Acrylic plastics techniques

This photoelastic stress analysis is a technique for the nondestructive determination of stress and strain components at any point in a stressed product by viewing a transparent plastic product. If not transparent, a plastic coating is used such as certain epoxy, polycarbonate, or acrylic plastics. This test method measures residual strains using an automated electro-optical system. 

The basic technique of using domes formed from acrylic sheet as skylights was developed in the 1950s and represented one of the earliest commercial applications of acrylic plastic. 

Volume 1 of this book is comprised of 25 chapters, and discusses the different types of natural rubber based blends and IPNs. The first seven chapters discuss the general aspects of natural rubber blends like their miscibility, manufacturing methods, production and morphology development. The next ten chapters describe exclusively the properties of natural rubber blends with different polymers like thermoplastic, acrylic plastic, block or graft copolymers, etc. Chapter 18 deals entirely with clay reinforcement in natural rubber blends. Chapters 19 to 23 explain the major techniques used for characterizing various natural rubber based blends. The final two chapters give a brief explanation of life cycle analysis and the application of natural rubber based blends and IPNs. 

AH the common monobasic (107) and dibasic esters (108) of tetrahydrofurfuryl alcohol have been prepared by conventional techniques the dibasic esters and some of the mono esters are effective as primary or secondary plasticizers for vinyl polymers. Tetrahydrofurfuryl acrylate [2399-48-6] and methacrjiate [2455-24-5] specialty monomers, have been produced by carbonylation (nickel carbonyl and acetylene) of the alcohol (109) as weU as by direct esterification (110—112) and ester interchange (111). 

The principal solution to fabrication difficulties is copolymerization. Three types of comonomers are commercially important vinyl chloride acrylates, including alkyl acrylates and alkyimethacrylates and acrylonitrile. When extmsion is the method of fabrication, other solutions include formulation with plasticizers, stabilizers, and extmsion aids plus applying improved extmsion techniques. The Hterature on vinyHdene chloride copolymers through 1972 has been reviewed (1). 

HS-GC methods have equally been used for chromatographic analysis of residual volatile substances in PS [219]. In particular, various methods have been described for the determination of styrene monomer in PS by solution headspace analysis [204,220]. Residual styrene monomer in PS granules can be determined in about 100 min in DMF solution using n-butylbenzene as an internal standard for this monomer solid headspace sampling is considerably less suitable as over 20 h are required to reach equilibrium [204]. Shanks [221] has determined residual styrene and butadiene in polymers with an analytical sensitivity of 0.05 to 5 ppm by SHS analysis of polymer solutions. The method development for determination of residual styrene monomer in PS samples and of residual solvent (toluene) in a printed laminated plastic film by HS-GC was illustrated [207], Less volatile monomers such as styrene (b.p. 145 °C) and 2-ethylhexyl acrylate (b.p. 214 °C) may not be determined using headspace techniques with the same sensitivities realised for more volatile monomers. Steichen [216] has reported a 600-fold increase in headspace sensitivity for the analysis of residual 2-ethylhexyl acrylate by adding water to the solution in dimethylacetamide. 

Acrylic Crosslinkers. Butanediol diacrylate (IV) (BDDA) is a popular crosslinker used in the preparation of many polymers used for inks, paints, and plastics. Low-levels of impurities can adversely affect product properties. As previously discussed, K+IDS provides a powerful qualitative technique, but yields poor quantitative data when analyzing volatile chemicals. BDDA is amenable to analysis by GC, unfortunately any higher-molecular-weight adducts exceed the volatility range amenable to GC. Moreover, BDDA is not chromophoric thereby HPLC characterization is also difficult. 

Rubber systems do stick to many plastics well, but they are relatively moisture-sensitive. There s always a risk that they may lose their adhesive strength at high humidity levels. At temperatures above about 40°C, they turn very soft and lose their inherent strength. Pure acrylates and modified acrylates are primary materials that provide PSAs with greater moisture resistance and thermal stability. Pure acrylates above all remain sufficiently adhesive up to about 150 or for short periods 200°C. Adhesive tapes of this kind are used for masking purposes in powdercoating techniques. 

---