a manner that allows synthesis of mikto-arm stars (324). 

Anionic polymerization of ethylene oxide by living carbanions of polystyrene was first carried out by Szwarc295. A limited number of methods have been reported in the preparation of A-B and A-B-A copolymers in which B was polystyrene and A was poly(oxyethylene)296-298. The actual procedure was to allow ethylene oxide to polymerize in a vacuum system at 70 °C with the polystyrene anion initiated with cumyl potassium in THF299. The yields of pure block copolymers are usually limited to about 80% because homopolymers are formed300. ... 

---